Deposition and Characterization of ZnSnSe2 Thin-Films Deposited by Using Sintered Stoichiometric Powder

Öz

In this work, ZnSnSe2 (ZTSe) thin films were deposited using crystalline powder grown by vertical Bridgman-Stockbarger technique. The deposition process was carried out by means of e-beam evaporation on the well-cleaned soda lime glass substrates and keeping them at the substrate temperature of 200°C. The structural, optical and electrical properties of ternary ZTSe thin films were investigated depending on the annealing temperature at 250 and 300°C. X-ray diffraction analysis showed that as-grown films were in amorphous structure, however annealing at 250°C triggered the crystallization on the preferred ternary structure and annealing at 300°C resulted in the changes from amorphous to the polycrystalline structure. Using the compositional analysis, the detail information about the stoichiometry and the segregation mechanisms of the constituent elements in the structure were determined for both as-grown and annealed samples. In addition, they were morphologically characterized using scanning electron microscopy technique. The electrical properties were analyzed using temperature dependent dark- and photo-conductivity measurements. From the variation of electrical conductivity as a function of the ambient temperature, the current transport mechanisms and corresponding activation energies at specific temperature intervals for each sample were determined. The optical properties for the ZTSe thin films were studied depending on the structural changes with annealing.

Anahtar Kelimeler

• Thin film,deposition,characterization

Kaynakça

1. [1] https://www.ise.fraunhofer.de/content/dam/ise/de/documents/publications/studies/Photovoltaics-Report.pdf
2. [2] G. Stechmann, S. Zaefferer, P. Konijnenberg, D. Raabe, C. Gretener, L. Kranz, J. Perrenoud, S. Buecheler, and A. N. Tiwari, ‘3-Dimensional microstructural characterization of CdTe absorber layers from CdTe/CdS thin film solar cells’, Sol. Energy Mater. Sol. Cells, 151:66–80, (2016).
3. [3] http://www.solarfrontier.com/eng/news/2017/1220_press.html.
4. [4] First Solar CdTe cell hits 22.1% efficiency’. [Online]. Available: http://optics.org/news/7/2/29. [Accessed: 25-Jun-2017].
5. [5] F. Liu, Y. Li, K. Zhang, B. Wang, C. Yan, Y. Lai, Z. Zhang, J. Li and Y. Liu,” In situ growth of Cu2ZnSnS4 thin films by reactive magnetron co-sputtering” Sol. Energy Mat. Sol. C.,94: 2431-2434, (2010).
6. [6] J. Kim, H. S. Lee and N. M. Park,” Post-annealing effect on the reactively sputter-grown CIGS thin films and its influence to solar cell performance Curr. Appl. Phys.,14: 63-68, (2014).
7. [7] M.A. Green, K. Emery, Y. Hishikawa, W. Warta, and E.D. Dunlop, “Solar cell efficiency tables (Version 38)”, Prog. Photovolt. Res. Appl. 19: 565-572 (2011)
8. [8] R Kamada, T. Yagioka, S. Adachi, A. Handa, K. Fai Tai, T. Kato, and H. Sugimoto, “New World Record Cu(In,Ga)(Se,S)2 Thin Film Solar Cell Efficiency

9. [9] Beyond 22% “, IEEE 43rd Photovolt. Spec. Confrence ,1287-1291, (2016).
10. [10] K. Sharma, B. L. Williams, A. Mittal, H. C. M. Knoops, B. J. Kniknie, N. J. Bakker, W. M. M. Kessels, R. E. I. Schropp and M. Creatore,” Expanding Thermal Plasma Chemical Vapour Deposition of ZnO:Al Layers for CIGS Solar Cells” Int. J. Photoenergy , 2014: 1-9, (2014).
11. [11] S.P. Yadav, P.S. Shinde, K.Y. Rajpure, C.H. Bhosale,” Photoelectrochemical properties of spray deposited n-ZnIn2Se4 thin films” Sol. Energy Mat. Sol. C. ,92: 453-456, (2008).
12. [12] S. Gul, J. K. Cooper, C. Corrado, B. Vollbrecht, F. Bridges, J. Guo, and J. Z. Zhang, J. Phys. Chem. C 115, 20864, (2011).
13. [13] L. Wang, M. Lu, X. Wang, Y. Yu, X. Zhao, P. Lv, H. Song, X. Zhang, L. Luo, C. Wu, Y. Zhang and J. Jie, “Tuning the p-type conductivity of ZnSe nanowires via silver doping for rectifying and photovoltaic device applications”, J. Mater. Chem. A, 1: 1148-1154, (2013).
14. [14] R. Kuronuma, Y. Miyamoto and Y. Mita, “Photoluminescence Characteristics of Sn-Doped, Molecular-Beam-Epitaxy-Grown ZnSe Crystal Layers”, Jpn. J. Appl. Phys. 45: 7789-7791, (2006).
15. [15] S. Adachi, “Earth-Abundant Materials for Solar Cells: Cu2-II-IV-VI4 Semiconductors”, John Wiley & Sons, Inc., United Kingdom, (2015).
16. [16] X. Sun ,Y. He and J. Feng, “Growth and characterization of ZnIn2Se4 buffer layer on CuInSe2 thin films”, J. Cryst. Growth, 312:48-51,(2009).
17. [17] H.M. Zeyada, M.S. Aziz and A.S. Behairy, “Structure formation and mechanisms of DC conduction in thermally evaporated nanocrystallite structure ZnIn2Se4 thin films”, Physica B ,404: 3957-3963, (2009).
18. [18] S. H. Choe, “Optical energy gaps of undoped and Co-doped ZnIn2Se4 single crystals”, Curr. Appl. Phys. ,9:1-3, (2009).
19. [19] E. R. Shaaban, “Optical constants and fitted transmittance spectra of varies thickness of polycrystalline ZnSe thin films in terms of spectroscopic ellipsometry”, J. Alloy Compd. ,563: 274-279, (2013).
20. [20] D. K. Schroder, “Semiconductor Material and Device Characterization” , John Wiley & Sons, Inc., New Jersey, (2006).