Structural and Mechanical Characterization of Natural Fluoroapatite/3Y-TZP Composites Consolidated by Spark Plasma Sintering

Öz

This study investigates the structural and mechanical properties of natural fluoroapatite (FAP)/3 mol% yttria-stabilized zirconia (3YSZ) composites consolidated by spark plasma sintering (SPS). Powder mixtures containing 0–100 vol.% 3YSZ were prepared and sintered at optimized temperatures between 800 and 1300 °C under 50 MPa for 10 min. Phase composition, microstructure, density, hardness, and fracture toughness were systematically characterized using XRD, SEM-EDS, Archimedes’ method, and Vickers indentation. High relative densities (96–99%) were achieved within short sintering times. XRD results confirmed the coexistence of tetragonal YSZ and hexagonal FAP phases without detectable secondary reactions. Mechanical properties increased with increasing YSZ content. Pure YSZ exhibited the highest hardness (13.66 GPa) and fracture toughness (5.52 MPa m0.5), while the 95YSZ–5FAP composite retained relatively high mechanical performance (13.46 GPa, 4.42 MPa m0.5). Higher FAP contents led to significant reductions in toughness. The results demonstrate that SPS enables dense bioactive composites while preserving the mechanical integrity of zirconia-rich compositions.

Anahtar Kelimeler

• fluorapatite
• ZrO2
• YSZ
• SPS
• composite

Spark Plazma Sinterleme Yöntemiyle Yoğunlaştırılan Doğal Florapatit/3Y-TZP Kompozitlerinin Yapısal ve Mekanik Özelliklerinin İncelenmesi

Öz

Bu çalışma, spark plazma sinterleme (SPS) yöntemiyle yoğunlaştırılan doğal florapatit (FAP) / %3 mol itriya ile stabilize edilmiş zirkonya (3YSZ) kompozitlerinin yapısal ve mekanik özelliklerini incelemektedir. %0–100 hacim oranında 3YSZ içeren toz karışımları hazırlanmış ve 50 MPa basınç altında, 800–1300 °C arasındaki optimize edilmiş sıcaklıklarda 10 dakika süreyle sinterlenmiştir. Faz bileşimi, mikroyapı, yoğunluk, sertlik ve kırılma tokluğu; XRD, SEM-EDS, Arşimet yöntemi ve Vickers indentasyonu kullanılarak sistematik biçimde karakterize edilmiştir. Kısa sinterleme sürelerinde yüksek bağıl yoğunluk değerleri (%96–99) elde edilmiştir. XRD sonuçları, ikincil reaksiyonlara dair herhangi bir belirti olmaksızın tetragonal YSZ ve hekzagonal FAP fazlarının birlikte varlığını doğrulamıştır. Mekanik özelliklerin, YSZ içeriğinin artmasıyla birlikte yükseldiği belirlenmiştir. Saf YSZ en yüksek sertlik (13,66 GPa) ve kırılma tokluğu (5,52 MPa m0.5) değerlerini sergilerken, %95YSZ–%5FAP kompoziti de görece yüksek mekanik performansını (13,46 GPa, 4,42 MPa m0.5) korumuştur. Daha yüksek FAP içerikleri, kırılma tokluğunda belirgin düşüşlere yol açmıştır. Elde edilen sonuçlar, SPS yönteminin, zirkonya açısından zengin bileşimlerin mekanik bütünlüğünü korurken yoğun ve biyoaktif kompozitlerin üretilmesine olanak sağladığını göstermektedir.

Anahtar Kelimeler

• florapatit
• ZrO2
• YSZ
• SPS
• kompozit

Kaynakça

1. Aktas B, Das R, Acıkgoz A, Ulas EO, Demircan G, Uyar E, et al. Fabrication of CaSiO₃-doped 3Y-ZrO₂ ceramics via DLP 3D printing: Structural, mechanical, and biological evaluation. Journal of Alloys and Compounds. 2025;1036:181895.
2. Gu Q, Yuan R, Sun D, Wallace G. Future Frontiers in Bioinspired Implanted Biomaterials. Advanced Materials. 2025;37(36):e06323.
3. Ahmed MMS, Rabbi SF, Hossen MZ, Islam S, Sarker MAH, Hossain N, et al. Recent Advances in Biocompatible Dental Materials. Biomedical Materials & Devices. 2026:1–36.
4. Ferreira C, Santiago A, Vasconcelos R, Paiva D, Pirih F, Araújo A, et al. Study of microstructural, mechanical, and biomedical properties of zirconia/hydroxyapatite ceramic composites. Ceramics International. 2022;48(9):12376–86.
5. Demir B, Duden EI, Ayas E. Characterization of MoAlB ceramics synthesized via spark plasma sintering with Si addition and SiC reinforcement. Journal of Alloys and Compounds. 2023;953:170115.
6. Alqutaibi AY, Ghulam O, Krsoum M, Binmahmoud S, Taher H, Elmalky W, et al. Revolution of current dental zirconia: A comprehensive review. Molecules. 2022;27(5):1699.
7. Cesar PF, de Paula Miranda RB, Santos KF, Scherrer SS, Zhang Y. Recent advances in dental zirconia: 15 years of material and processing evolution. Dental Materials. 2024;40(5):824–36.
8. Mamivand, M., M.A. Zaeem, and H. El Kadiri, Phase field modeling of stress-induced tetragonal-to-monoclinic transformation in zirconia and its effect on transformation toughening. Acta materialia, 2014. 64: p. 208-219.

9. Huang B, Chen M, Wang J, Zhang X. Advances in zirconia-based dental materials: Properties, classification, applications, and future prospects. Journal of Dentistry. 2024;147:105111.
10. Osman RB, Swain MV, Atieh M, Ma S, Duncan W. Ceramic implants (Y‐TZP): are they a viable alternative to titanium implants for the support of overdentures? A randomized clinical trial. Clinical Oral Implants Research. 2014;25(12):1366–77.
11. Nasiri-Tabrizi B, Fahami A. Synthesis and characterization of fluorapatite–zirconia composite nanopowders. Ceramics International. 2013;39(4):4329–37.
12. Pajor K, Pajchel L, Kolmas J. Hydroxyapatite and fluorapatite in conservative dentistry and oral implantology—A review. Materials. 2019;12(17):2683.
13. Bouslama N, Ayed FB, Bouaziz J. Sintering and mechanical properties of tricalcium phosphate–fluorapatite composites. Ceramics International. 2009;35(5):1909–17.
14. Cao Y, Li C, Xia Y, Ren K, Zhu S. Study on the fabrication and mechanical properties of HAp-3YSZ composites by flash sintering. Ceramics International. 2022;48(11):16300–5.
15. Tokita M. Progress of spark plasma sintering (SPS) method, systems, ceramics applications and industrialization. Ceramics. 2021;4(2):160–98.
16. Demir B, Ayas E. Effects of sintering temperature and doping content on luminescence properties of rare earth (Sm³⁺, Eu³⁺, and Dy³⁺) doped natural fluorapatite. Journal of Solid State Chemistry. 2022;306:122783.
17. Demir B. Novel MoSi₂–MoB₂ composites: Single-step in-situ synthesis from elemental powders via spark plasma sintering. Journal of Alloys and Compounds. 2025:185651.
18. Evans AG, Charles EA. Fracture toughness determinations by indentation. Journal of the American Ceramic Society. 1976;59(7–8):371–2.
19. Demir B, Derince D, Dayioglu T, Koroglu L, Karacaoglu E, Uz V, et al. Effects of doping content and crystallite size on luminescence properties of Eu³⁺ doped fluorapatites obtained from natural waste. Ceramics International. 2021;47(24):34657–66.
20. Demir B, Karacaoglu E, Agil AA, Koroglu L, Ayas E. Effect of Gd-codoping on photoluminescence properties of Eu-doped natural fluorapatite. Optik. 2023;287:171123.
21. Demir B, İmak A, Karacaoğlu E. Enhancing the photoluminescence performance of Sm-doped fluorapatite with Dy co-doping. Ceramics International. 2025.
22. Bartolomé JF, Smirnov A, Kurland H-D, Grabow J, Müller FA. New ZrO₂/Al₂O₃ nanocomposite fabricated from hybrid nanoparticles prepared by CO₂ laser co-vaporization. Scientific Reports. 2016;6(1):20589.
23. Flanagan D. Bite force and dental implant treatment: A short review. Medical Devices: Evidence and Research. 2017:141–8.
24. Kim DS, Lee JK. Sintered characteristics of 3 mole% yttria-stabilized zirconia polycrystals (3Y-TZP) implants manufactured by slip-casting and computer aided design/computer aided manufacturing (CAD/CAM). Journal of Nanoscience and Nanotechnology. 2021;21(7):3877–81.
25. Abraham AM, Venkatesan S. A review on application of biomaterials for medical and dental implants. Proceedings of the Institution of Mechanical Engineers, Part L: Journal of Materials: Design and Applications. 2023;237(2):249–73.
26. Adolfsson E, Hermansson L. Zirconia–fluorapatite materials produced by HIP. Biomaterials. 1999;20(14):1263–7.
27. Durmuşoğlu Ş, Altuner EE. Synthesis and Characterization of Erbia - Doped Yttria - Stabilized Ceria - Zirconia Based Nanoceramics. Turkish Journal of Nature and Science, 2025; 14(4), 158-164