This research has been initiated in order to investigate the pelletization of iron ore fines produced in
Turkish Iron Mines. The first experiments were conducted on Divriği Iron ore fines and the results showed
that it is possible to make pellets from these ores which are strong enough to be used in the blast
furnace.
The iron ore fines imust first be ground to -Î00 mesh and then should be mixed with 1-2 % bentonite
and enough water to make it suitable for pelletization. The mixture is then fed into a pelletizing drum
and the green pellets obtained are first dried at 105"C and then burned at 1200°C. Such pellets showed n
compression strength of 100-200 Kg. and their sulphur contents were decreased by about 50 %.
Öz
Memleketimizde istihsal edilmekte bulunan demir cevherlerinden elde edilen tozların peietleme usulüyle
aglomerasyonunun mümkün olup olmadığını tahkik için başlanan bu araştırmada, ilk olarak Divriği
Dmir Madenlerine ait demir tozları üzerinde çalışılmış ve alman neticelere göre mezkûr tozlardan yüksek
fırında kullanılabilecek özellikte peletler yapmanın mümkün olduğu anlaşılmıştır.
Pelet haline getirilecek olan tozların, önce -100 meşten daha ince bir eb'ada öğütülmesi ve % 1-2 nisbelinde
bentonit ve yeteri kadar su ile karıştırıldıktan sonra, döner bir tamburda peletlenmesi ve bilâhare
105°C de kurutulup 12(KPC de yakılması gerekmektedir. Bu suretle hazırlanan peletlerin 100-200 Kg. îık
bir basınca karşı koyabildiği ve kükürt muhtevalarında '%50 nisbetinde bir azalma meydana geldiği yapı
lan deneylerle sabit olmuştur.
Ayrıntılar
| Diğer ID | JA42RE46ZJ |
|---|---|
| Bölüm | Makaleler |
| Yazarlar | |
| Yayımlanma Tarihi | 1 Şubat 1967 |
| Gönderilme Tarihi | 1 Şubat 1967 |
| Yayımlandığı Sayı | Yıl 1967 Cilt: 6 Sayı: 1 |
Kaynak Göster