In this study, the surface coating (modification) of micronized calcite (CaCO3, d50=135 μm) in a stirred media (bead) mill with stearic acid was investigated. As a result of 15 min grinding and 5 min coating experiments, a product with d50=2.15 μm and specific surface area of 3.21 m2/cm3 was obtained. The activation rate of this final product as an indicator of coating rate was 97.7%. According to the optimum coating results, the stearic acid rate was determined as 1%, the modification time was 7.5 min, the ball load was 900 g and the stirring speed was 600 rpm.
Calcite Stearic acid Surface modification Dry coating Active ratio
Scientific Research Projects (BAP) Coordination Unit of Niğde Ömer Halisdemir University
MMF-2022/02
Bu çalışmada mikronize kalsitin (CaCO3, d50=135 μm) stearik asitli karıştırmalı ortam (bilyalı) değirmende yüzey kaplaması (modifikasyonu) incelenmiştir. Yapılan 15 dak öğütme ve 5 dak kaplama deneyleri sonucunda d50=2,15 μm ve özgül yüzey alanı 3.21 m2/cm3 olan bir ürün elde edilmiştir. Kaplama oranının bir göstergesi olarak nihai ürünün aktive oranı %97.7 elde edilmiştir. Optimum kaplama sonuçlarına göre stearik asit oranı %1, modifikasyon süresi 7.5 dak, bilya yükü 900 gr ve karıştırma hızı 600 rpm olarak belirlenmiştir.
Kalsit Stearik asit Yüzey modifikasyonu Kuru kaplama Aktive oranı
Niğde Ömer Halisdemir Üniversitesi Bilimsel Araştırma Projeleri (BAP) Koordinasyon Birimi
MMF-2022/02
Birincil Dil | İngilizce |
---|---|
Konular | Endüstriyel Hammaddeler |
Bölüm | Makaleler |
Yazarlar | |
Proje Numarası | MMF-2022/02 |
Erken Görünüm Tarihi | 31 Mayıs 2024 |
Yayımlanma Tarihi | |
Gönderilme Tarihi | 13 Kasım 2023 |
Kabul Tarihi | 21 Mart 2024 |
Yayımlandığı Sayı | Yıl 2024 Cilt: 13 Sayı: 3 |