Partially Transformation of Zinc Nitrate to Zinc Compounds on PVC Nanofibers at Low Temperature Heat Treatment and Investigation of the Products’ Optical Properties
PVC Nanoliflerde Çinko Nitratın Düşük Sıcaklıkta Isıl İşlemle Kısmi Olarak Diğer Çinko Bileşiklerine Dönüşümü ve Optik Özelliklerinin İncelenmesi

Yezdan Irem AKGÜL [1] , Yakup AYKUT [2]


Zinc compounds are photoactive material and they are incorporated into the material to differentiate the optical

properties of the material. PVC/Zn(NO3)2 (polyvinyl chloride /zinc nitrate) composite precursor nanofibers were produced by

electrospinning by dissolving PVC and Zn(NO3)2 in the electrospinning solution together. As-spun nanofibers are treated with

aqueous NaOH and then stayed at 80°C for one hour to partially convert Zn(NO3)2 to zinc compounds in/on the PVC nanofibers.

Nanofibers have been investigated in terms of morphological, chemical, thermal and optical properties. An increase in transmittance

values was observed at the nanofibers after thermal treatment due to the ratio of Zn(NO3)2 in the precursor PVC/ Zn(NO3)2

nanofibers, and a decrease in reflectance values was observed. The produced fine nanofibers and nanofiber coated surfaces could be

potentially used to coat drapery fabrics, where controllable light transmission is required.

Çinko bileşikleri fotoaktif malzemeler olup polimerler başta olmak üzere birçok malzemenin içerisine katılarak malzemelerin
optik özelliklerini farklılaştırabilmektedirler. Çinko bileşiklerinin üretilen polimer nanolifin her bölgesinde bulunmasını sağlamak
amacıyla çinko nitrat (Zn(NO3)2) prekürsor polivinil klorür (PVC) ile birlikte çözülerek elektro çekim metoduyla PVC/Zn(NO3)2
kompozit nanolifler üretilmiştir. Nanolifler önce sulu NaOH çözeltisiyle işlem, ardından 80oC de fırınlanarak PVC nanoliflerdeki
Zn(NO3)2 ın diğer çinko bileşiklerine dönüştürülmesi sağlanmıştır. Nanolifler morfolojik, kimyasal, termal ve optik özellikler
bakımından incelenmiştir. Prekürsor PVC/Zn(NO3)2 nanoliflerdeki Zn(NO3)2 oranına bağlı olarak termal işlem sonrası nanoliflerde
transmittans değerlerinde artma gözlemlenirken reflektans değerlerinde azalma gözlemlenmiştir. Üretilen ince nanolifler ve nanolif
kaplı yüzeyler içerisindeki çinko bileşeni miktarına bağlı olarak ışık geçişinin kontrollü olması istenen perdelik kumaşların
kaplanmasında kullanılabilirler.
  • -
Birincil Dil en
Bölüm Makaleler
Yazarlar

Orcid: 0000-0003-1170-5105
Yazar: Yezdan Irem AKGÜL

Orcid: 0000-0002-5263-1985
Yazar: Yakup AYKUT (Sorumlu Yazar)

Tarihler

Yayımlanma Tarihi : 27 Haziran 2019

Bibtex @araştırma makalesi { teksmuh588822, journal = {Tekstil ve Mühendis}, issn = {1300-7599}, eissn = {2147-0510}, address = {}, publisher = {Tekstil Mühendisleri Odası}, year = {2019}, volume = {26}, pages = {118 - 124}, doi = {}, title = {Partially Transformation of Zinc Nitrate to Zinc Compounds on PVC Nanofibers at Low Temperature Heat Treatment and Investigation of the Products’ Optical Properties}, key = {cite}, author = {AKGÜL, Yezdan Irem and AYKUT, Yakup} }
APA AKGÜL, Y , AYKUT, Y . (2019). Partially Transformation of Zinc Nitrate to Zinc Compounds on PVC Nanofibers at Low Temperature Heat Treatment and Investigation of the Products’ Optical Properties. Tekstil ve Mühendis , 26 (114) , 118-124 . Retrieved from https://dergipark.org.tr/tr/pub/teksmuh/issue/46933/588822
MLA AKGÜL, Y , AYKUT, Y . "Partially Transformation of Zinc Nitrate to Zinc Compounds on PVC Nanofibers at Low Temperature Heat Treatment and Investigation of the Products’ Optical Properties". Tekstil ve Mühendis 26 (2019 ): 118-124 <https://dergipark.org.tr/tr/pub/teksmuh/issue/46933/588822>
Chicago AKGÜL, Y , AYKUT, Y . "Partially Transformation of Zinc Nitrate to Zinc Compounds on PVC Nanofibers at Low Temperature Heat Treatment and Investigation of the Products’ Optical Properties". Tekstil ve Mühendis 26 (2019 ): 118-124
RIS TY - JOUR T1 - Partially Transformation of Zinc Nitrate to Zinc Compounds on PVC Nanofibers at Low Temperature Heat Treatment and Investigation of the Products’ Optical Properties AU - Yezdan Irem AKGÜL , Yakup AYKUT Y1 - 2019 PY - 2019 N1 - DO - T2 - Tekstil ve Mühendis JF - Journal JO - JOR SP - 118 EP - 124 VL - 26 IS - 114 SN - 1300-7599-2147-0510 M3 - UR - Y2 - 2019 ER -
EndNote %0 Tekstil ve Mühendis Partially Transformation of Zinc Nitrate to Zinc Compounds on PVC Nanofibers at Low Temperature Heat Treatment and Investigation of the Products’ Optical Properties %A Yezdan Irem AKGÜL , Yakup AYKUT %T Partially Transformation of Zinc Nitrate to Zinc Compounds on PVC Nanofibers at Low Temperature Heat Treatment and Investigation of the Products’ Optical Properties %D 2019 %J Tekstil ve Mühendis %P 1300-7599-2147-0510 %V 26 %N 114 %R %U
ISNAD AKGÜL, Yezdan Irem , AYKUT, Yakup . "Partially Transformation of Zinc Nitrate to Zinc Compounds on PVC Nanofibers at Low Temperature Heat Treatment and Investigation of the Products’ Optical Properties". Tekstil ve Mühendis 26 / 114 (Haziran 2019): 118-124 .
AMA AKGÜL Y , AYKUT Y . Partially Transformation of Zinc Nitrate to Zinc Compounds on PVC Nanofibers at Low Temperature Heat Treatment and Investigation of the Products’ Optical Properties. Tekstil ve Mühendis. 2019; 26(114): 118-124.
Vancouver AKGÜL Y , AYKUT Y . Partially Transformation of Zinc Nitrate to Zinc Compounds on PVC Nanofibers at Low Temperature Heat Treatment and Investigation of the Products’ Optical Properties. Tekstil ve Mühendis. 2019; 26(114): 124-118.