Mechanical Properties of Polypropylene Fiber Added Mud Bricks

Öz

In this study, mud bricks were produced by using polypropylene fiber with 6 mm, 12 mm and 19 mm length. Polypropylene fiber was added to the clay soil in proportion of 0% (without additives), 0.5%, 1% and 1.5% by weight. A total of 10 different mixtures, 1 mixture without additives and 9 different mixtures with polypropylene additives, were created and mudbrick bricks were produced. 3 mud brick samples were produced for each fiber length and for each mix proportion. The volume losses, unit volume weights, compressive strengths and bending damage loads of these samples were investigated. As a result of the study, it was observed that as the mix ratio of polypropylene fiber additive samples and fiber length increased, the volume loss decreased between 8.57% and 37.25%, and the unit volume weight decreased between 1.54% and 7.25%.Compressive strengths were found to increase between 11.67% and 44.93% as the fiber ratio and length increased compared to non-additive samples. It was observed that bending damage loads increased between 43.19% and 250.05% compared to samples without additives.

Anahtar Kelimeler

• Fiber,mud brick,polypropylene fiber

Polipropilen Lif Katkılı Kerpiç Tuğlaların Fiziksel ve Mekanik Özelliklerinin İncelenmesi

Öz

Bu çalışmada lif katkılı kerpiç tuğla üretimi gerçekleştirmek için kullanılan killi toprak ile boyları 6 mm, 12 mm ve 19 mm olan polipropilen lif kullanılmıştır. Killi toprağa ağırlıkça % 0 (katkısız), % 0,5 , % 1 ve % 1,5 oranlarında polipropilen lif katılmıştır. Katkısız karışımdan 1, polipropilen katkılı karışımlardan 9 farklı karışım toplam 10 adet farklı karışım oluşturularak kerpiç tuğla üretimi gerçekleştirilmiştir. Her bir karışım için 3 adet kerpiç tuğla numunesi üretilmiştir. Üretilen bu örneklerin hacim kayıpları, birim hacim ağırlıkları, basınç dayanımları ve eğilme hasar yükleri araştırılmıştır. Çalışma sonucunda polipropilen lif katkılı numunelerin katkı oranı ve lif boyu arttıkça hacim kaybının katkısız numunelere göre %8,57 ile %37,25 aralığında azaldığı, birim hacim ağırlığının ise %1,54 ile %7,25 aralığında azaldığı görülmüştür. Basınç dayanımlarının katkısız numunelere göre lif oranı ve boyu arttıkça %11,67 ile %44,93 aralığında arttığı görülmüştür. Eğilme hasar yüklerinin ise katkısız numunelere göre %43,19 ile %250,05 aralığında arttığı tespit edilmiştir.

 

Anahtar Kelimeler

• polipropilen lif,kerpiç tuğla,basınç dayanım,eğilme dayanımı

Kaynakça

1. Afroughsabet, V., & Ozbakkaloglu, T. (2015). Mechanical and durability properties of high-strength concrete containing steel and polypropylene fibers. Construction and building materials, 94, 73-82.
2. Afroughsabet, V., Biolzi, L., & Monteiro, P. J. (2018). The effect of steel and polypropylene fibers on the chloride diffusivity and drying shrinkage of high-strength concrete. Composites Part B: Engineering, 139, 84-96.
3. Anonim 2019a. http://www.mta.gov.tr/v3.0/bilgimerkezi/tugla-kiremit
4. Anonim 2019b. http://tuzyapgeridonusum.com/killi-toprak nedir.html
5. Binici, H.,Aksogan, O., Bakbak, D., Kaplan, H., &Isik, B. (2009). Sound insulation of fibrere inforced mud brick walls. Construction and Building Materials, 23(2), 1035-1041.
6. Caf M. (2012). Polipropilen Ve Çelik Lifli Betonların Darbe Dayanımı, Yüksek Lisans Tezi, Atatürk Üniversitesi, Erzurum Dengiz E (2009). Değirmisaz Kömür Üstü Atıklarının Tuğla Üretiminde Kullanılabilirliğinin Araştırılması. Yüksek Lisans Tezi, Dumlupınar Üniversitesi, Fen Bilimleri Enstitüsü, Seramik Mühendisliği Anabilim Dalı, Kütahya, 63 s.
7. Fathi, H., Lameie, T., Maleki, M., & Yazdani, R. (2017). Simultaneous effects of fiber and glass on the mechanical properties of self-compacting concrete. Construction and Building Materials, 133, 443-449.
8. Gencel, O.,Sütçü, M., Erdoğmuş, E., Koç, V., Çay, V. V., Gök, M. S. (2013). Properties of brick swith waste ferro chromium slagand zeolite. Journal of cleaner production, 59, 111-119.

9. Gürdal, E., Acun, S. (2004). Mineral Esaslı Sıvalarda Polipropilen Lif Katkısının Fiziksel Ve Mekanik Özelliklere Etkisinin İncelenmesi, 2. Ulusal Yapı Malzemesi Kongresi Ve Sergisi, İstanbul Teknik Üniversitesi, October 6-8, İstanbul
10. Kakooei, S., Akil, H. M., Jamshidi, M., Rouhi, J. (2012). The effects of polypropylene fibers on the properties of reinforced concrete structures. Construction and Building Materials, 27(1), 73-77.
11. Şahin, M. (2007), “Betonla Uyumlu Polipropilen Elyaf Takviyeli Kompozitlerin Üretimi ve Özellikleri”. Yüksek Lisans Tezi, Marmara Üniversitesi Fen Bilimleri Enstitüsü, İstanbul
12. Şahin M. (2009), “Borik Asit Katkılı Tuğla Üretiminin Araştırılması”. Yüksek Lisans Tezi,Afyon Kocatepe Üniversitesi Fen Bilimleri Enstitüsü, Afyonkarahisar