Effect of Hard Raw Material Particle Size and Sintering Temperature on Properties of the Wall Tile Bodies

Öz

It is known that the technological properties of ceramic tiles are related to the raw material characteristics (grain size distribution, chemical composition, mineralogical structure). In this study, quartz and pegmatite hard raw materials, which constitute approximately 30% of the standard wall tile body recipe, were used in the composition after 90 minutes grinding process and the prepared bodies were fired at different temperatures (1110, 1120, 1127 and 1147 C). After sintering, firing shrinkage (%), water absorption (%), fired strength and L*a*b* color parameters were determined and compared with the standard tile body. The phases and microstructure images of the samples were characterized by XRD and SEM analyses respectively. As a result, it was seen that by grinding the hard raw materials, it is possible to obtain structures with superior physical and mechanical properties at lower temperatures compared to the standard.

Anahtar Kelimeler

• Ceramic wall tile
• Particle size
• Sintering
• Physical properties

Sert Hammadde Tane Boyutu ve Pişirim Sıcaklığının Duvar Karosu Bünye Özelliklerine Etkisi

Öz

Seramik karoların teknolojik özelliklerinin bünyede kullanılan hammadde karakteristikleri (tane boyut dağılımı, kimyasal bileşim, mineralojik yapı) ile ilişkili olduğu bilinmektedir. Bu çalışmada, standart duvar karosu bünye reçetesinin yaklaşık %30’unu oluşturan kuvars ve pegmatit sert hammaddeleri 90 dakika öğütme işlemi sonrasında reçetede kullanılmış ve hazırlanan bünyeler farklı sıcaklıklarda (1110, 1120, 1127 ve 1147 C) pişirilmiştir. Sinterleme sonrası bünyelerin; pişme küçülmesi (%), su emme (%), mukavemet ve L*, a* ve b*renk parametreleri belirlenmiş ve standart bünye ile kıyaslamaları yapılmıştır. Numunelerin içerdiği fazlar ve mikroyapı görüntüleri sırasıyla XRD ve SEM analizleri ile karakterize edilmiştir. Sonuç olarak, sert hammaddelerin öğütülmesiyle standarta göre daha düşük sıcaklıklarda, daha üstün fiziksel ve mekanik özelliklere sahip bünyeler elde edilebileceği görülmüştür.

Anahtar Kelimeler

• Seramik Duvar Karosu
• Tane Boyutu
• Sinterleme
• Fiziksel Özellikler

Kaynakça

1. [1] Ozturk, Z.B., Gultekin, E.E. 2014. Determination of the Effect of the Addition of Pumice on the Technological Properties of Wall Tile Using the Factorial Design Method. Advances in Ceramic Science and Engineering (ACSE),3, 110. B.Tanışan vd. / Sert Hammadde Tane Boyutu ve Pişirim Sıcaklığının Duvar Karosu Bünye Özelliklerine Etkisi
2. [2] Ozturk Z.B. 2017. Effect of addition of Avanos’s (Nevsehir) clays on the physical and microstructure properties of ceramic tile. Journal of the Australian Ceramic Society, 53101–107.
3. [3] Emrullahoğlu, Ö.F., Özçelik F. 2002. Etibank Kırka Boraks Atığının Yer Karosu Bünye Özelliklerine Etkisi. 1. Uluslararası Bor Sempozyumu, Kütahya, 213–218.
4. [4] Cengiz, Ö., Kara, A. 2009. Tek Pişirim Duvar Karosu Bünyelerinde Borik Asit İlavesinin Sinterleme Davranışına Etkileri. Afyon Kocatepe Üniv. Fen ve Müh. Bilimleri Dergisi, 9(3), 29–35.
5. [5] Elmas, S., Tarhan, İ. 2019. The Effect of Combination of Boric Acid and Lithium Carbonate on Sintering and Microstructure in Single Firing Wall Tile. Journal of Scientific Perspectives, 3(2), 85–98.
6. [6] Moreno, A., Garcia-Ten, J., Bou, E., Gozalbo, A. 2000. Using Boron as an Auxiliary Flux in Porcelain Tile Compositions. In proceedings of 4th World Congress on Ceramic Tile Quality QUALICER, Castellion, 77–91.
7. [7] Ediz, N., Yurdakul, A. 2009. Characterization of Porcelain Tile Bodies with Colemanite Waste Added as a New Sintering Agent. Journal of Ceramic Processing Research, 10 (4), 414–422.
8. [8] Yet, G. 2007. Yer karosu bünyelerinde farklı ergiticilerin çamur reolojisi ve sinterleme üzerine etkileri. Anadolu Üniversitesi, Fen Bilimleri Enstitüsü, Yüksek Lisans Tezi, 123s, Eskişehir.

9. [9] Turkmen, O., Kucuk, A., Akpinar, S. 2015. Effect of Wollastonite Addition on Sintering of Hard Porcelain. Ceramics International, 41, 5505 5512.
10. [10] Sánchez-Muñoz, L., Carda, J. B., Cerisuelo, E., Tuduri, F., Plaza, S. 2002. Elaboration of Porcelain Stoneware Tiles at 1170°C by Addition of Wollastonite. Key Engineering Materials, 206, 2205–2208.
11. [11] Bragança, S. R., Lengler, H. C. M., Bergmann, C. P. 2012. Wollastonite as a Flux for Ceramics Bodies. Materials Science Forum, 727, 1016–1021.
12. [12] Bayca, S. U. 2009. Effects of the Addition of Ulexite to the Sintering Behavior of a Ceramic Body. Journal of Ceramic Processing Research, 10(2), 162–166
13. [13] Başaran, N., Tamsü,N. 2021. Üleksit ve Manyezit Karışım Komp. Porselen Karo Sinterlemesi Üzerine Etkisinin İncelenmesi. Seramik - Journal of the Turkish Ceramics Society, 1(2) 26–32.
14. [14] Gines, A., Orenga, A., Sheth, A., Thiery, D. 2004. Use of Spdumene for Manufacturing Porcelain Tile Bodies of High Whiteness. Industrie Ceramique, 996, 50–52.
15. [15] Ochen, W., Oruru, B., Dujanga, F. 2019. Effect of Quartz Prticle Size on Sintering Behavior and Flexural Strength of Porcelain Tiles Made from Raw Materials in Uganda. Advances in Materials, 8(1), 33–40.
16. [16] Stathis, G., Ekonomakou, A., Stournaras, C. J., Ftikosa, C. 2004. Effect of Firing Conditions, Filler Grain Size and Quartz Content on Bending Strength and Physical Properties of Sanitaryware Porcelain. Journal of the European Ceramic Society, 24, 2357–2366.
17. [17] Alves, H.J., Melchiades, F.G., Boschi A.O. 2012. Effect of Feldspar Particle Size on the Porous Microstructure and Stain Resistance of Polished porcelain tiles. Journal of the Eur. Ceramic Soc. 32(10), 2095–2102.
18. [18] TS EN 14411/Grup BIII, Su Emmesi E> %10 olan Kuru Preslenmiş Seramik Karolar, Mart, 2006.
19. [19] Z.Bayer Ozturk, N.Ay, “An investigation of the effect of alkaline oxides on porcelain tiles using factorial design”, Journal of Ceramic Processing Research. Vol. 13, No. 5, pp. 635~640 (2012)
20. [20] Aydın, T., Tarhan, M., Tarhan, B. 2019. Addition of Cement Kiln Dust in Ceramic Wall Tile Bodies. Journal of Thermal Analysis and Calorimetry, 136, 527–533.