Effect of Drilling-Induced Delamination on the Flexural Strength of GNPs-Reinforced Carbon Fiber Sandwich Composites

Öz

In this study, the effect of drilling-induced delamination damage on the flexural strength of sandwich composites with 0.5% by weight GNPs (graphene nanoplatelets) reinforced carbon fiber face sheets (GNPs/carbon sandwich) and nanoparticle-free Neat/carbon sandwich composites was investigated. In three-point bending specimens, drilling operations were performed with hole diameters of 5 mm and 6 mm. Delamination damage at the entry and exit points of the holes were observed through microscopic imaging and evaluated. Image processing techniques were applied to microscopic images, and quantitative values were obtained. According to the three-point bending test results, the lowest strength loss was observed in GNP/carbon sandwich composites. The highest bending strength was measured as 800 N in GNP/carbon sandwich composites. The lowest bending strength was found to be 450 N in pure/carbon sandwich composites drilled with a 6 mm diameter hole. Adding GNPs nanoparticles to carbon fiber sandwich composites reduced delamination damage caused by drilling. GNPs-reinforced sandwich composites showed better bending strength compared to sandwich composites without nanoparticles.

Anahtar Kelimeler

• Graphene nanoplatelets (GNPs)
• Sandwich composites
• Delamination damage
• Drilling process
• Flexural strength

Destekleyen Kurum

This study was supported by Selçuk University Scientific Research Projects Coordination Office (BAP) with project number 19301010.

Etik Beyan

The authors declare that the principles of scientific research and publication ethics were followed at all stages of the study.

Delme Kaynaklı Delaminasyonun GNP Takviyeli Karbon Fiber Sandviç Kompozitlerin Eğilme Dayanımı Üzerindeki Etkisi

Öz

Bu çalışmada, delme kaynaklı delaminasyon hasarının %0,5 ağırlık oranında GNPs (grafen nanoplakacıklar) takviyeli karbon fiber yüzeyli sandviç kompozitlerin (GNPs/karbon sandviç) ve nanopartikül içermeyen Neat/karbon sandviç kompozitlerin eğilme dayanımına etkisi araştırılmıştır. Üç nokta eğme numunelerinde 5 mm ve 6 mm delik çaplarında delme işlemleri gerçekleştirilmiştir. Delik giriş ve çıkış bölgelerindeki delaminasyon hasarı mikroskobik görüntüler kullanılarak değerlendirilmiştir. Mikroskobik görüntülere görüntü işleme teknikleri uygulanmış ve kantitatif değerler elde edilmiştir. Üç nokta eğme testi sonuçlarına göre en düşük dayanım kaybı GNPs/karbon sandviç kompozitlerde gözlenmiştir. En yüksek eğilme dayanımı GNPs/karbon sandviç kompozitlerde 800 N olarak ölçülürken, en düşük eğilme dayanımı 6 mm çapında delinen Neat/karbon sandviç kompozitlerde 450 N olarak bulunmuştur. Karbon fiber sandviç kompozitlere GNP eklenmesi, delme kaynaklı delaminasyon hasarını azalttı ve nanopartikül içermeyen sandviç kompozitlere kıyasla eğilme dayanımında daha az bozulmaya yol açtı.

Anahtar Kelimeler

• Grafen nanoplakalar (GNP
• Sandviç kompozitler
• Delaminasyon hasarı
• Delme işlemi
• Eğilme dayanımı

Destekleyen Kurum

Bu çalışma,Selçuk Üniversitesi Bilimsel Araştırma Projeleri Koordinasyon Ofisi (BAP) tarafından 19301010 numaralı proje ile desteklenmiştir.

Etik Beyan

Yazarlar, çalışmanın tüm aşamalarında bilimsel araştırma ve yayın etiği kurallarına uyulduğunu beyan eder.

Kaynakça

1. Geier, N., J.P. Davim, and T. Szalay, Advanced cutting tools and technologies for drilling carbon fibre reinforced polymer (CFRP) composites: A review. Composites Part A: Applied Science and Manufacturing, 2019. 125: p. 105552.
2. Karataş, M.A. and H. Gökkaya, A review on machinability of carbon fiber reinforced polymer (CFRP) and glass fiber reinforced polymer (GFRP) composite materials. Defence Technology, 2018. 14(4): p. 318-326.
3. Arias, G.G., et al., Thermal analysis by finite elements of hotends for 3D printing by fused filament fabrication. Periodica Polytechnica Mechanical Engineering, 2021. 65(2): p. 129-133.
4. Lukacs, T., C. Pereszlai, and N. Geier, Delamination measurement in glass fibre reinforced polymer (GFRP) composite based on image differencing. Composites Part B: Engineering, 2023. 248: p. 110381.
5. Pereira, A.C., et al., Machinability and surface integrity of glass fiber reinforced plastic composite: A review. Journal of Materials Research and Technology, 2025.
6. Demirci, I. (2026). Delamination damage analysis of GNPs-Filled carbon fiber composites through three-point bending and drilling experiments. Journal of Composite Materials, 60(14), 1305-1321.
7. Demirci, I. (2026). Delamination damage analysis of GNPs-Filled carbon fiber composites through three-point bending and drilling experiments. Journal of Composite Materials, 60(14), 1305-1321.
8. Xu, J., Q. An, and M. Chen, A comparative evaluation of polycrystalline diamond drills in drilling high-strength T800S/250F CFRP. Composite Structures, 2014. 117: p. 71-82.

9. Poór, D. I., Geier, N., Pereszlai, C., & Xu, J. (2021). A critical review of the drilling of CFRP composites: Burr formation, characterisation and challenges. Composites Part B: Engineering, 223, 109155.
10. Anand, R.S. and K. Patra, Mechanistic cutting force modelling for micro-drilling of CFRP composite laminates. CIRP Journal of Manufacturing Science and Technology, 2017. 16: p. 55-63.
11. Davim, J.P., Machining composites materials. 2013: John Wiley & Sons.
12. Davim, J.P., Machining: fundamentals and recent advances. 2008.
13. Khashaba, U.A., Drilling of polymer matrix composites: a review. Journal of composite materials, 2013. 47(15): p. 1817-1832.
14. Panchagnula, K.K., N.V.K. Jasti, and J.S. Panchagnula, Prediction of drilling induced delamination and circularity deviation in GFRP nanocomposites using deep neural network. Materials Today: Proceedings, 2022. 62: p. 7118-7123.
15. Ali, H.M., A. Iqbal, and L. Liang, A comparative study on the use of drilling and milling processes in hole making of GFRP composite. Sadhana, 2013. 38(4): p. 743-760.
16. Monoranu, M., et al., The effect of particle reinforcements on chip formation and machining induced damage of modified epoxy carbon fibre reinforced polymers (CFRPs). Composites Part A: Applied Science and Manufacturing, 2022. 154: p. 106793.
17. Binali, R., et al., A review on progress trends of machining of Carbon Fiber Reinforced Plastics. Journal of Materials Research and Technology, 2024. 33: p. 4332-4359.
18. Geng, D., et al., Delamination formation, evaluation and suppression during drilling of composite laminates: A review. Composite Structures, 2019. 216: p. 168-186.
19. Babu, J., et al., Assessment of delamination in composite materials: a review. Proceedings of the Institution of Mechanical Engineers, Part B: Journal of Engineering Manufacture, 2016. 230(11): p. 1990-2003.
20. Gaugel, S., et al., A comparative study on tool wear and laminate damage in drilling of carbon-fiber reinforced polymers (CFRP). Composite Structures, 2016. 155: p. 173-183.
21. Makhesana, M.A., et al., Evaluation of drilling and hole quality characteristics in green machining aluminium alloys: A new approach towards green machining. Journal of Manufacturing Processes, 2024. 129: p. 176-186.
22. Dhakate, S.R. and O.P. Bahl, Effect of carbon fiber surface functional groups on the mechanical properties of carbon–carbon composites with HTT. Carbon, 2003. 41(6): p. 1193-1203.
23. Demirci, I. and I. Saritas, Damage analysis of Nomex honeycomb sandwich structures using image processing and artificial intelligence approaches. Polymer Composites, 2025. 46(2): p. 1121-1138.
24. Da Silva, L. R. R., Pereira, A. C., Monteiro, S. N., Kuntoğlu, M., Binali, R., Khan, A. M., ... & Pimenov, D. Y. (2025). Review of advances and challenges in machining of metal matrix composites. Journal of Materials Research and Technology, 37, 1061-1085.