Production of propolis/TiO2 (P-TiO2) nano composites for degradation of food dyes

Öz

Aim of this study is to produce highly active hybrid propolis-TiO₂ nanocomposites using sol-gel method and to use it remediation of food industry waste. Propolis solution was prepared in ethanol and added to sol-gel mixture at increasing volume (0.25, 0.50, 0.75, 1.00 mL) to prepare propolis-TiO₂ (P-TiO₂) hybrid catalyst. Neat TiO₂ was also prepared by the same sol-gel technique and its action was compared to propolis doped ones. Catalysts were calcinated at 300 ^oC to obtain desired anatase form.

After production the catalysts were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and FTIR. Sunset Yellow (SY), Allura red (AR) and Tartrazine (TT) were used as model compounds ([C]₀=10 mgL^-1, catalyst mass=1 gL^-1) . Concentration of dyes were monitored by UV-vis spectrometry. P-TiO2 catalyst prepared with 1.00 mL propolis solution was extremely effective for removal of all dyes studies for both 254 nm and 365 nm light exposure. LED light exposure provided lower removal rate (approx.. 25%) but it was still significant for dye removal.

Anahtar Kelimeler

• Photocatalysis,Propolis,TiO2,Dye

Destekleyen Kurum

TÜBİTAK

Proje Numarası

1649B031600549

Teşekkür

Thanks to TÜBİTAK for financial support.

Kaynakça

1. 1. Chen, X., Burda, C. 2008. “The electronic origin of the visible-light absorption properties of C-, N- and S-doped TiO2 nanomaterials” J. Am. Chem. Soc., 130, 5018–5019. DOI: 10.1021/ja711023z
2. 2. Zaleska, A. 2008. “Doped-TiO2: A review” Recent Patents on Engineering 2, 157-164.
3. 3. Martins, A. C., Cazetta, A. L., Pezoti, O., Souza, J. R.B., Zhang, T., Pilau, E. J., Asefa, T., Almeida V. C. 2017. “Sol-gel synthesis of new TiO2/activated carbon photocatalyst and its application for degradation of tetracycline”, Ceram. Intern. 43, 4411–4418. http://dx.doi.org/10.1016/j.ceramint.2016.12.088
4. 4. Leary, R., Westwood A. 2011. “Carbonaceous nanomaterials for the enhancement of TiO2 photocatalysis”, Carbon 49, 741–772.
5. 5. Dong, F., Guo, S., Wang, H., Li X., Wu, Z. 2011. “Enhancement of the visible light photocatalytic activity of C-doped TiO2 nanomaterials prepared by a green synthetic approach”, J. Phys. Chem. C 115, 13285–13292. doi.org/10.1021/jp111916q
6. 6. Rahman, M. N. A., Rahim, N. A. A., Kamarudin, W. F. W., Irwan, Z., Amin, A. R. M., Muhammud, A., Muda, S. M., Akhir, N. E. F. M. 2018. “Solar photocatalytic degradation of food dye (Tartrazine) using zinc oxide catalyst” Int. J. Eng. Technol. 7, 222-226.
7. 7. Zazouli, M. A., Ghanbari, F., Yousefi, M., Madihi-Bidgolie, S. 2017. “Photocatalytic degradation of food dye by Fe3O4-TiO2 nanoparticles in presence of peroxymonosulfate: The effect of UV sources” J. Environ. Chem. Eng., 5, 2459-2468.
8. 8. Ranade, M.R., Navrotsky, A., Zhang, H.Z., Banfield, J.F., Elder, S.H., Zaban, A., Borse, P.H., Kulkarni, S.K., Doran, G.S., Whitfield H.J. 2002. “Energetics of nanocrystalline TiO2” PNAS 99, Suppl. 2, 6476-6481.

9. 9. Zhang, H., Banfield, J.F. 2002. “Kinetics of crystallization and crystal growth of nanocrystalline anatase in nanometer-sized amorphous titania” J. Chem. Mater. 14, 4145-4154.
10. 10. Koç Keşir, M., Dilber, G., Sökmen, M., Durmuş, M. 2019. “Use of new quaternized water soluble zinc phthalocyanin derivatives for effective dye sensitization of TiO2”. J. Sol-Gel Sci. Technol. https://doi.org/10.1007/s10971-019-05109-w
11. 11. Sökmen, M., Koc Kesir, M., Alomar, S. Y. 2017. “Phthalocyanine-TiO2 nanocomposites for photocatalytic applications: A review” Am. J. Nanosci. 3, 63-80.