Relationship between Wood Physical Properties of English Oak (Quercus robur L.) and Soil Variables

Yıl 2016, Cilt: 12 Sayı: 1, 61 - 71, 15.06.2016

İbrahim Bektaş Suphi Oruç Bekir Cihad Bal , Ayşenur Kılıç Ak

Öz

In this study, some of the physical properties of the Q. robur L. wood, which is one of the most important tree species in the forestry of Turkey, and primary soil elements that have an effect during the formation of these properties, were investigated. For this purpose, test trees that were supplied from Dörtyol (Hatay) region were used. As a result of the tests, it was found that the annual ring width of Quercus robur L. wood was 2.1 mm, air dry density was 0.776 g/cm3, complete dry density was 0.721 g/cm3, volume-density value was 0.612 g/cm3, radial direction shrinking was 4.9%, tangential direction shrinking was 6.5%, volumetric shrinking was 11.4%, tangential direction swelling was 9.5%, radial direction swelling was 5.2% and volumetric swelling was found as 14.7%. According to obtained data, it was understood that it is rather suitable to grow Quercus robur L. wood in the soil characteristics of the habitat.

Anahtar Kelimeler

English oak, Density, Shrinkage, Swelling, Soil characteristics

Saplı Meşe (Quercus robur L.) Odununun Fiziksel Özelliklerinin Toprak Değişkenleriyle İlişkisi

Öz

Bu çalışmada, Türkiye ormancılığının önemli ağaç türlerinden biri olan Saplı meşe (Q. robur L.) odununun bazı fiziksel özellikleri ile bunların oluşumunda etkili olan başlıca toprak elamanları üzerinde çalışılmıştır. Bu amaçla testlerde, Dörtyol (Hatay) yöresinden temin edilen deneme ağaçları kullanılmıştır. Yapılan deneyler sonucunda, Saplı meşede yıllık halka genişliği 2.1 mm, hava kurusu yoğunluk 0.776 g/cm3, tam kuru yoğunluk 0.721 g/cm3, hacim-ağırlık değeri 0.612 g/cm3, radyal yönde daralma %4.9, teğet yönde daralma %6.5, hacmen daralma %11.4, teğet yönde genişleme % 9.5 radyal yönde genişleme %5.2 ve hacmen genişleme %14.7 olarak bulunmuştur. Elde edilen bulgulara göre, yetişme ortamı toprak özelliklerinin, meşenin yetişmesi için oldukça uygun oranlarda olduğu anlaşılmıştır.

Anahtar Kelimeler

Saplı meşe, Yoğunluk, Daralma, Genişleme, Toprak özellikleri

Kaynakça

• Anonim, 2014. Türkiye Orman Varlığı. TC. Orman ve Su İşleri Bakanlığı, Orman Genel Müdürlüğü, Orman İdaresi ve Planlama Dairesi Başkanlığı, Yayın No: 115, Ankara.
• As, N., Dündar, T., Büyüksarı, Ü. 2008. Budakların Odunun Fiziksel ve Mekanik Özellikleri Üzerine Etkileri İstanbul Üniversitesi Orman Fakültesi Dergisi Cilt:58 Sayı:2
• Bal, B.C. 2011. Okaliptüs grandis (Eucalyptus grandis W. Hill ex maiden) odununun fiziksel ve mekanik özellikleri ve lamine ağaç malzeme üretiminde kullanılması üzerine araştırmalar, KSÜ Fen Bilimleri Enstitüsü, Doktora Tezi, Kahramanmaraş.
• Bal, B. C., Bektaş, İ., Tutuş, A., Kaymakçı, A. 2011. The Within-Tree Variation in Some Physical Properties in Eucalyptus Grandis Grown in Karabucak Region, Düzce University journal of forestry, 7 (2):82-88.
• Bal, B. C., Bektaş, İ. 2012. The physical properties of heartwood and sapwood of Eucalyptus grandis, Proligno, 8 (4):35-43.
• Bal, B. C., Bektaş, İ., Kaymakçı, A. 2012, Toros Sedirinde Genç Odun ve Olgun Odunun Bazı Fiziksel ve Mekanik Özellikleri, KSÜ, Journal of Engineering Sciences 15 (2):17-27.
• Bal, B.C. 2013. Effects of Heat Treatment on the Physical Properties of Heartwood and Sapwood of Cedrus Libani. Bioresources 8(1):211-219.
• Bal, B.C., Bektaş, İ. 2013. The Mechanical Properties of Heartwood and Sapwood of Eucalyptus Grandis Grown in Karabucak, Turkey, Düzce University Journal of Forestry, 9 (1):71-77.
• Bircan, Ş. 2008. Batı Karadeniz Kıyı Bölgesinde Yetişen Kayın (Fagus orientalis Lipsky) Odununun Fiziksel ve Mekanik Özelliklerinin Yetişme Ortamı Değişkenleriyle İlişkisi. Düzce Üniversitesi, Fen Bilimleri Enstitüsü, Yüksek Lisans Tezi, Düzce.
• Bozkurt, A. Y., Göker, Y. 1996. Orman Ürünlerinden Faydalanma. İstanbul Üniversitesi, Orman Fakültesi, İstanbul.