The comparison of color stability of composite resins after ımmersion in different drinks

Yıl 2013, Cilt: 23 Sayı: 1, 24 - 29, 01.01.2013

Öz

Purpose: The purpose of this study was to evaluate the color stability of different composite resins upon exposure to different drinks which were highly consumed in daily life. Materials and methods: Twenty-five disc-shaped (15×2 mm) cylindrical specimens were prepared for each of 6 different composite resins (Filtek Silorane, Aelite Aesthetic Enamel, Quixfill, Ceram X Mono, Grandio, IntenS). The specimens of each composite resin groups were divided into 5 subgroups (n=5) for storage for 48 hours at 37°C in different types of solutions: water, coffee, tea, cola, and red wine. The color values of all groups were measured before and after exposure to different solutions with a colorimeter (Minolta CR-300). Data were recorded according to the CIE L*a*b* system and then color changes (ΔE*) were calculated. The statistical analysis of the color variation data included a 2way analysis of variance (ANOVA) and the means were compared by Tukey HSD test (α=.05). Results: For the 6 restorative materials tested, the lowest ΔE* values were observed in the water immersed group (p<0.05). The highest color differences were observed in the red wine and coffee immersed groups (p<0.05). When comparing the restorative materials, Aelite Aesthetic Enamel and Filtek Silorane demonstrated significantly showed less color change than the other composite groups (p<0.05). Conclusions: Discoloration of composite resins is based on the composition of the composite resins as well as the type of the drinks. Silorane-based composite resins are resistant to external discoloration.

Kaynakça

  • Fontes S T, Fernandez M R, de Moura C M, Meireles S S. Color stability of a nanofill composite: effect of different immersion media. J Appl Oral Sci 2009; 17: 388-91.
  • Mundim F M, Garcia Lda F R, Cruvinel D R, Lima F A, Bachmann L, Pires-de-Souza Fde C. Color stability, opacity and degree of conversion of preheated composites. J Dent 2011;39: e25-9.
  • Nasim I, Neelakantan P, Sujeer R, Subbarao C V. Color stability of microfilled, microhybrid and nanocomposite resins--an in vitro study. J Dent 2010; 38s: e137-42.
  • Pires-de-Souza Fde C, Garcia Lda F, Roselino Lde M, Naves L Z. Color stability of silorane-based composites submitted to accelerated artificial ageing--an in situ study. J Dent 2011; 39s: e18
  • Perez M M, Ghinea R, Ugarte-Alvan L I, Pulgar R, Paravina RD. Color and translucency in siloranebased resin composite compared to universal and nanofilled composites. J Dent 2010; 38s: e110-6.
  • Türkün L S, Türkün M. Effect of bleaching and repolishing procedures on coffee and tea stain removal from three anterior composite veneering materials. J Esthet Restor Dent 2004; 16: 290-301.
  • Patel S B, Gordan V V, Barret A A, Shen C. The effect of surface finishing and storage solutions on the color stability of resin-based composites. J Am Dent Assoc 2004; 135: 587-94.
  • Guler A U, Yılmaz F, Kulunk T, Guler E, Kurt S. Effects of different drinks on stainability of resin composite provisional restorative materials. J Prosthet Dent 2005; 94: 118-24.
  • Ertaş E, Güler A U, Yücel A C, Köprülü H, Güler E. Color stability of resin composites after immersion in different drinks. Dent Mater J 2006; 25: 371-6.
  • Inokoshi S, Burrow MF, Kataumi M, Yamada T, Takatsu T. Opacity and color changes of toothcolored restorative materials. Oper Dent 1996; 21:73-80.
  • Yannikakis S A, Zissis A J, Polyzois G L, Caroni C. Color stability of provisional resin restorative materials. J Prosthet Dent 1998; 80: 533-9.
  • Ergücü Z, Türkün L S, Aladag A. Color stability of nanocomposites polished with one-step systems. Oper Dent 2008; 33: 413-20.
  • Ferracane J L. Buonocore Lecture. Placing dental composites--a stressful experience. Oper Dent 2008; 33: 247-57.
  • Boaro L C, Gonçalves F, Guimaraes T C, Ferracane J L, Versluis A, Braga R R. Polymerization stress, shrinkage and elastic modulus of current lowshrinkage restorative composites. Dent Mater 2010; 26: 1144-50.
  • Duarte Jr S, Phark J H, Varjao F M, Sadan A. Nanoleakage, ultramorphological characteristics, and microtensile bond strengths of a new lowshrinkage composite to dentin after artificial aging. Dent Mater 2009; 25: 589-600.
  • Lien W, Vandewalle K S. Physical properties of a new silorane-based restorative system. Dent Mater 2010; 26: 337-44.
  • Arocha MA, Mayoral JR, Lefever D, Mercade M, Basilio J, Roig M. Color stability of siloranes versus methacrylate-based composites after immersion in staining solutions. Clin Oral Investig 2012; Sep 20. [Epub ahead of print]

Farklı içeceklerde bekletilen kompozit rezinlerin renk stabilitelerinin karşılaştırılması

Yıl 2013, Cilt: 23 Sayı: 1, 24 - 29, 01.01.2013

Öz

Amaç: Bu çalışmanın amacı günlük hayatta sıkça tüketilen içeceklerde bekletilen farklı kompozit rezinlerin renk stabilitelerini değerlendirmektir. Gereç ve Yöntem: Altı farklı kompozit rezin grubundan (Filtek Silorane, Aelite Aesthetic Enamel, Quixfill, Ceram X Mono, Grandio, IntenS) disk şeklinde (15x2mm) 25’er adet örnek hazırlandı. Her bir kompozit grubunda hazırlanan örnekler 5 alt gruba ayrılarak (n=5) farklı tipteki solüsyonlarda (su, kahve, çay, kola ve kırmızı şarap) 37°C’ de 48 saat süresince bekletildi. Bütün gruplardaki kompozit örneklerin renk değerleri solüsyonlarda bekletilmeden önce ve bekletildikten sonra kolorimetre cihazı (Minolta CR-300) ile ölçüldü. Veriler CIE L*a*b* sistemine göre kaydedilerek renk farklılıkları (ΔE*) hesaplandı. Renk değişimlerinin istatistiksel analizi çift yönlü varyans analizi (Two-way ANOVA) ile yapılırken ortalamaların çoklu karşılaştırılması için Tukey HSD testi (α=.05) kullanıldı. Bulgular: Test edilen 6 farklı kompozit rezin için en düşük ΔE* değerleri su içerisinde bekletilen gruplarda tespit edilmiştir (p<0.05). En yüksek renk değişimi ise kırmızı şarap ve kahvede bekletilen gruplarda tespit edilmiştir (p<0.05). Restoratif materyaller karşılaştırıldığında Aelite Aesthetic Enamel, ve Filtek Silorane gruplarında belirgin olarak daha az renk değişimi gözlenmiştir (p<0.05). Sonuç: Kompozit rezinlerde oluşan renklenmelerin içeceğin tipi ve rezin kompozitin bileşimi ile ilgili olduğu tespit edilmiştir. Siloran esaslı kompozit rezinler dışsal renklenmelere karşı dirençlidir.

Kaynakça

  • Fontes S T, Fernandez M R, de Moura C M, Meireles S S. Color stability of a nanofill composite: effect of different immersion media. J Appl Oral Sci 2009; 17: 388-91.
  • Mundim F M, Garcia Lda F R, Cruvinel D R, Lima F A, Bachmann L, Pires-de-Souza Fde C. Color stability, opacity and degree of conversion of preheated composites. J Dent 2011;39: e25-9.
  • Nasim I, Neelakantan P, Sujeer R, Subbarao C V. Color stability of microfilled, microhybrid and nanocomposite resins--an in vitro study. J Dent 2010; 38s: e137-42.
  • Pires-de-Souza Fde C, Garcia Lda F, Roselino Lde M, Naves L Z. Color stability of silorane-based composites submitted to accelerated artificial ageing--an in situ study. J Dent 2011; 39s: e18
  • Perez M M, Ghinea R, Ugarte-Alvan L I, Pulgar R, Paravina RD. Color and translucency in siloranebased resin composite compared to universal and nanofilled composites. J Dent 2010; 38s: e110-6.
  • Türkün L S, Türkün M. Effect of bleaching and repolishing procedures on coffee and tea stain removal from three anterior composite veneering materials. J Esthet Restor Dent 2004; 16: 290-301.
  • Patel S B, Gordan V V, Barret A A, Shen C. The effect of surface finishing and storage solutions on the color stability of resin-based composites. J Am Dent Assoc 2004; 135: 587-94.
  • Guler A U, Yılmaz F, Kulunk T, Guler E, Kurt S. Effects of different drinks on stainability of resin composite provisional restorative materials. J Prosthet Dent 2005; 94: 118-24.
  • Ertaş E, Güler A U, Yücel A C, Köprülü H, Güler E. Color stability of resin composites after immersion in different drinks. Dent Mater J 2006; 25: 371-6.
  • Inokoshi S, Burrow MF, Kataumi M, Yamada T, Takatsu T. Opacity and color changes of toothcolored restorative materials. Oper Dent 1996; 21:73-80.
  • Yannikakis S A, Zissis A J, Polyzois G L, Caroni C. Color stability of provisional resin restorative materials. J Prosthet Dent 1998; 80: 533-9.
  • Ergücü Z, Türkün L S, Aladag A. Color stability of nanocomposites polished with one-step systems. Oper Dent 2008; 33: 413-20.
  • Ferracane J L. Buonocore Lecture. Placing dental composites--a stressful experience. Oper Dent 2008; 33: 247-57.
  • Boaro L C, Gonçalves F, Guimaraes T C, Ferracane J L, Versluis A, Braga R R. Polymerization stress, shrinkage and elastic modulus of current lowshrinkage restorative composites. Dent Mater 2010; 26: 1144-50.
  • Duarte Jr S, Phark J H, Varjao F M, Sadan A. Nanoleakage, ultramorphological characteristics, and microtensile bond strengths of a new lowshrinkage composite to dentin after artificial aging. Dent Mater 2009; 25: 589-600.
  • Lien W, Vandewalle K S. Physical properties of a new silorane-based restorative system. Dent Mater 2010; 26: 337-44.
  • Arocha MA, Mayoral JR, Lefever D, Mercade M, Basilio J, Roig M. Color stability of siloranes versus methacrylate-based composites after immersion in staining solutions. Clin Oral Investig 2012; Sep 20. [Epub ahead of print]
Toplam 17 adet kaynakça vardır.

Ayrıntılar

Birincil Dil Türkçe
Bölüm Makaleler
Yazarlar

Yrd. Doç. Dr. Eda Güler Bu kişi benim

Yrd. Doç. Dr. Nihan Gönülol Bu kişi benim

Doç. Dr. Ali Çağın Yücel Bu kişi benim

Yrd.doç.dr. Fikret Yılmaz Bu kişi benim

Prof.dr. Engin Ersöz Bu kişi benim

Yayımlanma Tarihi 1 Ocak 2013
Yayımlandığı Sayı Yıl 2013 Cilt: 23 Sayı: 1

Kaynak Göster

APA Güler, Y. D. D. E., Gönülol, Y. D. D. . N., Yücel, D. D. . A. Ç., Yılmaz, Y. F., vd. (2013). Farklı içeceklerde bekletilen kompozit rezinlerin renk stabilitelerinin karşılaştırılması. Atatürk Üniversitesi Diş Hekimliği Fakültesi Dergisi, 23(1), 24-29.
AMA Güler YDDE, Gönülol YDDN, Yücel DDAÇ, Yılmaz YF, Ersöz PE. Farklı içeceklerde bekletilen kompozit rezinlerin renk stabilitelerinin karşılaştırılması. Ata Diş Hek Fak Derg. Ocak 2013;23(1):24-29.
Chicago Güler, Yrd. Doç. Dr. Eda, Yrd. Doç. Dr. Nihan Gönülol, Doç. Dr. Ali Çağın Yücel, Yrd.doç.dr. Fikret Yılmaz, ve Prof.dr. Engin Ersöz. “Farklı içeceklerde Bekletilen Kompozit Rezinlerin Renk Stabilitelerinin karşılaştırılması”. Atatürk Üniversitesi Diş Hekimliği Fakültesi Dergisi 23, sy. 1 (Ocak 2013): 24-29.
EndNote Güler YDDE, Gönülol YDDN, Yücel DDAÇ, Yılmaz YF, Ersöz PE (01 Ocak 2013) Farklı içeceklerde bekletilen kompozit rezinlerin renk stabilitelerinin karşılaştırılması. Atatürk Üniversitesi Diş Hekimliği Fakültesi Dergisi 23 1 24–29.
IEEE Y. D. D. E. Güler, Y. D. D. . N. Gönülol, D. D. . A. Ç. Yücel, Y. F. Yılmaz, ve P. E. Ersöz, “Farklı içeceklerde bekletilen kompozit rezinlerin renk stabilitelerinin karşılaştırılması”, Ata Diş Hek Fak Derg, c. 23, sy. 1, ss. 24–29, 2013.
ISNAD Güler, Yrd. Doç. Dr. Eda vd. “Farklı içeceklerde Bekletilen Kompozit Rezinlerin Renk Stabilitelerinin karşılaştırılması”. Atatürk Üniversitesi Diş Hekimliği Fakültesi Dergisi 23/1 (Ocak 2013), 24-29.
JAMA Güler YDDE, Gönülol YDDN, Yücel DDAÇ, Yılmaz YF, Ersöz PE. Farklı içeceklerde bekletilen kompozit rezinlerin renk stabilitelerinin karşılaştırılması. Ata Diş Hek Fak Derg. 2013;23:24–29.
MLA Güler, Yrd. Doç. Dr. Eda vd. “Farklı içeceklerde Bekletilen Kompozit Rezinlerin Renk Stabilitelerinin karşılaştırılması”. Atatürk Üniversitesi Diş Hekimliği Fakültesi Dergisi, c. 23, sy. 1, 2013, ss. 24-29.
Vancouver Güler YDDE, Gönülol YDDN, Yücel DDAÇ, Yılmaz YF, Ersöz PE. Farklı içeceklerde bekletilen kompozit rezinlerin renk stabilitelerinin karşılaştırılması. Ata Diş Hek Fak Derg. 2013;23(1):24-9.

Bu eser Creative Commons Alıntı-GayriTicari-Türetilemez 4.0 Uluslararası Lisansı ile lisanslanmıştır. Tıklayınız.