Öz
In this work, steel chemistry and the effects of the cooling rate on the yield behaviour in Ti-V-Al interstitial free steel were investigated experimentally for six grades of steel plate. The steels were austenitised at 950 ± 10 °C for 15 minutes and then cooled at different cooling rates in order to see the effect of different cooling rates on yield behaviour of interstitial free steels. Reducing the cooling rate reduces the yield point elongation and is conducive to continuous yielding. Grains are coarsening during slow cooling, this decrease yield strength of the steels. Vanadium additions allow discontinuous yielding over a wide range of cooling rates compared to Ti steels.
Anahtar Kelimeler
Öz
Bu çalışmada çelik kimyası ve soğuma hızının arayer atomu içermeyen Ti-V-Al çeliklerindeki akma noktasına etkisi altı çeşit çelik levha için deneysel olarak araştırılmıştır. Çelikler, 950 ± 10 °C de 15 dakika östenitleme işlemi uygulandıktan sonra farklı soğuma hızlarının arayer atomu içermeyen çeliklerdeki akma noktası üzerine etkisini araştırmak için farklı soğuma hızlarında soğutulmuştur. Soğuma hızının düşmesi akma noktası uzamasını düşürerek sürekli akma davranışına sebep olmuştur. Yavaş soğuma süresince taneler büyüyerek, çeliklerin akma dayanımını düşürmüştür. Çeliklere vanadyum'un eklenmesi, titanyum çelikleriyle karşılaştırıldığında geniş bir soğuma aralığında sürekli olmayan akmaya izin vermiştir.
Anahtar Kelimeler
Ayrıntılar
| Birincil Dil | Türkçe |
|---|---|
| Bölüm | Makale |
| Yazarlar | |
| Yayımlanma Tarihi | 1 Şubat 2001 |
| Yayımlandığı Sayı | Yıl 2001 Cilt: 7 Sayı: 2 |