Investigation of Wear Performance of Different Amount SiC Reinforcements A356 Matrix Composite Materials Produced by Semi-Solid Process Method

Yıl 2020, , 1237 - 1243, 01.12.2020
https://doi.org/10.2339/politeknik.642506

Öz

In this study, the wear performance of A356 matrix
composite materials produced by different amount SiC reinforcement semi-solid
moulding method was investigated. In the A356 matrix, was added four different
amounts (5%, 10, 15 and 20) SiC. Composite powders mixed without ball (30
minutes) in the vibrating type mill were cold pressed (800 MPa) and green
compacts were produced. The produced green compacts, in 550 °C mold temperature
and in 600 °C furnace temperature, 100 MPa pressing force was pressed for 1 minute.
Produced samples were characterized with microstructure, hardness and
sphericity ratio. The wear tests were performed using a pin on-disk type wear
testing device with 0.2 ms-1 sliding speed, under two different
loads (30 and 60 N) and at four different sliding distances (500 m, 1000, 1500
and 2000). As a result of the studies, the hardness increases with increasing
amount of SiC in the composite material, while the sphericity rates decrease.
As a result of the wear tests, while the highest weight loss, 5% SiC was
obtained, the lowest weight loss was obtained in 20% SiC additional composite
materials.

Kaynakça

  • Ghandvar H., Farahany S., and Idris M. H., “Effect of wettability enhancement of SiC particles on impact toughness and dry sliding wear behavior of compocasted A356/20SiCp composites”, Tribology Transactions, 61(1): 88-99, (2018).
  • Hirata Y., Suzue N., Matsunaga N., and Sameshima S., “Particle size effect of starting SiC on processing, microstructures and mechanical properties of liquid phase-sintered SiC”, Journal of the European Ceramic Society, 30(9): 1945-1954, (2010).
  • Hamid A. A., Ghosh P. K., Jain S. C. and Ray S., “The influence of porosity and particles content on dry sliding wear of cast in situ Al (Ti)-Al2O3 (TiO2) composite”, Wear, 265(1-2): 14-26, (2008).
  • Akbari M., Shojaeefard M. H., Asadi P., and Khalkhali A., “Wear performance of A356 matrix composites reinforced with different types of reinforcing particles”, Journal of Materials Engineering and Performance, 26(9): 4297-4310, (2017).
  • Vijeesh V., and Prabhu K.N., “Review of microstructure evolution in hypereutectic Al-Si alloys and its effect on wear properties”, Transactions of the Indian Institute of Metals, 67(1): 1-18, (2014).
  • Shamsipour M., Pahlevani Z., Shabani M. O., and Mazahery A., “Optimization of the EMS process parameters in compocasting of high-wear-resistant Al-nano-TiC composites”, Applied Physics A, 122(4): 457-465, (2016).
  • Akbari M., Aliha M. R. M., Keshavarz S. M. E., and Bonyadi A., “Effect of tool parameters on mechanical properties, temperature, and force generation during FSW”, Proceedings of the Institution of Mechanical Engineers, Part L: Journal of Materials: Design and Applications, 233(6): 1033-1043, (2019).
  • Tutunchilar S., Givi M. B., Haghpanahi M., and Asadi P., “Eutectic Al–Si piston alloy surface transformed to modified hypereutectic alloy via FSP”, Materials Science and Engineering: A, 534: 557-567, (2012).
  • Özyürek D., Yıldırım M., and Çiftçi İ., “The tribological properties of A356-SiCp metal-matrix composites fabricated by thixomoulding technique”, Science and Engineering of Composite Materials, 19(4): 351-356, (2012).
  • Atkinson H. V. , “Alloys for semi-solid processing”, In Solid State Phenomena, Trans Tech Publications, 192: 16-27, (2013).
  • Zhang Q. Q., Cao Z. Y., Zhang Y. F., Su G. H., and Liu Y. B., “Effect of compression ratio on the microstructure evolution of semisolid AZ91D alloy”, Journal of Materials Processing Technology, 184(1-3): 195-200, 2007.
  • Seo P. K., Kim D. U., and Kang C. G., “The effect of the gate shape on the microstructural characteristic of the grain size of Al-Si alloy in the semi-solid die casting process”, Materials Science and Engineering: A, 445: 20-30, (2007).
  • Aztekin H., Ōzyūrek D., and Çetinkaya K., “Production of hypo-eutectic Αl-Si alloy based metal matrix composite with thixomoulding processing”, High Temperature Materials and Processes, 29(3): 169-178, (2010).
  • Şi̇mşek İ., Şimşek D., Özyürek D., “Yarı-katı işlem yöntemi ile üretilen Al-SiC kompozit malzemelerin aşınma davranışlarının incelenmesi”, 3rd International Symposium on Innovative Approaches in Scientific Studies, Ankara/Turkey, 4(1): 545-548, (2019).
  • Alhawari K. S., Omar M. Z., Ghazali M. J., Salleh M. S., and Mohammed M. N., “Microstructural evolution during semi solid processing of Al-Si-Cu alloy with different Mg contents”, Transactions of Nonferrous Metals Society of China, 27(7): 1483-1497, (2017).
  • Şimşek İ., Yıldırım M., Tunçay T., Özyürek D., Şimşek D., “Mekanik alaşımlama/öğütme yöntemi ile üretilen Al-SiC kompozitlerin incelenmesi”, Technological Applied Sciences, 13(2): 165-171, (2018).

Yarı Katı Kalıplama Yöntemi İle Üretilen Farklı Miktarlarda SiC Takviyeli A356 Matrisli Kompozit Malzemelerin Aşınma Performansının İncelenmesi

Yıl 2020, , 1237 - 1243, 01.12.2020
https://doi.org/10.2339/politeknik.642506

Öz

Bu
çalışmada, farklı miktarlarda SiC ilave edilerek yarı katı kalıplama yöntemi
ile üretilen Al A356 matrisli kompozit malzemelerin aşınma davranışları
incelenmiştir. Al A356 matrise, ağırlıkça 4 farklı oranda (%5, 10, 15 ve 20)
SiC ilave edilmiştir. Titreşimli tip değirmende bilyesiz olarak (30 dakika)
karıştırılan tozlar, soğuk preslenerek (800 MPa) ham numuneler üretilmiştir.
Üretilen ham numuneler 550 °C kalıp sıcaklığı ve 600 °C fırın sıcaklığında 30
dakika ortam atmosferinde bekletilmiş ve 100 MPa basınç ile 1 dakika
preslenmiştir. Üretilen numuneler mikroyapı, sertlik ve küresellik oranı ile
karakterize edilmiştir. Aşınma testleri standart pin on-disk aşınma test
cihazında 0,2 ms-1 kayma hızı, iki farklı yük (30 ve 60 N) ve dört
farklı aşınma mesafesi (500, 1000, 1500 ve 2000 m) kullanılarak yapılmıştır.
Yapılan çalışmalar sonucunda, kompozit malzeme içerisinde artan SiC miktarı ile
sertlik artarken, küresellik oranları ise azalmaktadır. Aşınma testleri
sonucunda en yüksek ağırlık kaybı %5 SiC içeren numunelerde elde edilirken, en
düşük ağırlık kaybı ise %20 SiC ilave kompozit malzemelerde elde edilmiştir.

Kaynakça

  • Ghandvar H., Farahany S., and Idris M. H., “Effect of wettability enhancement of SiC particles on impact toughness and dry sliding wear behavior of compocasted A356/20SiCp composites”, Tribology Transactions, 61(1): 88-99, (2018).
  • Hirata Y., Suzue N., Matsunaga N., and Sameshima S., “Particle size effect of starting SiC on processing, microstructures and mechanical properties of liquid phase-sintered SiC”, Journal of the European Ceramic Society, 30(9): 1945-1954, (2010).
  • Hamid A. A., Ghosh P. K., Jain S. C. and Ray S., “The influence of porosity and particles content on dry sliding wear of cast in situ Al (Ti)-Al2O3 (TiO2) composite”, Wear, 265(1-2): 14-26, (2008).
  • Akbari M., Shojaeefard M. H., Asadi P., and Khalkhali A., “Wear performance of A356 matrix composites reinforced with different types of reinforcing particles”, Journal of Materials Engineering and Performance, 26(9): 4297-4310, (2017).
  • Vijeesh V., and Prabhu K.N., “Review of microstructure evolution in hypereutectic Al-Si alloys and its effect on wear properties”, Transactions of the Indian Institute of Metals, 67(1): 1-18, (2014).
  • Shamsipour M., Pahlevani Z., Shabani M. O., and Mazahery A., “Optimization of the EMS process parameters in compocasting of high-wear-resistant Al-nano-TiC composites”, Applied Physics A, 122(4): 457-465, (2016).
  • Akbari M., Aliha M. R. M., Keshavarz S. M. E., and Bonyadi A., “Effect of tool parameters on mechanical properties, temperature, and force generation during FSW”, Proceedings of the Institution of Mechanical Engineers, Part L: Journal of Materials: Design and Applications, 233(6): 1033-1043, (2019).
  • Tutunchilar S., Givi M. B., Haghpanahi M., and Asadi P., “Eutectic Al–Si piston alloy surface transformed to modified hypereutectic alloy via FSP”, Materials Science and Engineering: A, 534: 557-567, (2012).
  • Özyürek D., Yıldırım M., and Çiftçi İ., “The tribological properties of A356-SiCp metal-matrix composites fabricated by thixomoulding technique”, Science and Engineering of Composite Materials, 19(4): 351-356, (2012).
  • Atkinson H. V. , “Alloys for semi-solid processing”, In Solid State Phenomena, Trans Tech Publications, 192: 16-27, (2013).
  • Zhang Q. Q., Cao Z. Y., Zhang Y. F., Su G. H., and Liu Y. B., “Effect of compression ratio on the microstructure evolution of semisolid AZ91D alloy”, Journal of Materials Processing Technology, 184(1-3): 195-200, 2007.
  • Seo P. K., Kim D. U., and Kang C. G., “The effect of the gate shape on the microstructural characteristic of the grain size of Al-Si alloy in the semi-solid die casting process”, Materials Science and Engineering: A, 445: 20-30, (2007).
  • Aztekin H., Ōzyūrek D., and Çetinkaya K., “Production of hypo-eutectic Αl-Si alloy based metal matrix composite with thixomoulding processing”, High Temperature Materials and Processes, 29(3): 169-178, (2010).
  • Şi̇mşek İ., Şimşek D., Özyürek D., “Yarı-katı işlem yöntemi ile üretilen Al-SiC kompozit malzemelerin aşınma davranışlarının incelenmesi”, 3rd International Symposium on Innovative Approaches in Scientific Studies, Ankara/Turkey, 4(1): 545-548, (2019).
  • Alhawari K. S., Omar M. Z., Ghazali M. J., Salleh M. S., and Mohammed M. N., “Microstructural evolution during semi solid processing of Al-Si-Cu alloy with different Mg contents”, Transactions of Nonferrous Metals Society of China, 27(7): 1483-1497, (2017).
  • Şimşek İ., Yıldırım M., Tunçay T., Özyürek D., Şimşek D., “Mekanik alaşımlama/öğütme yöntemi ile üretilen Al-SiC kompozitlerin incelenmesi”, Technological Applied Sciences, 13(2): 165-171, (2018).
Toplam 16 adet kaynakça vardır.

Ayrıntılar

Birincil Dil Türkçe
Konular Mühendislik
Bölüm Araştırma Makalesi
Yazarlar

İjlal Şimşek 0000-0001-6542-8567

Doğan Şimşek 0000-0001-8339-9704

Dursun Özyürek 0000-0002-8326-9982

Yayımlanma Tarihi 1 Aralık 2020
Gönderilme Tarihi 4 Kasım 2019
Yayımlandığı Sayı Yıl 2020

Kaynak Göster

APA Şimşek, İ., Şimşek, D., & Özyürek, D. (2020). Yarı Katı Kalıplama Yöntemi İle Üretilen Farklı Miktarlarda SiC Takviyeli A356 Matrisli Kompozit Malzemelerin Aşınma Performansının İncelenmesi. Politeknik Dergisi, 23(4), 1237-1243. https://doi.org/10.2339/politeknik.642506
AMA Şimşek İ, Şimşek D, Özyürek D. Yarı Katı Kalıplama Yöntemi İle Üretilen Farklı Miktarlarda SiC Takviyeli A356 Matrisli Kompozit Malzemelerin Aşınma Performansının İncelenmesi. Politeknik Dergisi. Aralık 2020;23(4):1237-1243. doi:10.2339/politeknik.642506
Chicago Şimşek, İjlal, Doğan Şimşek, ve Dursun Özyürek. “Yarı Katı Kalıplama Yöntemi İle Üretilen Farklı Miktarlarda SiC Takviyeli A356 Matrisli Kompozit Malzemelerin Aşınma Performansının İncelenmesi”. Politeknik Dergisi 23, sy. 4 (Aralık 2020): 1237-43. https://doi.org/10.2339/politeknik.642506.
EndNote Şimşek İ, Şimşek D, Özyürek D (01 Aralık 2020) Yarı Katı Kalıplama Yöntemi İle Üretilen Farklı Miktarlarda SiC Takviyeli A356 Matrisli Kompozit Malzemelerin Aşınma Performansının İncelenmesi. Politeknik Dergisi 23 4 1237–1243.
IEEE İ. Şimşek, D. Şimşek, ve D. Özyürek, “Yarı Katı Kalıplama Yöntemi İle Üretilen Farklı Miktarlarda SiC Takviyeli A356 Matrisli Kompozit Malzemelerin Aşınma Performansının İncelenmesi”, Politeknik Dergisi, c. 23, sy. 4, ss. 1237–1243, 2020, doi: 10.2339/politeknik.642506.
ISNAD Şimşek, İjlal vd. “Yarı Katı Kalıplama Yöntemi İle Üretilen Farklı Miktarlarda SiC Takviyeli A356 Matrisli Kompozit Malzemelerin Aşınma Performansının İncelenmesi”. Politeknik Dergisi 23/4 (Aralık 2020), 1237-1243. https://doi.org/10.2339/politeknik.642506.
JAMA Şimşek İ, Şimşek D, Özyürek D. Yarı Katı Kalıplama Yöntemi İle Üretilen Farklı Miktarlarda SiC Takviyeli A356 Matrisli Kompozit Malzemelerin Aşınma Performansının İncelenmesi. Politeknik Dergisi. 2020;23:1237–1243.
MLA Şimşek, İjlal vd. “Yarı Katı Kalıplama Yöntemi İle Üretilen Farklı Miktarlarda SiC Takviyeli A356 Matrisli Kompozit Malzemelerin Aşınma Performansının İncelenmesi”. Politeknik Dergisi, c. 23, sy. 4, 2020, ss. 1237-43, doi:10.2339/politeknik.642506.
Vancouver Şimşek İ, Şimşek D, Özyürek D. Yarı Katı Kalıplama Yöntemi İle Üretilen Farklı Miktarlarda SiC Takviyeli A356 Matrisli Kompozit Malzemelerin Aşınma Performansının İncelenmesi. Politeknik Dergisi. 2020;23(4):1237-43.
 
TARANDIĞIMIZ DİZİNLER (ABSTRACTING / INDEXING)
181341319013191 13189 13187 13188 18016 

download Bu eser Creative Commons Atıf-AynıLisanslaPaylaş 4.0 Uluslararası ile lisanslanmıştır.