Effect of Different Coloured Resin Cements on the Shade of CAD/CAM Ceramics-Pilot Study

Yıl 2016, , 26 - 35, 01.01.2016

Şeyda Adıgüzel Neslin Velioğlu Seda Cengiz Selçuk Oruç

https://doi.org/10.21306/jids.2016.1.19

Öz

Aim: According to the improvements in full ceramic systems as well as resin cements, it is possible to obtain restoration shaving very similar optical properties with the natural tooth. The aim of this study is to examine the effect of different coloured resin cements on the CAD/CAM veneer ceramic cemented on zirconia specimens. Material and Method: IPS E max, Vita Suprinity and Vita Enamic all ceramic samples were prepared at A2 shade and appropriate veneer thickness 1,5 mm . First color measurements were performed with a spectrophotometer without cement, then put on zirconium with appropriate core thickness and recorded as CIE L*a*b* color system. All ceramic samples cemented to zirconium cores optically with Light, transparan shades of Panavia F and white, white opaque, yellow shades of Kerr. Second color measurements were performed and recorded tedavilerinde dayanak materyali olarak hakim bir yer almaktaydı. Ancak, estetiğin önemli olduğu ön bölgede özellikle dişetlerinin ince olduğu ve implantın bukkale doğru yerleştirildiği vakalarda titanyum dayanakların dişetinden yansıyan gri rengi estetik sıkıntılar oluşturduğu için, seramik dayanaklar gündeme gelmiştir. Günümüzde, zirkonya ve alumina dayanaklar estetik bölgelerde yaygın olarak kullanılmaktadır 9 . Üstün estetik özelliklerinden dolayı seramik dayanaklar mukozada renk değişikliğine neden olmazlar 10 . CAD/CAM sistemleri seramik dayanaklar için çok farklı olanaklar sunmaktadır 9 . Tam seramiklerin optik özelliklerini etkileyen faktörler göz önüne alınarak, CAD/CAM seramik çeşitlerinin ve rezin siman renklerinin zirkon dayanak opasitesini maskelemesi ve restorasyonun rengine etkisi incelemeye değerdir. Yapılan çalışmalar, tam seramik sistemlerde rengin, alt yapı materyalinin rengi ve kalınlığı, üst yapıda kullanılan porselenin fırınlama sayısı ve kalınlığı, glazür işlemleri ve aynı zamanda seçilen simantasyon ajanına da bağlı olduğunu göstermektedir 11 .Bu bilgilerin ışığı altında çalışmamızın amacı, zirkon alt yapılar üzerine farklı tip CAD/CAM seramik bloklarla hazırlanmış örneklerin rengine, farklı renk rezin simanların etkisinin değerlendirilmesidir. Özellikle estetik amaçla kullanılan lityum disilikat seramikleri kuvvetlendirmek için yapısına eklenen zirkonyum ve rezinin estetik açıdan bir değişikliğe neden olup olmayacağı, kullanılan rezin simanların final restorasyon rengine etkisinin değerlendirilmesi hipotezimizi oluşturmaktadır

Anahtar Kelimeler

CAD/CAM, Ceramic, Resin cement, Shade, Zirconium.

Farklı Renkteki Rezin Simanların CAD/CAM Seramiklerin Rengine Etkisi-Pilot Çalışma

Öz

Amaç: Tam seramik sistemlerin ve rezin simanların geliştirilmesi ile beraber, optik özellikleri doğal dişe çok yakın restorasyonlar elde edilebilmektedir. Bu çalışmanın amacı; farklı renklerdeki rezin simanların zirkon örnekler üzerine yapıştırılacak, çeşitli CAD/CAM veneer seramiklerinin rengine etkisini incelemektir.Gereç ve Yöntem: A2 renginde ve uygun veneer kalınlıklarında 1,5mm , IPS e.max CAD, Vita Enamic ve Vita Suprinity örnekler hazırlandı. İlk ölçümler siman uygulamadan önce, uygun alt yapı kalınlığında hazırlanan zirkonyum örnekler üzerine konularak spektrofotometre cihazıyla yapıldı ve CIE L*a*b* renk sisteminde kaydedildi. Daha sonra veneer örnekler zirkon alt yapılara Panavia F transparan, light ve Kerr white, white opak, yellow rezin simanlar ile yapıştırıldı. İkinci renk ölçümleri yapıldı ve CIE L*a*b* renk sisteminde kaydedildi. Renk farklılıkları ΔE hesaplandı ve Wilcoxon testi ve Kruskal-Wallis testi ile istatistiksel olarak analiz edildi.Bulgular: Simanlar arasındaki bütün renk değişiklikleri ΔE istatistiksel olarak anlamlı olmadığı gözlendi. Tam seramik örneklerin, siman uygulanmadan önce ve uygulandıktan sonraki CIE L*a*b* değerleri arasında ise, istatistiksel açıdan anlamlı farklılık tespit edilemedi p

Anahtar Kelimeler

CAD/CAM, Renk, Rezin siman, Seramik, Zirkonyum.

Kaynakça

• 1. Douglas RD. Precision of in vivo colorimetric assessments of teeth. J Prosthet Dent.1997; 77: 70-469.
• 2. Niu E,Agustin M,& Douglas RD. Color match of machinable lithium disilicate ceramics: Effects of cement color and thickness. J Prosthet Dent. 2014; 111(1): 42-50.
• 3. Yaman P, Qazi SR, Dennison JB, Razzoog ME. Effect of adding opaque porcelain on the final color of porcelain laminates. J ProsthetDent. 1997; 77(2):40-136.
• 4. Vichi A, Ferrari M, Davidson CL. Influence of ceramic and cement thickness on the masking of various types of opaque posts. J ProsthetDent. 2000; 83:7-412.
• 5. Terzioglu H, Yilmaz B, Yurdukoru B. The effect of different shades of specific luting agents and IPS empress ceramic thickness on over all color. Int J Periodontics Rest Dent.2009; 29(5):499-505.
• 6. Barath VS, Faber FJ, Westland S, Niedermeier W. Spectrophotometric analysis of all-ceramic materials and their interaction with luting agents and different backgrounds. Adv Dent Res.2003; 17:55-60.
• 7. Chang J, Silva J, Sakai M, Kristiansen J, Nagai S. The optical effect of composite luting cement on all ceramic crowns. J Dent. 2009; 37: 43-937.
• 8. Alqahtanı MQ, Aljuraıs RM, Alshaafı MM. The effects of different shades of resin luting cement on the color of ceramic veneers. Dent Mater J.2012; 31(3): 354-361.
• 9. Günal B, Ulusoy M, DurmaYüksel TM, & Yılmaz SK. Seramik abutmentlerin mekanik, biyolojik ve estetik açıdan değerlendirilmesi. Atatürk Ünv Diş Hek Fak Derg. 2015; 10.
• 10. Vanlıoğlu B, Özkan Y., & Özkan, Y. K. Estetik bölgede implant-üstü restorasyonlarda güçlendirilmiş seramik dayanaklar. Atatürk Ünv Diş Hek Fak Derg. 2012; (5).
• 11. Chu FCS, Chow TW, Chai J, DLaw MJ. Contrast ratios and masking ability of three types of ceramic veneers. J Prosthet Dent. 2007; 98: 359-364.
• 12. Dede DÖ,Armaganci A, Ceylan G, Çankaya S, & Çelık E. Influence of abutment material and luting cements color on the final color of all ceramics. Acta Odontol Scand. 2013; 71(6): 1570-1578.
• 13. Yavuzyılmaz H, Turhan B, Bavbek B, Kurt E. Tam Porselen Sistemleri. Gazi Ünv Diş Hek Fak Derg. 2005; 22(1):8-41.
• 14. Kelly JR, Nishimura I, Campbell SD. Ceramics in dentistry: Historical roots and current prespectives. J Prosthet Dent. 1996; 75: 18-32.
• 15. Kilinc E, Antonson SA, Hardigan PC, & Kesercioglu A. Resin cement color stability and its influence on the final shade of all-ceramics. J Dent. 2011; 39: 30-36.
• 16. Rosentiel SF, Land M, Fujimoto J. Contemporary Fixed Prosthodontics. 3rd Ed. St. Louis:CV Mosby; 2001.
• 17. Heffernan MJ, Aquilino SA, Diaz- Arnold AM, Haselton DR, Stanford CM, Vargas MA. Relative translucency of six all-ceramic systems. Part I: Core materials. J Prosthet Dent. 2002; 49-88.
• 18. Conrad HJ, Seong WJ, Pesun IJ. Current ceramic materials and systems with clinical recommendations: a systematic review. J Prosthet Dent. 2007; 98(5):389-404.
• 19. Odén A, Andersson M, Krystek-Ondracek I, & Magnusson D. Five-year clinical evaluation of Procera All Ceram crowns. J Prosthet Dent. 1998; 80(4): 450-456.
• 20. Kürklü D, Azer SS, Yilmaz B, & Johnston WM. Porcelain thickness and cement shade effects on the colour and translucency of porcelain veneering materials.J Dent. 2013; 41(11): 1043-1050.
• 21. Yaman P, Qazi SR, Dennison JB, Razzoog ME. Effect of adding opaque porcelain on the final color of porcelain laminates. J ProsthetDent. 1997; 77(2):40-136.
• 22. Vichi A, Ferrari M, Davidson CL. Influence of ceramic and cement thickness on the masking of various types of opaque posts. J Prosthet Dent. 2000; 83:7-412.
• 23. Chu SJ, Devigus A, Mieleszko A. Fundamentals of color shade matching and communication in esthetic dentistry. Quintessence Pub Co Inc, 2004; 14-6.
• 24. Paul S, Peter A, Pietrobon N, Hammerle CH. Visual and spectrophotometric shade analysis of human teeth. J Dent Res. 2002; 81 (8): 578-82.
• 25. Lath DL, Wildgoose DG, Guan YH, Lilley TH, Smith RN, Brook AH. A digital image analysis system for the assessment of tooth whiteness compared to visual shade matching. J Clin Dent. 2007; 18 (1): 17-20.
• 26. Carossa S, Lombardo S, Pera P, Corsalini M, Rastello ML, Preti PG. Influence of posts and cores on light transmission through different all-ceramic crowns: spectrophotometric and clinical evaluation. Int J Prosthodont. 2001; 14(1):9-14.
• 27. Azer SS, Drummond JL, Campbell SD, & Zaki AEM. Influence of core build up material on the fatigue strength of an all-ceramic crown. J Prosthet Dent. 2001; 86(6): 624-631.
• 28. Chaiyabutr Y, Kois JC, Lebeau D, Nunokawa G. Effect of abutment tooth color, cement color, and ceramic thickness on the resulting optical color of a CAD/CAM glass-ceramic lithium disilicate-reinforced crown. J Prosthet Dent. 2011; 105(2): 83-90.
• 29. De AzevedoCubas GB, Camacho GB, Demarco FF, Pereira-Cenci T. The effect of luting agents and ceramic thickness on the color variation of differentceramics against a chromatic background. Eur J Dent. 2011; 5(3):52-245.
• 30. Uzun G, Keyf F. Effect of differrent cement colors on the final color of Ips Empress ceramic restorations. Biotechnol&Biotechnol EQ. 2007;21:4-10.
• 31. Bilmeyer FW, Saltzman M. Principles of color technology. 3rd ed. New York: John Wiley&Sons; 1981.
• 32. Seghi, RR, Johnston, WM, O’Brien, WJ. Spectrophotometric analysis of color differences between porcelain systems. J Prosthet Dent. 1986; 56:35-40.
• 33. Bayındır F, WeeAg. The use of computer aided systems on tooth shade matching. Hacettepe Dişhek Fak Derg. 2006; 30: 40-46.
• 34. Chu SJ, Trushkowsky RD, Paravina RD. Dental color matching instruments and systems. Review of clinical and research aspects. J Dent. 2010; 38(2):2-16.