EFFECT OF PRESSING PRESSURE ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF NON-ALLOYED STEELS PRODUCED BY POWDER METALLURGY METHOD

Yıl 2017, Cilt: 6 Sayı: 1, 257 - 264, 31.01.2017
https://doi.org/10.28948/ngumuh.298186

Öz

   In this work, pressing pressure on microstructure and mechanical properties of non-alloyed powder metallurgy
(PM) steels were investigated. The mixed powders prepared in the predetermined proportions were pressed
unidirectionally under 650, 700, 750, 800 and 850 MPa. Samples of the tensile experiment were turned into
blocks by squeezing with the mould which had been prepared according to ASTM (E 8M) standards of powder
metal material tension sample. The pressed samples were sintered at argon atmosphere at 1200ºC for 1 hour. The
microstructure of the PM steels was characterised by optic microscope, SEM and EDS. Results indicated that
PM steel pressed at 750 MPa showed the highest values of yield strength and ultimate tensile strength. However,
when the amount of pressing pressure increased from 750 MPa to 850 MPa, yield strength, ultimate tensile
strength and elongation decreased. 

Kaynakça

  • JUN, D., LIU, Y.H., YU, S.R., LI, W.F. “Dry Sliding Friction and Wear Properties of Al2O3 and Carbon Short Fibres Reinforced Al-12Si Alloy Hybrid Composites”, Wear, 257, 930-940, 2004.
  • ERDEN, M.A., "Toz Metalürjisi İle Üretilen Çeliklerde Nikel İlavesinin Mikroyapı ve Mekanik Özellikler Üzerine Etkisinin Araştırılması" Gazi Üniversitesi Fen Bilimleri Dergisi Part C: Tasarım ve Teknoloji, 4(4), 241-245, 2016.

PRESLEME BASINCININ TOZ METALÜRJİSİ İLE ÜRETİLEN ALAŞIMSIZ ÇELİKLERİN MİKROYAPI VE MEKANİK ÖZELLİKLERİNE ETKİSİ

Yıl 2017, Cilt: 6 Sayı: 1, 257 - 264, 31.01.2017
https://doi.org/10.28948/ngumuh.298186

Öz

   Bu çalışmada, toz metalürjisi (TM) ile üretilen alaşımsız çeliklerde presleme basıncının mikroyapı mekanik
özellikleri üzerine etkisi araştırılmıştır. Belirlenen kimyasal kompozisyonda karıştırılan tozlar, ASTM (E 8M)
toz metal malzeme standartlarına uygun çekme numunesi şeklindeki kalıpta 650, 700, 750, 800 ve 850 MPa
presleme basıncılarında tek yönlü sıkıştırılarak blok haline getirilmiştir. Presleme işlemi gerçekleştirilen
numuneler argon atmosferinde 1200°C sinterleme sıcaklığında 1 saat sinterlenmiştir. Üretimi gerçekleştirilen
TM çeliklerinin mikroyapısı optik mikroskop, SEM ve EDS ile karakterize edilmiştir. Sonuçlar 750 MPa’da
preslenmiş TM çeliklerin en yüksek akma dayanımına ve çekme dayanımına sahip olduğunu göstermiştir. Fakat
presleme basıncının 750 MPa’dan 850 MPa’a çıkması ile akma dayanımı ve çekme dayanımı düşmüştür. 

Kaynakça

  • JUN, D., LIU, Y.H., YU, S.R., LI, W.F. “Dry Sliding Friction and Wear Properties of Al2O3 and Carbon Short Fibres Reinforced Al-12Si Alloy Hybrid Composites”, Wear, 257, 930-940, 2004.
  • ERDEN, M.A., "Toz Metalürjisi İle Üretilen Çeliklerde Nikel İlavesinin Mikroyapı ve Mekanik Özellikler Üzerine Etkisinin Araştırılması" Gazi Üniversitesi Fen Bilimleri Dergisi Part C: Tasarım ve Teknoloji, 4(4), 241-245, 2016.
Toplam 2 adet kaynakça vardır.

Ayrıntılar

Konular Malzeme Üretim Teknolojileri
Bölüm Malzeme ve Metalürji Mühendisliği
Yazarlar

Mehmet Akif Erden

Yayımlanma Tarihi 31 Ocak 2017
Gönderilme Tarihi 10 Haziran 2016
Kabul Tarihi 3 Eylül 2016
Yayımlandığı Sayı Yıl 2017 Cilt: 6 Sayı: 1

Kaynak Göster

APA Erden, M. A. (2017). PRESLEME BASINCININ TOZ METALÜRJİSİ İLE ÜRETİLEN ALAŞIMSIZ ÇELİKLERİN MİKROYAPI VE MEKANİK ÖZELLİKLERİNE ETKİSİ. Niğde Ömer Halisdemir Üniversitesi Mühendislik Bilimleri Dergisi, 6(1), 257-264. https://doi.org/10.28948/ngumuh.298186
AMA Erden MA. PRESLEME BASINCININ TOZ METALÜRJİSİ İLE ÜRETİLEN ALAŞIMSIZ ÇELİKLERİN MİKROYAPI VE MEKANİK ÖZELLİKLERİNE ETKİSİ. NÖHÜ Müh. Bilim. Derg. Ocak 2017;6(1):257-264. doi:10.28948/ngumuh.298186
Chicago Erden, Mehmet Akif. “PRESLEME BASINCININ TOZ METALÜRJİSİ İLE ÜRETİLEN ALAŞIMSIZ ÇELİKLERİN MİKROYAPI VE MEKANİK ÖZELLİKLERİNE ETKİSİ”. Niğde Ömer Halisdemir Üniversitesi Mühendislik Bilimleri Dergisi 6, sy. 1 (Ocak 2017): 257-64. https://doi.org/10.28948/ngumuh.298186.
EndNote Erden MA (01 Ocak 2017) PRESLEME BASINCININ TOZ METALÜRJİSİ İLE ÜRETİLEN ALAŞIMSIZ ÇELİKLERİN MİKROYAPI VE MEKANİK ÖZELLİKLERİNE ETKİSİ. Niğde Ömer Halisdemir Üniversitesi Mühendislik Bilimleri Dergisi 6 1 257–264.
IEEE M. A. Erden, “PRESLEME BASINCININ TOZ METALÜRJİSİ İLE ÜRETİLEN ALAŞIMSIZ ÇELİKLERİN MİKROYAPI VE MEKANİK ÖZELLİKLERİNE ETKİSİ”, NÖHÜ Müh. Bilim. Derg., c. 6, sy. 1, ss. 257–264, 2017, doi: 10.28948/ngumuh.298186.
ISNAD Erden, Mehmet Akif. “PRESLEME BASINCININ TOZ METALÜRJİSİ İLE ÜRETİLEN ALAŞIMSIZ ÇELİKLERİN MİKROYAPI VE MEKANİK ÖZELLİKLERİNE ETKİSİ”. Niğde Ömer Halisdemir Üniversitesi Mühendislik Bilimleri Dergisi 6/1 (Ocak 2017), 257-264. https://doi.org/10.28948/ngumuh.298186.
JAMA Erden MA. PRESLEME BASINCININ TOZ METALÜRJİSİ İLE ÜRETİLEN ALAŞIMSIZ ÇELİKLERİN MİKROYAPI VE MEKANİK ÖZELLİKLERİNE ETKİSİ. NÖHÜ Müh. Bilim. Derg. 2017;6:257–264.
MLA Erden, Mehmet Akif. “PRESLEME BASINCININ TOZ METALÜRJİSİ İLE ÜRETİLEN ALAŞIMSIZ ÇELİKLERİN MİKROYAPI VE MEKANİK ÖZELLİKLERİNE ETKİSİ”. Niğde Ömer Halisdemir Üniversitesi Mühendislik Bilimleri Dergisi, c. 6, sy. 1, 2017, ss. 257-64, doi:10.28948/ngumuh.298186.
Vancouver Erden MA. PRESLEME BASINCININ TOZ METALÜRJİSİ İLE ÜRETİLEN ALAŞIMSIZ ÇELİKLERİN MİKROYAPI VE MEKANİK ÖZELLİKLERİNE ETKİSİ. NÖHÜ Müh. Bilim. Derg. 2017;6(1):257-64.

download