Effect of Heat Input on Weld Microstructure in TIG Welding of Duplex Stainless Steels

Öz

Duplex stainless steels are used in many applications as in oil, chemical, petrochemical, nuclear and marine industries. Welding of duplex stainless steels requires higher attention due to changes in ferrite and austenite phase ratio in weld metal. Higher ferrite or austenite phase ratio induces decreases in mechanical properties and corrosion resistance. In this study, effect of heat input on weld microstructure of duplex stainless steels in TIG welding were investigated. Higher heat input induce austenite structure and grain size changes in weld metal.

Anahtar Kelimeler

• Duplex stainless steels,TIG welding,Mechanical properties

Çift Fazlı Paslanmaz Çeliklerin TIG Kaynağında Isı Girdisinin Kaynak Mikroyapısı Üzerindeki Etkisi

Öz

Çift fazlı paslanmaz çelikler kimya, petrokimya ve nükleer sanayii ile açık deniz uygulamalarında yaygın bir kullanıma sahiptir. Çift fazlı paslanmaz çeliklerin kaynağı, kaynak metalinde ferrit ve östenit faz oranlarının değişimi nedeniyle yüksek özen gerektirmektedir. Ferrit veya östenit oranı mekanik özelliklerin ve korozyon dayanımının olumsuz yönde değişmesine neden olmaktadır. Bu çalışmada, çift fazlı paslanmaz çeliklerin TIG kaynağında ısı girdisinin kaynak mikroyapısı üzerindeki etkisi araştırılmıştır. Yapılan çalışmalar sonucunda yüksek ısı girdisinin östenit yapısında ve tane boyutunda değişimlere yol açtığı belirlenmiştir.

Anahtar Kelimeler

• Çift fazlı paslanmaz çelikler,TIG kaynağı,Mekanik özellikler

Kaynakça

1. 1. Kısasöz, A., Karaaslan A., 2014. Finite Element Analysis of 2205 Duplex Stainless Steel Welds, Materials Testing, 56, 795-799.
2. 2. Kısasöz, A., Gurel, S., Karaaslan A., 2016. Effect of Annealing Time and Cooling Rate on Precipitation Processes in a Duplex Corrosion-Resistant Steel, Metal Science and Heat Treatment, 57, 544-547.
3. 3. Neessen, F., Bandsma, P., Smitweld, L., 2001. Tankers – A Composition in Duplex Stainless Steels, Welding Innovation, 18, 2-8.
4. 4. Horvarth, W., Prantl, W., Stuwe, H.P., Werner, E., 1995. Influence of Thermal Cycling on the Microstructure of a Ferritic–Austenitic Duplex Stainless Steel, Materials Characterization, 34, 277-285.
5. 5. Hertzman, S., Ferreira, P.J., Brolund, B., 1997. An Experimental and Theoretical Study of Heat-Affected Zone Austenite Reformation in Three Duplex Stainless Steels, Metallurgical and Materials Transactions, 28 A, 277-285.
6. 6. Geng, S., Sun, J., Gou, L., Wang, H., 2015. Evolution of Microstructure and Corrosion Behavior in 2205 Duplex Stainless Steel GTA Welding Joint, Journal of Manufacturing Processes, 19, 32-37.
7. 7. Ramirez, A.J., 2003. The Relationship Between Chromium Nitride and Secondary Austenite Precipitation in Duplex Stainless Steels, Metallurgical and Materials Transactions A, 34A, 1575-1597.