A research on some physical and mechanical properties of Foetid juniper wood

Öz

Wood has been one of the most important engineering materials from the past to the present. Wood has many different uses as both firewood and raw materials. Wood raw material is widely used especially in wooden structures and furniture industry. The physical, mechanical, chemical properties and biological durability properties of wood are important features. When deciding on the use of solid wood, these features are taken into account. In this study, some important physical and mechanical properties of Foetid juniper wood (Juniperus foetidissima Wild.) have been investigated. Oven-dried density, swelling percentages, fiber saturation point, water uptake percentage, bending strength, elastic modulus, impact bending strength, static hardness values were determined. According to data obtained Oven-dried density, swelling percentages, fiber saturation point, water uptake percentage, bending strength, elastic modulus, impact bending strength, static hardness values were 525 kg/m3, 5.76%, 3.75%, 0.13%, 9.64%, 18.35%, 76,93% N/mm2, 6701 N/mm2, 0.28 kgm/cm2, 45.7 N/mm2, 43.8 N/mm2, 62 N/mm2, respectively.

Anahtar Kelimeler

• Wood,Foetid Juniper

Kokulu ardıç odununun bazı fiziksel ve mekanik özellikleri üzerine bir araştırma

Öz

Odun geçmişten günümüze kadar çok önemli mühendislik malzemelerinden birisi olmuştur. Hem yakacak odun ve hem de yapacak odun olarak birçok farklı kullanım alanına sahiptir. Özellikle ahşap yapılarda ve mobilya sektöründe oldukça fazla kullanılmaktadır. Odunun fiziksel, mekanik, kimyasal özellikleri ve biyolojik dayanıklılık özellikleri, önemli özellikleridir. Masif odunun kullanım yerine karar verirken, bu özelliklerine dikkat edilir. Bu çalışmada, kokulu ardıç (Juniperus foetidissima Wild.) odununun, bazı önemli fiziksel ve mekanik özellikleri araştırılmıştır. Tam kuru yoğunluk, genişleme yüzdeleri, genişleme anizotropisi, lif doygunluk noktası, su alma yüzdesi, eğilme direnci, elastikiyet modülü, şok direnci, statik sertlik değeri belirlenmiştir. Elde edilen verilere göre; tam kuru yoğunluk 525 kg/m3, teğet yönde genişleme %5.76, radyal yönde genişleme %3.75, boyuna yönde genişleme %0.13, hacmen genişleme %9.64, lif doygunluk noktası %18.35, su alma yüzdesi%76.8, eğilme direnci 93 N/mm2, eğilmede elastikiyet modülü 6701 N/mm2, şok direnci 0.28 kgm/cm2, teğet yüzeyde sertlik 45.7, radyal yüzeyde sertlik 43.8 ve enine yüzeyde sertlik62 N/mm2olarak tespit edilmiştir.

Anahtar Kelimeler

• Odun,Kokulu ardıç

Teşekkür

Bu çalışmada sunulan, testlerin yapılmasında yardımcı olan Prof. Dr. Bekir Cihad BAL’a teşekkür ederim.

Kaynakça

1. Anonim, (2015), Türkiye orman varlığı, T.C. Orman ve Su İşleri Bakanlığı, Orman Genel Müdürlüğü, Türkiye orman varlığı kitabı, Ankara.
2. As, N., Koç, H., Doğu, D., Atik, C., Aksu, B., Erdinler, S., (2001), Türkiye'de yetişen endüstriyel öneme sahip ağaçların anatomik, fiziksel, mekanik ve kimyasal özellikleri, İstanbul Üniversitesi, Orman Fakültesi Dergisi, 51(1), 71-88.
3. Ay, N., (1994), Duglas (Pseudotsuga Menziesii (mirb.) Franco) odununun anatomik, fiziksel ve mekanik özellikleri, KTÜ Orman Fakültesi, Doktora Tezi, Trabzon.
4. Ayata, Ü., (2019), İzmir yöresinde yetişen erik, karabiber ve tespih odunlarının statik sertliğinin belirlenmesi üzerine bir araştırma, Mobilya ve Ahşap Malzeme Araştırmaları Dergisi, 2 (2), 94-102.
5. Bal, B.C., (2011), Okaliptüs grandis (Eucalyptus grandis W. Hill ex maiden) odununun fiziksel ve mekanik özellikleri ve lamine ağaç malzeme üretiminde kullanılması üzerine araştırmalar, KSÜ Fen Bilimleri Enstitüsü, Doktora tezi, Kahramanmaraş.
6. Bal, B.C., Bektaş, İ, (2012), The physical properties of heartwood and sapwood of Eucalyptus grandis, ProLigno, 8 (4), 35-43.
7. Bal, B.C., Bektaş, İ., Kaymakçı, A., (2012), Toros sedirinde genç odun ve olgun odunun bazı fiziksel ve mekanik özellikleri, KSÜ, Mühendislik Bilimleri Dergisi, 15 (2),17-27.
8. Bal, B.C., Bektaş, İ., Tutuş, A., Kaymakçı, A., (2011), The within-tree variation in some physical properties in eucalyptus grandis grown in Karabucak Region, Düzce Üniversitesi, Orman Fakültesi Dergisi, 7 (2), 82-88.

9. Bal, B.C., Bektaş, İ., (2013), The mechanical properties of heartwood and sapwood of E.grandis grown in Karabucak, Turkey, Düzce Üniversitesi, Ormancılık Dergisi 9 (1),71-77.
10. Bal, B. C., Bektaş, İ., (2018a), Kayın ve kavak odunlarında bazı fiziksel özelliklerle yoğunluk ilişkisinin belirlenmesi, Mobilya ve Ahşap Malzeme Araştırmaları Dergisi, 1(1), 1-10. DOI: 10.33725/mamad.420917.
11. Bal, B. C., Bektaş, İ., (2018b), Odunun yoğunluğu ile bazı mekanik özellikleri arasındaki ilişkinin belirlenmesi üzerine bir araştırma, Mobilya ve Ahşap Malzeme Araştırmaları Dergisi, 1(2), 51-61. DOI: 10.33725/mamad.467353.
12. Bao, F.C., Jiang, Z.H., Jiang, X.M., Lu, X.X., Luo, X.Q., Zhang, S.Y., (2001), Differences in wood properties between juvenile wood and mature wood in 10 species in China, Wood Science and Technology, 35(2001), 363-375.
13. Bektaş, İ., (1997), Kızılçam (Pinus Brutia ten.) Odununun teknolojik özellikleri ve yörelere göre değişimi, İstanbul Üniversitesi, Fen bilimleri Enstitüsü, Doktora Tezi, İstanbul. Bozkurt, Y., Erdin, N., (1997), Ağaç Teknolojisi Ders Kitabı, İ.Ü. Orman Fakültesi, Yayın no: 445, S: 1, İstanbul.
14. Bozkurt, Y., Göker, Y.(1996), Fiziksel ve Mekanik Ağaç Teknolojisi, İÜ, Orman Fakültesi Yayınları, Üniversite Yayın No:3944, İstanbul.
15. Bozkurt, A. Y. (1971), Önemli bazı ağaç türleri odunlarının tanımı, teknolojik özellikleri ve kullanış yerleri, İstanbul Üniversitesi Orman Fakültesi Yayınları, İ.Ü. Yayın No: 1653, O.F. Yayın No: 177, İstanbul.
16. Efe, FT, Bal, B.C., (2016), Yüksek sıcaklıkta ısıl işlem görmüş kızılçam (Pinus brutia ten.) odununun sertlik değerlerinde meydana gelen değişmeler, Afyon Kocatepe Üniversitesi, Fen ve Mühendislik Bilimleri Dergisi, 2016 (Özel sayı), 79-86.
17. Gerhards, C.C., (2007), Effect of moisture content and temperature on the mechanical properties of wood: an analysis of immediate effects, Wood and Fiber Science, 14(1), 4-36.
18. Güleç, T., (2011), Kahramanmaraş bölgesinde büyük göknar kabuk böceği (Pityokteines curvidens)’den zarar görmüş Toros göknar odununun bazı fiziksel, kimyasal ve mekanik özelliklerinin belirlenmesi, Kahramanmaraş Sütçü İmam Üniversitesi, Fen Bilimleri Enstitüsü, Yüksek Lisans Tezi, Kahramanmaraş.
19. Gündüz, G. (1999), Camiyanı karaçamı (Pinus nigra Arn. subsp. pallasiana var. Pallasiana)’nın bazı anatomik, teknolojik ve kimyasal özellikleri, Zonguldak Karaelmas Üniversitesi, Fen Bilimleri Enstitüsü, Doktora Tezi, Zonguldak.
20. Kord, B., Kialashaki, A., Kord, B., (2010), The within-tree variation in wood density and shrinkage and their relationship in Populus euramericana, Turkish Journal of Agriculture and Forestry 34:1-6.
21. Malkoçoğlu, A., (1994), Doğu kayını (Fagus Orientalis L.) odununun teknolojik özellikleri, Karadeniz Teknik Üniversitesi, Fen Bilimleri Enstitüsü, Doktora Tezi, Trabzon.
22. Şanıvar, N., Zorlu, İ., (1980), Ağaç işleri gereç bilgisi temel ders kitabı, Mesleki ve Teknik Öğretim Kitapları, Milli Eğitim Basımevi, İstanbul, Etüt ve Programlama Dairesi Yayınları No: 43.
23. TS 2471 (1976), Odunda, fiziksel ve mekaniksel deneyler için rutubet miktarı tayini, Türk Standartları Enstitüsü (TSE), Ankara.
24. TS 2472 (1976), Odunda, fiziksel ve mekaniksel deneyler için birim hacim ağırlığı tayini, Türk Standartları Enstitüsü (TSE), Ankara.
25. TS 2474 (1976), Odunun statik eğilme dayanımının tayini, Türkiye Standartlar Enstitüsü (TSE), Ankara.
26. TS 2477 (1976), Odunun çarpmada eğilme dayanımının tayini, Türkiye Standartlar Enstitüsü (TSE), Ankara.
27. TS 2478 (1976), Odunun statik eğilmede elastiklik modülünün tayini, Türkiye Standartlar Enstitüsü (TSE), Ankara.
28. TS 2479 (1976), Odunun statik sertliğinin tayini, Türkiye Standartlar Enstitüsü (TSE), Ankara.
29. TS 4084 (1983), Odunda radyal ve teğet doğrultuda şişmenin tayini, Türkiye Standartlar Enstitüsü (TSE), Ankara.
30. TS 4086 (1983), Odunda hacimsel şişmenin tayini, Türkiye Standartlar Enstitüsü (TSE), Ankara.
31. Yıldız, S. (2002), Isıl işlem uygulanan doğu kayını ve doğu ladini odunlarının fiziksel, mekanik, teknolojik ve kimyasal özellikleri, Karadeniz Teknik Üniversitesi, Fen Bilimleri Enstitüsü, Doktora Tezi, Trabzon.