The effects of Nano Silicate Mixtures with High Volume Fly Ash on High Performance Strengthening Mortar

Öz

In this study, 8 different mixtures were made. In these mixtures, silica nanoparticles were substituted for cement by 0% to 2% by 0.25%. The compressive and flexural strength of Nano Silicate Mixtures under the influence of high volume fly ash with low water content were investigated. 5×5×5 cm concrete cubic prisms were produced and subjected to compressive strength test on the 1st, 3rd and 7th days. These prepared concrete specimens were subjected to experiments on 1, 3 and 7 days. The aim of this study is to prevent the negative effect of high volume fly ash on the early age strength of concrete from the first day and to obtain high performance concrete.

Anahtar Kelimeler

• Nano silica
• Pozzolan
• Fly ash

UÇUCU KÜL İÇEREN YÜKSEK PERFORMANSLI GÜÇLENDİRME HARCINDA NANO SİLİKATIN ETKİSİ

Öz

Bu çalışmada 8 farklı karışım yapılmıştır. Bu karışımlarda, Nano Silikat %0 ’dan %2’ ye kadar % 0.25 arttırılarak çimento yerine ikame edilmiştir. Hazırlanan numunelerde su oranı düşük tutulup yüksek hacimde kullanılan Uçucu Külün etkisi altında ikame edilen Nano Silikatlı karışımların basınç ve eğilme altındaki davranışları araştırılmıştır. Numunelerde basınç dayanımı testi için 5×5×5 cm küp prizma betonlar hazırlanmış ve 1., 3. ve 7. günlerde deneylere tabi tutulmuştur. Bu çalışmanın amacı Nano Silikatlı numunelerin 1. günden itibaren Uçucu Külün erken yaş dayanımdaki negatif etkisini önlemek ve yüksek performanslı beton elde etmektir.

Anahtar Kelimeler

• Nano silikat
• Puzolan
• Uçucu kül

Kaynakça

1. ACRA and CSIRO Australian Standards, 2006, “Guide to Concrete Repair and Protection”, Australian Concrete Repair Association, Sydney, Australia.
2. Alexander, M.G., Stanish K., ‚Durability Design and Specification of Reinforced Concrete Structures Using a Multi-Factored Approach‛, Mindess Symposium, Third International Conference on Construction Materials, Vancouver, 22 - 24 August 2005.
3. ASTM C39/C39M, 2016, “Standard Test Method for Compressive Strength of Cylindrical Concrete Specimens”, American Society for Testing and Materials, Philadelphia, USA.
4. Cilason, N., ‚Quality Assurance and Quality Control for Concrete in Hot Climates‛, 9th International RILEM Conference on Concrete in Hot Climates, Torquay, England, No. 3, pp. 167-171, 21-25 September 1992.
5. Kanda, T., Li, V.C., 1999, ‚A New Micromechanics Design Theory for Pseudo Strain-Hardening Cementitious Composite‛, ASCE Journal of Engineering Mechanics, Vol. 125 (4), pp. 373-381.
6. Sahmaran M., Li M., Li V.C., 2007, ‚Transport Properties of Engineered Cementitious Composites under Chloride Exposure‛, ACI Materials Journal, Vol. 104, No. 6, pp. 604-611.