Kireçtaşı Kökenli Kırma Kumdaki İnce Madde Oranının Beton Kıvamına ve Dayanımına Etkisi

In this study, the effect of fine materials ratio in limestone aggregate to consistency and strength of concrete has been investigated. Within the scope of study, fifteen concrete designs were produced in three different groups. In the first group, 9 concrete mixtures which have 0.58-0.53-0.56 quantity of water/cement 3 for each were produced. In the second group, water/cement quantity of concrete mixtures were arranged to have the same slumps. The fine aggregate used in the concrete produced was 5 %, 10 % and 15 % of the area passing through the 0.075 mm sieve according to ASTM C 117. In this study according to aggregate granulometry, mineral filler which does not contain small material like clay raises quantity of concrete slump as small materials in concrete space. It is determined that in fine aggregate which is from limestone will used concrete, quantity of mineral filler can reach 15 %.

Bu çalışmada, kireçtaşı kökenli agrega içerisinde bulunan ince madde oranının beton kıvamına ve dayanımına olan etkileri araştırılmıştır. Çalışma kapsamında iki farklı grupta on beş tane beton tasarımı yapılmıştır. Birinci grupta 0.58-0.53-0.56 su/çimento oranına sahip, her farklı su/çimento oranından üçer tane olmak üzere dokuz adet beton üretilmiştir. İkinci gruptaki betonların ise çökmeleri eşit olacak şekilde su/çimento oranları ayarlanmıştır. Üretilen betonlarda kullanılan ince agreganın ASTM C 117’ye göre  0.075 mm elekten geçen kısmı % 5, % 10 ve % 15 olmuştur. Bu çalışmada kullanılan agrega granülometrisine göre kil türü ince malzeme içermeyen kireçtaşı kökenli ince maddenin beton boşluklarında ince malzeme vazifesi görerek betonun çökme miktarını arttırdığı tespit edilmiştir. Çökmeler ve basınç dayanımları açısından değerlendiğinde betonda kullanılacak kireçtaşı kökenli ince agregada ince madde oranının %  15 seviyesine kadar çıkarılabileceği belirlenmiştir.