FATIGUE PROPERTIES OF SPRING REINFORCES POLYMER GEARS

Abstract

Failure of gears, occur surface pressure stress and fracture at base of teeth. For steel gears, it is known that process of carburizing increases fatigue strength. Internal stress on the surface increases of fracture fatigue strength. In this study fatigue properties of polypropylene gear reinforced with 1.2 mm wire diameter metallic springs was investigated. Extension springs were used as reinforcement element and placed into the mould and stretched before injection of polypropylene material into the mould. After injection of polypropylene, stretched springs were loosened in order to obtain pre-stressing. Fatigue tests were performed on the produced gear. Reinforcement increased the strength of gears. At result of experiments, pre-stressing increase in service life 12 times more than that of specimens without reinforcement.

Keywords

• Polymer gears, Reinforcement, Fatigue, Pre-stressing

YAY TAKVİYELİ PLASTİK DİŞLİLERİN YORULMA ÖZELLİKLERİ

Öz

Dişlilerde hasar, diş dibinden kırılma ve yüzey basıncı ile oluşmaktadır. Çelik dişlilerde, karbürleme işlemi ile dişlilerin yorulma dayanımları artmaktadır. Kırılma yorulma dayanımının artışında, yüzeyde oluşan bası iç gerilmelerinin büyük etkisi vardır. Bu çalışmada, içine 1.2 mm tel çapına sahip yaylar yerleştirilmiş polipropilenden üretilmiş dişli çarkların özellikleri incelenmiştir. Yaylar, enjeksiyon kalıplama öncesi çekilip; kalıplama sonrası bırakılarak öngerilme oluşturulmuştur. Yorulma deneyleri gerçekleştirilmiş ve takviye yapılmasının dayanımı artırdığı görülmüştür. Deneyler sonucunda öngerilmenin, plastik dişlinin yorulma ömrünü takviyesiz numuneye göre 12 kata kadar artırdığı bulunmuştur.

Anahtar Kelimeler

• Plastik dişliler, Yay takviyesi, Yorulma dayanımı, Öngerilme