Effects of Filler Ratio on Mechanical Properties at Marble Powder/Polyester Composites

Öz

Marble dust, a by-product of the marble industry, has environmental and economic impact. Marble dust is utilized in several industrial processes. In this study the manufacturing of composite material with polyester matrix was realized and the mechanical properties of obtained materials were examined. Marble/polyester ratio was varied as 3; 3,5; 4; 4,5 and 5. The best micrograph of SEM was recorded at the marble/polyester ratio of 4. This composite material demonstrated the highest hardness (96 Shore A; 186.3 kg/mm2Vickers) and three point bending strength (60,17 N/mm2) values

Anahtar Kelimeler

• Marble powder, polymer composite material, SEM

Mermer Tozu/Polyester Kompozitlerde Dolgu Oranının Mekanik Özelliklere Etkileri

Öz

Günümüzde mermer işletmelerinde açığa çıkan atık tozlar gerek ekonomik, gerekse çevresel yönden önemli etkilere sahiptir. Atık mermer tozlarının sanayinin çeşitli dallarında değerlendirilmesi mümkündür. Çalışmada polyester matrisli kompozit malzeme üretimi gerçekleştirilmiş ve elde edilen malzemelerin mekanik özellikleri incelenmiştir. Mermer/polyester oranları kütlece 3; 3,5; 4; 4,5 ve 5 olarak değiştirilmiştir. Test sonuçları mermer/polyester oranının 4 olduğu durumda malzemenin diğerlerine göre daha yüksek mukavemet ve sertlik değerlerine sahip olduğunu göstermiş olup, en iyi SEM görüntüleri de bu oranda alınmıştır. Optimum oranda elde edilen numunedeki ölçülen sertlik Shore A cinsinden 96, Vickers sertliği 186,3 kg/mm2 ve üç noktadan eğmede çekme mukavemeti değeri ise 60,17 N/mm2olarak bulunmuştur.

Anahtar Kelimeler

• Mermer tozu, polimer kompozit malzeme, SEM