THE INVESTIGATION OF MICROHARDNESS VALUES IN TERMS OF TEMPERATURE AND DURATION OF AGED ALUMINIUM 2XXX AND 6XXX ALLOYS ACCORDING TO STATISTICS

Yıl 2009, Cilt 4, Sayı 1, 40 - 47, 01.02.2009

Öz

In this study, statistical values of microhardness were investigated in terms of temperature and duration of aged aluminium 2XXX and 6XXX alloys. AA 2024 and AA 6063 aluminum alloys were solution treated at two different temperatures of 490 °C and 520 °C. Then both samples were cooled to room temperature. After this process, the samples were aged at three different temperatures (140 °C, 180 °C, 220 °C) for ten different periods of time (2, 4, 6, 8, 10, 12, 14, 16, 18 and 20 h.). The microstructure of the aged was examined by optic analysis SEM-EDS and X-Ray. The hardness values of the aged were tested by microhardness tests. The samples were examined by Multivariate Analysis of Variance (MANOVA) with a confidence level of %95 to find out whether a statistically significant difference occurs. Temperature and duration on the wear behaviours of aged aluminium 2XXX and 6XXX alloys were statistically significant in microhardness values.

YAŞLANDIRILMIŞ 2XXX VE 6XXX ALÜMİNYUM ALAŞIMLARINDA SICAKLIK VE SÜRENİN MİKROSERTLİK DEĞERLERİNE ETKİSİNİN İSTATİSTİĞE GÖRE İNCELENMESİ

Yıl 2009, Cilt 4, Sayı 1, 40 - 47, 01.02.2009

Öz

Bu çalışmada, mikrosertliklerin istatistiksel değerleri yaşlandırılmış 2xxx ve 6xxx serisi alaşımların sıcaklık ve şartlarına gore incelenmiştir. AA2024 ve AA6063 alüminyum alaşımları 490 ve 520 C de çözeltiye alınmışlardır. Tüm örnekler oda sıcaklığında soğutulmuştur. Bu işlemden sonar üç farklı sıcaklıkta (140 °C, 180 °C, 220 °C)ve on farklı sürede (2, 4, 6, 8, 10, 12, 14, 16, 18, 20 saat) yaşlandırılmıştır. Yaşlandırılmış örneklerin mikroyapı incelemesi SEM- EDS de incelenmiş analizler X-Ray de gerçekleştirilmiştir. Istatistiksel olarakj farklılıklar olup olmadığını bulmak için %95 güvenirlikle MANOVA yardımıyla örnekler incelennmiştir. Sonuç olarak mikrosertlik değerlerinin güvenilir olduğu saptanmıştır.

Ayrıntılar

Birincil Dil Türkçe
Bölüm Elektrik Makinaları
Yazarlar

Ahmet MEYVECI Bu kişi benim


Ismail KARACAN Bu kişi benim


Emrah Hanifi Firat Bu kişi benim


Uğur ÇALIGÜLÜ Bu kişi benim


Hülya DURMUŞ Bu kişi benim

Yayımlanma Tarihi 1 Şubat 2009
Yayınlandığı Sayı Yıl 2009, Cilt 4, Sayı 1

Kaynak Göster

Bibtex @ { nwsatecapsci213979, journal = {Technological Applied Sciences}, eissn = {1308-7223}, address = {}, publisher = {E-Journal of New World Sciences Academy}, year = {2009}, volume = {4}, number = {1}, pages = {40 - 47}, doi = {10.12739/10.12739}, title = {YAŞLANDIRILMIŞ 2XXX VE 6XXX ALÜMİNYUM ALAŞIMLARINDA SICAKLIK VE SÜRENİN MİKROSERTLİK DEĞERLERİNE ETKİSİNİN İSTATİSTİĞE GÖRE İNCELENMESİ}, key = {cite}, author = {Meyvecı, Ahmet and Karacan, Ismail and Firat, Emrah Hanifi and Çalıgülü, Uğur and Durmuş, Hülya} }
APA Meyvecı, A. , Karacan, I. , Firat, E. H. , Çalıgülü, U. & Durmuş, H. (2009). YAŞLANDIRILMIŞ 2XXX VE 6XXX ALÜMİNYUM ALAŞIMLARINDA SICAKLIK VE SÜRENİN MİKROSERTLİK DEĞERLERİNE ETKİSİNİN İSTATİSTİĞE GÖRE İNCELENMESİ . Technological Applied Sciences , 4 (1) , 40-47 . Retrieved from https://dergipark.org.tr/tr/pub/nwsatecapsci/issue/20185/213979
MLA Meyvecı, A. , Karacan, I. , Firat, E. H. , Çalıgülü, U. , Durmuş, H. "YAŞLANDIRILMIŞ 2XXX VE 6XXX ALÜMİNYUM ALAŞIMLARINDA SICAKLIK VE SÜRENİN MİKROSERTLİK DEĞERLERİNE ETKİSİNİN İSTATİSTİĞE GÖRE İNCELENMESİ" . Technological Applied Sciences 4 (2009 ): 40-47 <https://dergipark.org.tr/tr/pub/nwsatecapsci/issue/20185/213979>
Chicago Meyvecı, A. , Karacan, I. , Firat, E. H. , Çalıgülü, U. , Durmuş, H. "YAŞLANDIRILMIŞ 2XXX VE 6XXX ALÜMİNYUM ALAŞIMLARINDA SICAKLIK VE SÜRENİN MİKROSERTLİK DEĞERLERİNE ETKİSİNİN İSTATİSTİĞE GÖRE İNCELENMESİ". Technological Applied Sciences 4 (2009 ): 40-47
RIS TY - JOUR T1 - YAŞLANDIRILMIŞ 2XXX VE 6XXX ALÜMİNYUM ALAŞIMLARINDA SICAKLIK VE SÜRENİN MİKROSERTLİK DEĞERLERİNE ETKİSİNİN İSTATİSTİĞE GÖRE İNCELENMESİ AU - Ahmet Meyvecı , Ismail Karacan , Emrah Hanifi Firat , Uğur Çalıgülü , Hülya Durmuş Y1 - 2009 PY - 2009 N1 - DO - T2 - Technological Applied Sciences JF - Journal JO - JOR SP - 40 EP - 47 VL - 4 IS - 1 SN - -1308-7223 M3 - UR - Y2 - 2022 ER -
EndNote %0 Technological Applied Sciences YAŞLANDIRILMIŞ 2XXX VE 6XXX ALÜMİNYUM ALAŞIMLARINDA SICAKLIK VE SÜRENİN MİKROSERTLİK DEĞERLERİNE ETKİSİNİN İSTATİSTİĞE GÖRE İNCELENMESİ %A Ahmet Meyvecı , Ismail Karacan , Emrah Hanifi Firat , Uğur Çalıgülü , Hülya Durmuş %T YAŞLANDIRILMIŞ 2XXX VE 6XXX ALÜMİNYUM ALAŞIMLARINDA SICAKLIK VE SÜRENİN MİKROSERTLİK DEĞERLERİNE ETKİSİNİN İSTATİSTİĞE GÖRE İNCELENMESİ %D 2009 %J Technological Applied Sciences %P -1308-7223 %V 4 %N 1 %R %U
ISNAD Meyvecı, Ahmet , Karacan, Ismail , Firat, Emrah Hanifi , Çalıgülü, Uğur , Durmuş, Hülya . "YAŞLANDIRILMIŞ 2XXX VE 6XXX ALÜMİNYUM ALAŞIMLARINDA SICAKLIK VE SÜRENİN MİKROSERTLİK DEĞERLERİNE ETKİSİNİN İSTATİSTİĞE GÖRE İNCELENMESİ". Technological Applied Sciences 4 / 1 (Şubat 2009): 40-47 .
AMA Meyvecı A. , Karacan I. , Firat E. H. , Çalıgülü U. , Durmuş H. YAŞLANDIRILMIŞ 2XXX VE 6XXX ALÜMİNYUM ALAŞIMLARINDA SICAKLIK VE SÜRENİN MİKROSERTLİK DEĞERLERİNE ETKİSİNİN İSTATİSTİĞE GÖRE İNCELENMESİ. NWSA. 2009; 4(1): 40-47.
Vancouver Meyvecı A. , Karacan I. , Firat E. H. , Çalıgülü U. , Durmuş H. YAŞLANDIRILMIŞ 2XXX VE 6XXX ALÜMİNYUM ALAŞIMLARINDA SICAKLIK VE SÜRENİN MİKROSERTLİK DEĞERLERİNE ETKİSİNİN İSTATİSTİĞE GÖRE İNCELENMESİ. Technological Applied Sciences. 2009; 4(1): 40-47.
IEEE A. Meyvecı , I. Karacan , E. H. Firat , U. Çalıgülü ve H. Durmuş , "YAŞLANDIRILMIŞ 2XXX VE 6XXX ALÜMİNYUM ALAŞIMLARINDA SICAKLIK VE SÜRENİN MİKROSERTLİK DEĞERLERİNE ETKİSİNİN İSTATİSTİĞE GÖRE İNCELENMESİ", Technological Applied Sciences, c. 4, sayı. 1, ss. 40-47, Şub. 2009, doi:10.12739/10.12739