Effect of Notch Position on Impact Toughness of Friction Stir Processed Low Carbon Steel
Öz
The effect of single-pass friction stir
processing (FSP) on the room temperature impact toughness of a low carbon steel
was investigated via Charpy impact test. A fine-grained (FG) microstructure was
achieved into the processed zone by large deformation and simultaneous dynamic
recrystallization during FSP. The average grain size decreased from 25 μm down
to 3.0 μm after FSP. Grain refinement by FSP increased the impact energies as a
result of refined grains separated mostly by high-angle of misorientation.
Toughness of steel before FSP was about 8.7 J, and it increased up to 11.2 J
after processing depending on the notch positions of the samples. The peak
impact toughness value of 11.2 J was achieved with the notch position located
at top of the surface of processed steel plate.
Anahtar Kelimeler
Kaynakça
- Aktarer, S.M., Sekban, D.M., Saray, O., Kucukomeroglu,T., Ma, Z.Y., Purcek, G. (2015) Materials Science and Engineering: A, 636 311-319.
- Joo, M.S., Suh, D.W., Bhadeshia, H.K.D.H. (2013) Isij Int, 53 1305-1314.
- Lienert, B.T.J., Stellwag, J.W.L., Grimmett, B.B., Warke, R.W. (2003) Welding Journal Research Supplement, 82 1-9.
- Ma, Z.Y. (2008) Metall Mater Trans A, 39A 642-658.
- Ma, Z.Y., Pilchak, A.L., Juhas, M.C., Williams, J.C. (2008) Scripta Mater, 58 361-366.
- Mishra, R.S., Ma, Z.Y. (2005) Materials Science and Engineering: R: Reports, 50 1-78.
- Prangnell, P.B., Heason, C.P. (2005) Acta Mater, 53 3179-3192.
- Ray, A., Paul, S.K., Jha, S. (1995) J Mater Eng Perform, 4 679-688.
Ayrıntılar
Birincil Dil
Türkçe
Konular
-
Bölüm
-
Yazarlar
Dursun Murat Sekban
Bu kişi benim
Semih Mahmut Aktarer
Bu kişi benim
Zongyi Ma
Bu kişi benim
Yayımlanma Tarihi
3 Nisan 2017
Gönderilme Tarihi
3 Nisan 2017
Kabul Tarihi
-
Yayımlandığı Sayı
Yıl 2017 Sayı: 207