Al2O3 Ceramics with Graded Porosity Produced from Natural and Artificial Pore Formers
Öz
Al2O3
ceramics with graded porosity were produced by using corn starch and PMMA
sphere as pore former additives (PFA). Graded porosity was obtained by
uniaxially pressing the stacks of Al2O3 mixtures with and
without PFA together. Pressed samples were heat-treated to remove PFAs at 600oC
and sintered at 1540oC. Final porosity of graded ceramics produced
from starch and PMMA were measured as 12 and 16%, obtained median pore size
were 3 and 11 µm, respectively. The elastic moduli of the samples were measured
by pulse-echo method and results showed that moduli values of the samples
varied significantly depending on the PFA type. PMMA added samples had lower
elastic moduli values than starch added ceramics as a result of higher pore
size and interconnected pore structure. By using the pulse-echo method, the
elastic properties of the graded samples couldn’t be measured effectively.
Anahtar Kelimeler
Kaynakça
- 1. Studart, A.R., Gonzenbach, U.T., Tervoort, E., Gauckler, L.J., “Processing routes to macroporous ceramics: A review”, Journal of the American Ceramic Society, 89 (6): 1771–1789 (2006).
- 2. Miao, X., Sun, D., “Graded/gradient porous biomaterials”, Materials, 3: 26-47, (2010).
- 3. Tampieri, A., Celotti, G., Sprio, S., Delcogliano, A., Franzese, S., “Porosity-graded hydroxyapatite ceramics to replace natural bone”, Biomaterials, 22: 1365-1370, (2001).
- 4. Li, J-F, Takagi, K., Ono, M., Pan, W., Watanabe, R., Almajid, A., Taya, M., “Fabrication and evaluation of porous piezoelectric ceramics and porosity-graded piezoelectric actuators”, Journal of the American Ceramic Society, 86(7): 1094–1098 (2003).
- 5. Werner, J., Linner-Kremar, B., Friess, W., Greila, P., “Mechanical properties and in vitro cell compatibility of hydroxyapatite ceramics with graded pore structure”, Biomaterials, 23: 4285-4294, (2002).
- 6. Roy, W.R., “Porosity of ceramics”, Marcel Dekker Inc, New York, (1996).
- 7. Asmani, M., Kermel, C., Leriche, A., Ourak, M., “Influence of porosity on Young’s modulus and poisson’s ratio in alumina ceramics”, Journal of the European Ceramic Society, 21: 1081-1086, (2001).
- 8. Deng, Z-Y, Fukasawa, T., Ando, M., “Microstructure and mechanical properties of porous alumina ceramics fabricated by the decomposition of aluminum hydroxide”, Journal of the American Ceramic Society, 84(11): 2638–2644, (2001).
Ayrıntılar
Birincil Dil
Türkçe
Konular
Mühendislik
Bölüm
Araştırma Makalesi
Yazarlar
Yayımlanma Tarihi
15 Eylül 2017
Gönderilme Tarihi
22 Eylül 2017
Kabul Tarihi
-
Yayımlandığı Sayı
Yıl 2017 Cilt: 20 Sayı: 3