Üleksit Atığı İçeren Duvar Karolarının Farklı Sinterleşme Sıcaklıklarında Üretimi

Experimental compositions were prepared by the additions of ulexite concentrator waste to a standard wall tile body sintered at different temperatures. Tests of linear firing shrinkage, water absorption, and fired bending strength (eğilme mukavemeti) were done. XRD analyses were conducted to determine major crystalline phases in wall tile bodies. SEM-EDX analyses were performed to study the microstructural evolution of the standard and experimental wall tile bodies. Colorimetric analyses were also made. The wall tile body containing 5 weight percent ulexite concentrator waste fired at 925 ^oC for 6 minutes was determined to be the optimal composition with 0.60 % of linear firing shrinkage, 17.66 % of water absorption, and 208.60 of kg/cm² fired bending strength (eğilme mukavemeti) . Sintering temperature was reduced from 1182 ^oC of industrial practice down to 925 ^oC. Utilization of ulexite concentrator waste in tile bodies will help reduce energy costs in favour of the environment and economy.

Üleksit konsantratör atığının standard duvar karosu bünyesine katılması ve değişik sıcaklıklarda sinterleşmesiyle deneysel numuneler hazırlanmıştır. Doğrusal pişme küçülmesi, su absorpsiyonu ve pişme bükülme testleri yapılmıştır. X-ışınları kırınım analizleri duvar karolarının kristal fazlarını tayin etmekte; SEM-EDX analizleri standard ve deneysel duvar karolarının mikro yapılarındaki değişimlerin anlaşılmasında kullanılmıştır. Renk analizleri de gerçekleştirilmiştir. 925°C de 6 dakika pişirilen %5 üleksit konsantratör atığı %0.6 doğrusal pişme küçülmesi, %17.66 su emme ve 208.6 kg/cm² pişme bükülmesi değerleriyle optimum konsantratör atık derişimi olarak belirlenmiştir. Endüstriyel üretimde 1182°C olan sinterleşme sıcaklığı 925°C’ ye düşürülmüştür. Üleksit konsantratör atığının duvar karolarında kullanımı enerji maliyetlerini düşürmeye yardım ederek ekonomi ve çevreye yarar sağlayacaktır.