The Effect of Cooling Rate on Microstructure and Mechanical Properties of Al-Mg-Si (6063) Alloy

Abstract

In this study, the effect of cooling rate on microstructure and mechanical properties of Al-Mg-Si (6063) alloys was investigated. In order to obtain different cooling rate, samples heat treated at 520 oC for 2 h and then cooled in furnace, sand, air, oil and water environments. A decrease in the cooling rate caused the growth of grains and precipitates as the strength of Al-Mg-Si alloys reduced. As a result, Al-Mg-Si alloy was found to change significantly the properties of strength and forming depending on the cooling conditions.

Keywords

• Aluminium alloy, Cooling rate, Mechanical properties

Al-Mg-Si Alaşımının Mikroyapı ve Mekanik Özelliklerine Soğuma Hızının Etkisi

Öz

Bu çalışmada, soğuma hızının Al-Mg-Si (6063) alaşımından elde edilen numunelerin mikroyapı ve mekanik özelliklerine etkisi deneysel olarak araştırılmıştır. Farklı soğuma hızı elde edebilmek için numuneler 520 °C’de 2 saat solüsyona alındıktan sonra fırın, kum, hava, yağ ve su ortamlarında soğutulmuşlardır. Soğuma hızının düşmesi tane ve çökeltilerin büyümesine neden olarak Al-Mg-Si alaşımının dayanımını düşürmüştür. Çalışma sonucunda soğuma şartlarına bağlı olarak Al-Mg-Si alaşımının dayanım ve şekillenebilme özelliklerinde belirgin bir değişme olduğu tespit edilmiştir.

Anahtar Kelimeler

• Anahtar Mekanik özellikler kelimeler

Kaynakça

1. Altenpohl DG. Aluminum Technology, Applications and Environment, A Profile of a Modern Metal. 6th ed. NYS, USA, Wiley, 1998.
2. Troeger LP, Starke EA. “Microstructural and Mechanical Characterization of a Superplastic 6xxx Aluminum Alloy”. Materials Science and Engineering: A, 277(1-2), 102-113, 2000.
3. Helby M. “Aluminium Extrusion”. A Flexible Approach Construction Mater World”. 1, 101–102, 1993.
4. Sun Y. Wear Behavior of Heat Treatable Aluminium Alloys. MSc Thesis, İstanbul Technical University, İstanbul, Turkey, 1998. [5] Şendeniz M. Seçilen Bir Al-Mg-Si Alaşımının (AlMgSi0.5: Değişimlerinin İncelenmesi. Yüksek Lisans Tezi, Uludağ Üniversitesi, Bursa, Türkiye, 2006. Özellik
5. Siddiqui RA, Abdullah HA. “Influence of aging Parametres on the Mechanical Properties of 6063 Aluminium Alloy”. Journal of Materials Processing Technology, 102, 234-240, 2000.
6. Gavgali M, Totik Y, Sadeler R. “The Effect of Artificial Aging on Wear Properties of AA 6063 Alloy”. Materials Letters, 57(24-25), 3713-3721, 2003.
7. Rafiq AS, Hussein AA, Khamis RA. “Infuence of Aging Parameters on the Mechanical Properties of 6063 Aluminium Alloy”. Journal of Materials Processing Technology, 102, 234-240, 2000.
8. Meyveci A. Yaşlandırılmış 2XXX ve 6XXX Serisi Alüminyum Alaşımlarının Aşınma Davranışlarının İncelenmesi. Yüksek Lisans Tezi, Karabük Üniversitesi, Karabük, Türkiye, 2007.

9. Gündüz S. “Kimyasal Bileşim ve Soğuma Hızının Arayer Atomu İçermeyen Mikroalaşım Çeliklerinin Mekanik Özelliklerine Etkisi”. Gazi Üniversitesi Fen Bilimleri Enstitüsü Dergisi, 16(1), 171–178, 2003.
10. Gündüz G, Kaçar R. "Strengthening of 6063 Aluminium Alloy 46(6), 345-350, 2008. Kovove Materialy,
11. Güleryüz K, Kaçar R. “Deformasyon Yaşlanmasının AA7075 Alüminyum Alaşımının Mekanik Özelliklerine Etkisinin İncelenmesi”. 6th International Advanced Technologies Symposium (IATS’11), Elazığ, Türkiye, 16-18 May 2011.