AN INNOVATIVE TEST APPARATUS FOR ELECTROMAGNETIC SHIELDING EFFECTIVENESS TEST OF TEXTILE MATERIALS

Yıl 2015, Cilt: 22 Sayı: 99, 14 - 26, 30.09.2015
https://doi.org/10.7216/130075992015229903

Öz

Electromagnetic shielding effectiveness (SE) of textile and various composite materials should be measured since their SE values cannot be calculated as in the conventional metal plate. Coaxial Holder Method is a measurement method that SE of textile materials is tested in the controlled test area. This measurement method has several shortcomings such as limited frequency range and impractical test conditions. In this study, firstly a new test apparatus was developed with an aim to overcome limitations of ASTM D 4935. Then, SE values of hybrid fabrics produced under the controlled conditions were tested with this new test apparatus and the test results compared with SE results obtained from ASTM D 4935 method.

Kaynakça

  • Sevgi, L., (2000), Elektromanyetik Elektromanyetik Kirlilik, EMO İstanbul. Uyumluluk
  • Şeker, S., Çerezci, O., (2000), Radyasyon Kuşatması- Elektriğin ve Nükleer Enerjinin Sağlığımıza Etkileri, Boğaziçi Üniversitesi Yayınevi, İstanbul.
  • Palamutçu S., Dağ N., (2009), Fonksiyonel Tekstiller I : Elektromanyetik Kalkanlama Amaçlı Tekstil Yüzeyleri, Tekstil Teknolojileri Elektronik Dergisi, 3, 1, 87-101.
  • Su, C. I., Chern, J. T., (2004), Effect of Stainless Steel- Containing Fabrics on Electromagnetic Shielding Effectiveness, Textile Research Journal, 74(1), 51-54.
  • Chen, H.C., Lee, K.C., Lin, J.H., Koch, M., (2007), Comparison of Electromagnetic Shielding Effectiveness Properties of Diverse Conductive Textiles via Various Measurement Techniques, Journal of Materials Processing Technology, 192–193, 549–554.
  • Donohoe, J. P., JunXu, Pittman C.U., Jr., (2005), Variability of dual TEM cell shielding effectiveness measurements for vapor grown carbon nano fiber/vinyl ester composites, Electromagnetic Compatibility, International Symposium on, 1, 190-194.
  • IEEE-STD-299, (2006), IEEE Standard Method for Measuring the Effectiveness of Electromagnetic Shielding Enclosures, IEEE National Standards Institute.
  • Koprowska, J.,Pietranik, M., Stawski, W., (2004), New Type of Textiles with Shielding Properties, Fibres&Textiles in Eastern Europe, 12, 3.
  • Kılıç, G., Örtlek, H.G., Saraçoğlu, Ö.G., (2009), Elektromanyetik Radyasyona Karşı Koruyucu Tekstillerin Ekranlama Etkinliği (SE) Ölçüm Yöntemleri, Tekstil ve Mühendis, 72, 7-15.
  • Więckowski, T. W., Janukiewicz J. M., (2006), Methods for Evaluating the Shielding Effectiveness of Textiles, Fibres&Textiles in Eastern Europe, 14, 5 (59), 18-22.
  • Özsoy, S., (1998), Elektromanyetik Dalga Teorisi, Erciyes Üniversitesi Matbaası, Kayseri.
  • Roh, J., S., Chi, Y., S, Kang, T., J., Nam, S., W., (2008), Electromagnetic Shielding Effectiveness of Multifunctional Metal Composite Fabrics, T. Res., Journal, 78 (9), 825-835.
  • Cheng, L., Zhang, T., Gua, M., Li, J., Wang, S., Tang, H., (2015), mathematical model of stainless steel composite fabric, The Journal of The Textile Institute, 106, 6, 577-586.
  • Yu, Z., Zhang, J., Lou, C., He, H., Chen, A., Lin, J., (2015), Determination antibacterial properties of multifunctional warpknitted fabrics, The Journal of The Textile Institute, DOI: 10.1080/00405000.2014.984444. shielding and
  • Ersoy, M. S., Önder, E., (2008), Shielding Textiles Against Electromagnetic Radiation, International Nonwoven Technical Textiles Technology Magazine,1.çeyrek, 18, 52- 61.
  • Janda, N., B., (2004), Development of a Predictive Shielding Effectiveness Model for Carbon Fiber/Nylon Based Composites, M.Sc. Thesis, Michigan Technological University, .
  • ASTM D 4935-99, (2001), Standard Test Method for Measuring the Electromagnetic Shielding Effectiveness of Planar Materials, ASTM.

Tekstil Malzemelerinin Elektromanyetik Kalkanlama Etkinliği Ölçümünde Yenilikçi Bir Test Aparatı

Yıl 2015, Cilt: 22 Sayı: 99, 14 - 26, 30.09.2015
https://doi.org/10.7216/130075992015229903

Öz

Tekstil ve çeşitli kompozit malzemelerin elektromanyetik kalkanlama etkinliğinin (SE), klasik metal plakalarda olduğu gibi hesaplanması mümkün olmadığından, ölçülmesi gerekmektedir. Koaksiyel Tutucu Metodu, tekstil malzemelerinin SE ölçümünün kontrollü test alanlarında gerçekleştirildiği bir ölçüm yöntemidir. Bu metotla yapılan ölçümlerin; test numunesinin yerleştirilmesinde zorluklar ve ölçüm frekans aralığının düşük olması gibi çeşitli dezavantajları mevcuttur. Bu çalışma kapsamında öncelikle mevcut koaksiyel tutucu metodun (ASTM D 4935) dezavantajlarını ortadan kaldıracak yapıda yeni bir test aparatı geliştirilmiştir. Ardından kontrollü şartlarda üretilen hibrit kumaşların, geliştirilen test aparatı ile gerçekleştirilen SE ölçümleri, mevcut koaksiyel tutucu metottan elde edilen ölçüm sonuçları ile karşılaştırılmıştır.

Kaynakça

  • Sevgi, L., (2000), Elektromanyetik Elektromanyetik Kirlilik, EMO İstanbul. Uyumluluk
  • Şeker, S., Çerezci, O., (2000), Radyasyon Kuşatması- Elektriğin ve Nükleer Enerjinin Sağlığımıza Etkileri, Boğaziçi Üniversitesi Yayınevi, İstanbul.
  • Palamutçu S., Dağ N., (2009), Fonksiyonel Tekstiller I : Elektromanyetik Kalkanlama Amaçlı Tekstil Yüzeyleri, Tekstil Teknolojileri Elektronik Dergisi, 3, 1, 87-101.
  • Su, C. I., Chern, J. T., (2004), Effect of Stainless Steel- Containing Fabrics on Electromagnetic Shielding Effectiveness, Textile Research Journal, 74(1), 51-54.
  • Chen, H.C., Lee, K.C., Lin, J.H., Koch, M., (2007), Comparison of Electromagnetic Shielding Effectiveness Properties of Diverse Conductive Textiles via Various Measurement Techniques, Journal of Materials Processing Technology, 192–193, 549–554.
  • Donohoe, J. P., JunXu, Pittman C.U., Jr., (2005), Variability of dual TEM cell shielding effectiveness measurements for vapor grown carbon nano fiber/vinyl ester composites, Electromagnetic Compatibility, International Symposium on, 1, 190-194.
  • IEEE-STD-299, (2006), IEEE Standard Method for Measuring the Effectiveness of Electromagnetic Shielding Enclosures, IEEE National Standards Institute.
  • Koprowska, J.,Pietranik, M., Stawski, W., (2004), New Type of Textiles with Shielding Properties, Fibres&Textiles in Eastern Europe, 12, 3.
  • Kılıç, G., Örtlek, H.G., Saraçoğlu, Ö.G., (2009), Elektromanyetik Radyasyona Karşı Koruyucu Tekstillerin Ekranlama Etkinliği (SE) Ölçüm Yöntemleri, Tekstil ve Mühendis, 72, 7-15.
  • Więckowski, T. W., Janukiewicz J. M., (2006), Methods for Evaluating the Shielding Effectiveness of Textiles, Fibres&Textiles in Eastern Europe, 14, 5 (59), 18-22.
  • Özsoy, S., (1998), Elektromanyetik Dalga Teorisi, Erciyes Üniversitesi Matbaası, Kayseri.
  • Roh, J., S., Chi, Y., S, Kang, T., J., Nam, S., W., (2008), Electromagnetic Shielding Effectiveness of Multifunctional Metal Composite Fabrics, T. Res., Journal, 78 (9), 825-835.
  • Cheng, L., Zhang, T., Gua, M., Li, J., Wang, S., Tang, H., (2015), mathematical model of stainless steel composite fabric, The Journal of The Textile Institute, 106, 6, 577-586.
  • Yu, Z., Zhang, J., Lou, C., He, H., Chen, A., Lin, J., (2015), Determination antibacterial properties of multifunctional warpknitted fabrics, The Journal of The Textile Institute, DOI: 10.1080/00405000.2014.984444. shielding and
  • Ersoy, M. S., Önder, E., (2008), Shielding Textiles Against Electromagnetic Radiation, International Nonwoven Technical Textiles Technology Magazine,1.çeyrek, 18, 52- 61.
  • Janda, N., B., (2004), Development of a Predictive Shielding Effectiveness Model for Carbon Fiber/Nylon Based Composites, M.Sc. Thesis, Michigan Technological University, .
  • ASTM D 4935-99, (2001), Standard Test Method for Measuring the Electromagnetic Shielding Effectiveness of Planar Materials, ASTM.
Toplam 17 adet kaynakça vardır.

Ayrıntılar

Birincil Dil Türkçe
Konular Mühendislik
Bölüm Makaleler
Yazarlar

Ebru Türksoy Bu kişi benim

Sümeyye Üstüntağ Bu kişi benim

Öznur Sarıtaş Bu kişi benim

Ömer Saraçoğlu Bu kişi benim

Yayımlanma Tarihi 30 Eylül 2015
Yayımlandığı Sayı Yıl 2015 Cilt: 22 Sayı: 99

Kaynak Göster

APA Türksoy, E., Üstüntağ, S., Sarıtaş, Ö., Saraçoğlu, Ö. (2015). Tekstil Malzemelerinin Elektromanyetik Kalkanlama Etkinliği Ölçümünde Yenilikçi Bir Test Aparatı. Tekstil Ve Mühendis, 22(99), 14-26. https://doi.org/10.7216/130075992015229903
AMA Türksoy E, Üstüntağ S, Sarıtaş Ö, Saraçoğlu Ö. Tekstil Malzemelerinin Elektromanyetik Kalkanlama Etkinliği Ölçümünde Yenilikçi Bir Test Aparatı. Tekstil ve Mühendis. Eylül 2015;22(99):14-26. doi:10.7216/130075992015229903
Chicago Türksoy, Ebru, Sümeyye Üstüntağ, Öznur Sarıtaş, ve Ömer Saraçoğlu. “Tekstil Malzemelerinin Elektromanyetik Kalkanlama Etkinliği Ölçümünde Yenilikçi Bir Test Aparatı”. Tekstil Ve Mühendis 22, sy. 99 (Eylül 2015): 14-26. https://doi.org/10.7216/130075992015229903.
EndNote Türksoy E, Üstüntağ S, Sarıtaş Ö, Saraçoğlu Ö (01 Eylül 2015) Tekstil Malzemelerinin Elektromanyetik Kalkanlama Etkinliği Ölçümünde Yenilikçi Bir Test Aparatı. Tekstil ve Mühendis 22 99 14–26.
IEEE E. Türksoy, S. Üstüntağ, Ö. Sarıtaş, ve Ö. Saraçoğlu, “Tekstil Malzemelerinin Elektromanyetik Kalkanlama Etkinliği Ölçümünde Yenilikçi Bir Test Aparatı”, Tekstil ve Mühendis, c. 22, sy. 99, ss. 14–26, 2015, doi: 10.7216/130075992015229903.
ISNAD Türksoy, Ebru vd. “Tekstil Malzemelerinin Elektromanyetik Kalkanlama Etkinliği Ölçümünde Yenilikçi Bir Test Aparatı”. Tekstil ve Mühendis 22/99 (Eylül 2015), 14-26. https://doi.org/10.7216/130075992015229903.
JAMA Türksoy E, Üstüntağ S, Sarıtaş Ö, Saraçoğlu Ö. Tekstil Malzemelerinin Elektromanyetik Kalkanlama Etkinliği Ölçümünde Yenilikçi Bir Test Aparatı. Tekstil ve Mühendis. 2015;22:14–26.
MLA Türksoy, Ebru vd. “Tekstil Malzemelerinin Elektromanyetik Kalkanlama Etkinliği Ölçümünde Yenilikçi Bir Test Aparatı”. Tekstil Ve Mühendis, c. 22, sy. 99, 2015, ss. 14-26, doi:10.7216/130075992015229903.
Vancouver Türksoy E, Üstüntağ S, Sarıtaş Ö, Saraçoğlu Ö. Tekstil Malzemelerinin Elektromanyetik Kalkanlama Etkinliği Ölçümünde Yenilikçi Bir Test Aparatı. Tekstil ve Mühendis. 2015;22(99):14-26.