The Research of the Usability of Unenriched Talc in Wall Tile Bodies

Öz

In this study, the talc sample obtained from Domaniç (Kütahya) region of Turkey together with the raw materials used for making fast and single-fired wall tile are studied by the use of various prescriptions concerning the effects on the technical features of several properties. The samples prepared under laboratory conditions are shaped with pressing method and fired at 1130 °C. The chemical compositions, granule dimensions and moisture content of talc and spray dried granules are determined. Thermo gravimetric and differential thermal analysis of the powder of these materials which were prepared based on the prescriptions are done. Water absorption, fired strength, fired shrinkage, true density, X-Ray diffraction analysis and scanning electron microscope analysis of sintered samples are done. To sum up, it was observed that the fired strength of the wall tile bodies with 15 % talc addition was increased by 1.07 times whereas water absorption value was decreased by 16.22 %. In this respect, it is apparent that these values are well-matched and in accordance with TS EN 14411:2008

Anahtar Kelimeler

• Ceramic wall tile
• Talc
• Spray dried granules
• Kütahya
• Domaniç

Zenginleştirilmemiş Talkın Duvar Karosu Massesinde Kullanılabilirliğinin Araştırılması

Öz

Bu çalışma kapsamında Domaniç (Kütahya) bölgesinden temin edilmiş bir talk numunesi hızlı tek pişirim duvar karosu yapımında kullanılan hammaddelerle değişik reçetelerde kullanılarak teknik özellikler üzerindeki etkileri araştırılmıştır. Laboratuvar koşullarında hazırlanan masse numuneleri presleme yöntemi ile şekillendirilerek işletmede hızlı pişirim koşullarında 1130 °C'de pişirilmiştir. Talk ve işletme massesinin kimyasal kompozisyonları, tane boyutu ve nem içeriği tespit edilmiştir. Reçetelere göre hazırlanmış tozların termogravimetrik ve diferansiyel termal analizleri yapılmıştır. Pişirilmiş numunelerin su emme, pişme mukavemeti, pişme küçülmesi, gerçek yoğunluk ölçümü, X-Işını difraksiyonu ve taramalı elektron mikroskobu analizleri yapılmıştır. Sonuç olarak, % 15 talk katkılı duvar karosu bünyelerinde pişme mukavemeti 1.07 kat artmış ve su emme değeri % 16.22 oranında azaltmıştır. Bu değerlerin TS EN 14411:2008'e uygun olduğu görülmüştür.

Anahtar Kelimeler

• Seramik duvar karosu
• Talk
• Granül masse
• Kütahya
• Domaniç

Kaynakça

1. Ahn, Y., Choi, L., Hwang, J.G., 1976. Development of
2. Fast-Firing Wall Tile Body: I, Tremolitic Talc- Wollastonite-Clay System. Journal of the Korean Ceramics Society, 13, 31-38. Anonim, 1996. Diğer Endüstri Mineralleri Çalışma
3. Grubu Raporu. Devlet Planlama Teşkilatı, 2421, 131- 159s., Ankara.
4. Bernardin, A.M., Medeiros, D.S., Riella, H.G., 2006.
5. Pyroplasticity in Porcelain Tiles. Materials Science and Engineering, 427, 316-319. Chandra, N., Agnihotry, N., Bhasin, S., Khan, A.F., 2005.
6. Effect of Addition of Talc on the Sintering Characteristics of Fly Ash Based Ceramic Tiles. Journal of the European Ceramic Society, 25(1), 81- Geçkinli, A.E., 1991. İleri Teknoloji Malzemeleri. İTÜ Kütüphanesi, 1454, 287s.
7. Geller, R.F., Creamer A.S., 1935. Talc in Whiteware
8. Bodies of the Wall-Tile Type. Journal of the American Ceramic Society, 18, 259-269. Grosjean, P., 1995. Influence of Talc on Single-Fired

9. White Body Floor Tile Compositions. Tile and Brick International, 11, 292-295. Hagar, D., 1940. Talc Containing Ceramic
10. Composition. United States Patent Office, 2.213.495. Haner, S., 2009. Talk ve Wollastonit İlavelerinin
11. Duvar Karosu Bünyesine Etkilerinin Araştırılması. Yüksek Lisans Tezi, DPÜ, Fen Bilimleri Enstitüsü, Kütahya, 73s. Haner, S., 2011. Wollastonit İlavesinin Duvar Karosu
12. Bünyesine Etkilerinin Araştırılması. Dumlupınar Üniversitesi Fen Bilimleri Enstitüsü Dergisi, 26, 117- 128
13. Hildick-Smith, G.Y., 1976. The Biology of Talc. British
14. Journal of Industrial Medicine, 33, 217-229. Huining, H., 1999. Studies on Porcelain Exterior-Wall
15. Tile Using Talc-Clay. China Ceramic Industry. Il’ina, V.P., Lebedeva, G.A., Ozerova, G.P., Inina, I.S., 200 The Effect of Talc-Chlorite Schist on Properties of Ceramic Tiles. Glass and Ceramics, 62, 11-12. Kara, A., Özer F., Kayacı, K., Özer, P., 2006.
16. Development of a Multipurpose Tile Body: Phase and Microstructural Development, Journal of European Ceramic Society, 26, 3769-3782.
17. Kartal, A., Konuk, R.E., Evcin, A., 2004. Nevşehir
18. Yöresi Pomzasının Yer Karosu Massesinde Kullanımı Üzerine Araştırmalar. 5. Endüstriyel Hammaddeler Sempozyumu, DEÜ, Sabancı Kültür Merkezi, 13-14 Mayıs, İzmir, 110-113. Kayacı, K., Kaşıkçı, H., Çifçi, M., Aylakçı, B., 2004. Söğüt
19. (Bilecik) Civarındaki Alkalili Hammaddelerin Yer- Duvar Kullanılabilirliğinin Araştırılması. 5. Endüstriyel Hammaddeler Sempozyumu, DEÜ, Sabancı Kültür Merkezi, 13-14 Mayıs, İzmir, 37-41. Olarak Lee, S.J., Lee, C.H., 2000. Critical Size Effect for
20. Chemically Doped β-Cristobalite Transformation. Materials Letter, 45, 175-179. Özbay, N., 2005. Talk ve Kullanım Alanları. Soma MYO
21. Teknik Bilimler Dergisi, 4. Perricone, A.C., Stone, R.L., 1954. Interface Reactions
22. Between Glazes and the Crystal Phases in a High-Talc Tile Body. Journal of the American Ceramic Society, 37, 33-38. Sousa, S.J.G., Holanda, J.N.F., 2005. Sintering Behavior of Porous Wall Tile Bodies During Fast Single-Firing
23. Process. Materials Research, 8, 198. Tatar, İ., Ediz, N., Bentli, İ., 2004. Diatomit Katkılı Çini
24. Karo Bünye Üretimi. 5. Endüstriyel Hammaddeler Sempozyumu, DEÜ, Sabancı Kültür Merkezi, 13-14 Mayıs, İzmir, 313-317. Uz, B., 2000. Mineraller, İstanbul, 436s.
25. Virta, R.L., 2001. Talc and Pyrophyllite. U.S. Geological
26. Survey Minerals Yearbook, 76.