Effects of different mouthwashes on microhardness, surface roughness and color change of universal resin composites

Yıl 2025, Cilt: 42 Sayı: 1, 29 - 35, 03.01.2025

Ayşenur Bulut , Cansu Dağdelen Ahısha , Oya Bala , Sinem Akgül

Öz

OBJECTIVE: The aim of this study was to investigate the effect of different mouthwashes (Andorex and Listerine Cool Mint) on the microhardness, surface roughness and color change of different universal resin composites (Omnichroma, G-aenial A’chord and Charisma Diamond
One).
MATERIALS AND METHOD: A total of 90 specimens were prepared, 30 for each of the resin composites used in the study, the prepared samples were kept in artificial saliva for 24 hours. Initial microhardness measurements were measured by using a Vickers hardness measuring device,
surface roughness measurements were made by using a profilometer device, and color measurements were made by using a spectrophotometer device. The specimens were randomly divided into three groups. Each group was immersed in artificial saliva, in Andorex mouthwash, and in Listerine Cool Mint mouthwash for 24 hours respectively. Microhardness, surface roughness, and color measurements were measured again. The obtained
datas were analyzed with a one-way analysis of variance and Tukey’s multiple comparison test at a statistical significance level of p<0.05.
RESULTS: It was observed that all universal resin composites showed a decrease in surface microhardness values and an increase in roughness values after immersed in mouthwash. The greatest color change was obtained from the specimes which were immersed in Andorex mouthwash. The color change of the specimens prepared with Omnichroma immersed in Andorex mouthwash was significantly higher than the other groups (p<0.05).
CONCLUSION: The ingredients of the mouthwashes used may play a role in the microhardness, surface roughness, and color change of universal resin composites.

Anahtar Kelimeler

Color, Dental resin composite, Mouthwashes, Surface Properties

Üniversal rezin kompozitlerin mikrosertliği, yüzey pürüzlülüğü ve renk değişimi üzerine farklı ağız gargaralarının etkileri

Öz

ÖZET
AMAÇ: Bu çalışmanın amacı, üç farklı üniversal rezin kompozitin (Omnichroma, G-aenial A’chord ve Charisma Diamond One) mikrosertliği, yüzey pürüzlülüğü ve renk değişimi üzerine farklı ağız gargaralarının (Andorex ve Listerine Cool Mint) etkisini araştırmaktır.
GEREÇ VE YÖNTEM: Çalışmada kullanılan rezin kompozitlerin her biri için 30 adet olacak şekilde toplam 90 adet örnek hazırlandı, sonrasında yapay tükürükte 24 saat bekletildi. Başlangıç mikrosertlik ölçümleri Vickers sertlik ölçüm cihazı, yüzey pürüzlülük ölçümleri profilometre cihazı ve
renk ölçümleri ise spektrofotometre cihazı kullanılarak yapıldı. Sonrasında, hazırlanan örnekler rastgele üç gruba ayrıldı. Grup 1’deki örnekler yapay tükürük içinde, Grup 2’deki örnekler Andorex ağız gargarasında, Grup 3’teki örnekler Listerine Cool Mint ağız gargarası içerisinde 24 saat bekletildi. Takiben, her örneğin mikrosertlik, yüzey pürüzlülüğü ve renk ölçümleri tekrar alındı. Elde edilen veriler tek yönlü varyans analizi ve Tukey çoklu
karşılaştırma testi ile istatistiksel olarak p<0.05 anlamlılık düzeyinde analiz edildi.
BULGULAR: Tüm üniversal rezin kompozitler ağız gargaraları içerisinde bekletildikten sonra mikrosertlik değerlerinde azalma, yüzey pürüzlülük değerlerinde ise artış olduğu gözlendi (p<0.05). En fazla renk değişimi, Andorex ağız gargarası içerisinde bekletilen gruptaki örneklerden
elde edildi. Andorex ağız gargarası içerisinde bekletilen Omnichroma ile hazırlanan örneklerin renk değişimi diğer gruplara göre anlamlı derecede daha yüksek olduğu görüldü (p<0.05).
SONUÇ: Üniversal rezin kompozitlerin mikrosertliği, yüzey pürüzlülüğü ve renk değişiminde kullanılan ağız gargaralarının içerikleri rol oynayabilir.

Anahtar Kelimeler

Dental Rezin Kompozit, Gargaralar, Renk, Yüzey Özellikleri

Kaynakça

• Mansurov ZA. Recent Achievements and Future Challenges in Nanoscience and Nanotechnology. Eurasian Chem J 2020; 22: 241–53.
• Moszner N, Salz U. New developments of polymeric dental composites. Prog Polym Sci 2001; 26: 535-76.
• Ferracane JL. Resin composite- state of the art. Dent Mater 2011; 27: 29-8.
• Vichi A, Ferrari M, Davidson CL. Color and opacity variations in three different resin based composite products after water aging. Dent Mater 2004; 20: 530-34.
• Aydın N, Karaoğlanoğlu S, Oktay EA, Ersöz B. Investigation of single shade composite resin surface roughness and color stability. Atatürk Üniv Diş Hek Fak Derg 2021; 31: 207-14.
• Akgül S, Gündoğdu C, Çalışkan Z, Çelik A, Bala O. Farkli İçeceklerin Üniversal Rezin Kompozitlerin Renk Stabilitesi ve Yüzey Özelliklerine Etkisinin İncelenmesi. Selcuk Dent J 2022; 9: 445-50.
• Ozer S, Sen Tunc E, Tuloglu N, Bayrak S. Solubility of two resin composites in different mouthrinses. Biomed Res Int 2014;1-5.
• Dos Santos PA, Garcia PP, De Oliveira AL, Chinelatti MA, Palma-Dibb RG. Chemical and morphological features of dental composite resin: influence of light curing units and immersion media. Microsc Res Tech 2010; 73: 176-81.
• Miranda DDA, Bertoldo CEDS, Aguiar FHB, Lima D, Lovadino JR. Effects of mouthwashes on Knoop hardness and surface roughness of dental composites after different immersion times. Brazil Oral Res 2011; 25: 168-73.
• Bagheri R, Burrow MF, Tyas M. Influence of foodsimulating solutions and surface finish on susceptibility to staining of aesthetic restorative materials. J Dent 2005; 33: 389-98.
• Menon A, Ganapathy DM, Mallikarjuna AV. Factors that influence the colour stability of composite resins. Drug Invent Tod 2019; 11: 744-49.
• Tekçe N, Tuncer S, Demirci M, Serim ME, Baydemir C. The effect of different drinks on the color stability of different restorative materials after one month. Restor Dent Endod 2015; 40: 255-61.
• Gurgan S, Onen A, Koprulu H. In vitro effects of alcohol-containing and alcohol-free mouthrinses on microhardness of some restorative materials. J Oral Rehabil 1997; 24: 244-6.
• De Morais Sampaio GA, Peixoto LR, de Vasconcelos Neves G, do Nascimento Barbosa D. Effect of mouthwashes on color stability of composite resins: A systematic review. J Prosth Dent 2021; 126: 386-92.
• Villalta P, Lu H, Okte Z, Garcia-Godoy F, Powers JM. Effects of staining and bleaching on color change of dental composite resins. J Prosthet Dent 2006; 95: 137-42.
• Moran JM. Chemical plaque control-prevention for the masses. Periodonto 2000; 15: 109-17.
• Yesilyurt C, Yoldas O, Altintas SH, Kusgoz A. Effects of food‐ simulating liquids on the mechanical properties of a silorane‐based dental composite. Dent Mater J 2009; 28: 362‐7.
• Penugonda B, Settembrini L, Scherer W, Hittelman E, Strassler H. Alcohol-containing mouthwashes: effect on composite hardness. J Clin Dent 1994; 5: 60-2.
• Oivanen M, Keulemans F, Garoushi S, Vallittu PK, Lassila L. The effect of refractive index of fillers and polymer matrix on translucency and color matching of dental resin composite. Biomater İnvestig Dent 2021; 8: 48-3.
• Abo El Naga A, Yousef M. Evaluation of different restorative materials after exposure to chlorhexidine. J Am Sci 2012; 8: 628-31.
• Baig AR, Shori DD, Shenoi PR, Ali SN, Shetti S, Godhane A. Mouthrinses affect color stability of composite. J Conserv Dent 2016; 19: 355.
• Carpenter G, Pramanik R, Proctor G. An in vitro model of chlorhexidine‐induced tooth staining. J Periodont Res 2005; 40: 225-30.