Properties of UV-Curable Bisphenol-A Glycerolate Diacrylate Coatings Containing 1H,1H,2H,2H-Perfluorodecyl Acrylate Monomer

Yıl 2018, , 836 - 844, 30.09.2018

Mustafa Çakır , Emre Akın Perihan Ulak

https://doi.org/10.31202/ecjse.426693

Cited By: 1

Öz

In this study, fluorine chains were bonded with covalently in epoxy acrylate system via UV light. For this purpose, five different coating samples prepared. Bisphenol-A glycerolate diacrylate (epoxy acrylate) and 1,6-Hexanediol diacrylate were used as the main coating solution. The weight ratio of Bisphenol-A glycerolate diacrylate and HDDA was determined as 7/3. As a long fluorine chain, 1H,1H,2H,2Hperfluorodecyl acrylate (PFOA) was added into the main coating solution in the ratios of 0.25 wt %, 0.50 wt %, 0.75 wt % and 1 wt %. All prepared solutions were coated on aluminum plates by 75 µm by wire wound applicator and then cured via UV dryer. Physical properties of coatings were measured by tests such as MEK rubbing test for solvent resistance, gloss 60o test for brightness, cross-cut test for adhesion property and pencil hardness test for scratch resistance. Hydrophobicity was measured as static water contact angle test. The total surface energy was calculated by contact angle measurement software. In terms of mechanical properties, sheen impact test (for coating samples) and Shore - D hardness tests (for free film samples) were carried out. By examining the results of all these tests; cross-cut adhesion and gloss 60o values decrease with the fluorine
content. On the other hand, by the increasing within the content of the fluorine chains, Taber abrasion resistance and hydrophobicity increase significantly but sheen impact resistance and Shore - D hardness values decrease slightly. In terms of cost and overall results, the most proper and multifunctional coating seemed at 0.25 wt %.

Anahtar Kelimeler

Epoxy acrylate, 1H, 2H, 2H-perfluorodecyl acrylate, UV-curable coatings, hydrophobic surface

1H, 1H, 2H, 2H-Perflorodesil Akrilat Monomeri İçeren UV ile Sertleşebilen Bisfenol – A Gliserolat Diakrilat Kaplamalarının Özellikleri

Öz

Bu çalışmada flor zincirleri, UV ışığı ile sertleşebilen epoksi akrilat sistemine kovalent olarak bağlandı. Bu amaçla beş farklı kaplama örneği hazırlanmıştır. Ana kaplama çözeltisi olarak Bisfenol-A gliserolat diakrilat (epoksiakrilat) ve 1,6-Heksandiol diakrilat kullanıldı. Bisfenol-A gliserolat diakrilat ve HDDA'nın ağırlık oranı 7/3 olarak belirlendi. Uzun bir flor zinciri olarak 1H, 1H, 2H, 2H-perflorodesil akrilat (PFOA) ağırlıkça % 0.25, % 0.50, % 0.75 ve % 1 oranlarında ana kaplama çözeltisi içine ilave edildi. Hazırlanan tüm çözeltiler, alüminyum plakalar üzerinde 75 µm tel sargılı aplikatör ile kaplandı ve daha sonra UV kurutucu ile sertleştirildi. Kaplamaların fiziksel özellikleri; solvent direnci MEK ovma testiyle, parlaklık 60o parlaklık ölçüm testiyle, çizilme direnci kalem sertliği testiyle, yapışma özelliği çapraz-kesme testiyle yapılmıştır. Yüzeylerin hidrofob özelliği statik su temas açısı testiyle ölçüldü. Toplam yüzey enerjisi temas açısı ölçüm yazılımı ile hesaplandı. Mekanik özellikler açısından, Sheen darbe testi (kaplama numuneleri için) ve Shore-D sertlik testleri (serbest film numuneleri için) yapıldı. Bu testlerin sonuçları ele alındığında, çapraz kesme-yapışma ve parlaklık 60o değerleri flor içeriğinin artması ile azaldığı gözlemlendi. Diğer taraftan Taber aşınma direnci ve hidrofobisite önemli ölçüde artmaktadır, ancak darbelere karşı dayanıklılık ve Shore-D sertlik değerleri azalmıştır. Maliyet ve genel sonuçlar açışından bakıldığında en uygun ve çok fonksiyonlu kaplama % 0.25 olduğu bulunmuştur.

Anahtar Kelimeler

Epoksiakrilat, 1H, 2H, 2H-perflorodesil akrilat, UV ile sertleşebilen kaplamalar, hidrofobik yüzey

Kaynakça

• Referans1Chattopadhyay D.K, Panda S.S., Raju K.V.S.N., Thermal and Mechanical Properties of Epoxy Acrylate/Methacrylates UV Cured Coatings, Progress in Organic Coatings 54 (2005) 10–19
• Referans2L. Shen, Y. Li, J. Zheng, M. Lu, K. Wu, Modified epoxy acrylate resin for photocurable temporary protective coatings, Progress in Organic Coatings 89 (2015) 17–25
• Referans3T.C., Canak, Kaya, K., İ.E. Serhatlı, Boron Containing UV - Curable Epoxy Acrylate Coatings, Progress in Organic Coatings 77 (2014) 1911–1918
• Referans4Y.H. Lin, K.H. Liao, C.K. Huang, N.K. Chou, S.S. Wang, S.H. Chuc, K.H. Hsieh, Superhydrophobic films of UV - Curable Fluorinated Epoxy Acrylate Resins, Polymer Int. 2010; 59: 1205–1211
• Referans5M.K. Gosh, K.L Mittal, Polyimides: Fundamentals and Applications, Marcel Dekker, New York, 1996, pp 7–48.
• Referans6L. Tao, H. Yang, J. Liu, L. Fan, S. Yang, Synthesis and Characterization of Highly Optical Transparent and Low Dielectric Constant Fluorinated Polyimides, Polymer 50 (2009) 6009–6018
• Referans7K.U. Jeong, J. J. Kim, T.-H. Yoon, Synthesis and Characterization of Novel Polyimides Containing Fluorine and Phosphine Oxide Moieties, Polymer 42 (2001) 6019-6030
• Referans8B. Jones, Technical Director, Halocarbon Products Corporation, Fluoropolymers for Coating Applications, JCT Coatings Tech Magazine 1 (2008) 1-10
• Referans9C. Kizilkaya, S. Karataş, N.K. Apohan, A. Gungor, Synthesize and Characterization of Novel Polyimide/SiO2 Nanocomposite Materials Containing Phenyl phosphine Oxide via Sol-Gel Technique, Journal of Applied Polymer Science, 115 (2010) 3256–3264
• Referans10M. V. Kahraman, Z. S. Akdemir, I. Kartal, N. K. Apohan, A. Gungor, Preparation of Fluorine Containing hybrid coatings: Investigation of Coating Performance onto ABS and PMMA Substrates, Polymer Adv. Technol., 22 (2011) 981–986
• Referans11M. V. Kahraman, G. Bayramoglu, Y. Boztoprak, A. Gungor, N. K. Apohan, Synthesis of Fluorinated/Methacrylated Epoxy based Oligomers and Investigation of its Performance in the UV Curable Hybrid Coatings, Progress in Organic Coatings 66 (2009) 52–58
• Referans12Çakir M. Investigation of Coating Performance of UV-Curable Hybrid Polymers Containing 1H,1H,2H,2H-Perfluorooctyltriethoxysilane, Coatings, (2017) 7, 37
• Referans13Shundrina, IK, Vaganova, TA, Kusov, SZ, Rodionov, VI, Karpova, EV, Koval, VV, Gerasimova, YV, Malykhin, EV, “Synthesis and Characterization of Polyimides Based on Novel Isomeric Perfluorinated Naphthylenediamines.” Journal of Fluorine Chemistry, 130 (2009) 733–741