Comparative Experimental Investigation Of The Properties Of Wood With Heat Treatment At Two Different Levels.

Öz

In this study, the draft pieces obtained from sessile oak (Quercus petrea L), chestnut (Castenea sativa), taurus cedar (Cedrus libani), yellow pine (Pinus sylvestris), were heat-treated at 175°C and 205°C and physical measurements and tests were applied to the test samples developed from them according to the relevant standards. As a result, it was determined that the rates of change of the examined physical property data obtained from the experiments of coniferous and broadleaf wood samples heat-treated both in the same cabinet at 175°C and in the same cabinet at 205°C were very close to each other, and that both wood species can be heat-treated together in a cabinet at the average temperature of the two temperatures, so that both wood species can be heat-treated much closer to each other and a significant amount of energy can be saved.

Anahtar Kelimeler

• Wood preservation tecniques
• heat treatment
• hygroscopy
• physical properties

İki Farklı Düzeyde Isıl İşlem Uygulanmış Ahşap Özelliklerinin Karşılaştırmalı Deneysel Olarak İncelenmesi.

Öz

Bu çalışmada, sapsız meşe (Quercus petrea L), kestane (Castenea sativa) toros sediri (Cedrus libani), sarıçam (Pinus sylvestris), odunlarından elde edilen taslak parçalara 175°C ve 205°C ısıl işlem yapılmış ve bunlardan geliştirilen deney örneklerine igili standartlara göre fiziksel ölçüm ve testler uygulanmıştır. Sonuç olarak, hem 175 C sıcaklıktaki aynı kabinde hem de 205C sıcaklıktaki aynı kabinde ısıl işlem görmüş iğne yapraklı ve yayvan yapraklı ahşap örneklerin deneylerinden elde edilen incelenmiş fiziksel özellik verilerinin değişim oranlarının birbirleri ile çok yakın olduğu, her iki ahşap türünün iki sıcaklığın ortalaması sıcaklıkta bir kabinde birlikte ısıl işlem uygulanabileceği böylece, hem iki ahşap türünde birbirine çok daha yakın ısıl işlem etkisi elde edilebileceği hem de önemli miktarda enerji tasarrufu sağlanabileceği belirlenmiştir.

Anahtar Kelimeler

• Ahşap koruma teknikleri
• ısıl işlem
• higroskopi
• fiziksel özellikler

Kaynakça

1. [1] Altunok M., Güneş M. (2022) . Ön Isıl İşlem Uygulanmış Ahşap Kirişlerin Farklı İklim Şartlarındaki Mekanik Davranışlarının İncelenmesi, Gazi Üniversitesi Fen Bilimleri Dergisi,GU J Sci, Part C, 10(2): 300-313).
2. [2] Altunok M. ,Bülbül R., Güneş M. (2023). Farklı Isıl İşlem ve Klimatik Uygulamanın Yapısal Ahşabın Fiziksel ve Mekanik Özellikleri Üzerine Etkilerinin Deneysel İncelenmesi ,Gazi Üniversitesi Fen Bilimleri Dergisi11(1):263-272.
3. [3] Aydemir D., Gündüz G.(2009). Ahşabın Fiziksel, Kimyasal, Mekanik Ve Biyolojik Özellikleri Üzerine Isıyla Muamelenin Etkisi, Bartın Orman Fakültesi Dergisi Cilt:11,Sayı:15,71-81.
4. [4] Bürüç D., Aydemir G., Bakır K. (2019). Doğu Kayını ve Saplı Meşe Odunlarının Bazı Özellikleri Üzerine Isıl İşlemin Etkisi, Bartın Üniversitesi, Orman Fakültesi Dergisi ,21(3): 713-721.
5. [5] Doruk Ş., Altunok M., Perçin O. (2010), Emprenye ve Isıl İşlemin Ahşap Malzemenin Bazı Fiziksel ve Mekanik Özelliklerine Etkileri , Politeknik Dergisi, 2023; 26(4). [6] Fengel D and Wegener G.(1989) , Wood : Chemistry, Ultrastructure Reactions Walter De Germany.
6. [7] Flanagan, (2017) , Kompozit Ahşap Kuleler, 80 Katlı Ahşap Gökdelen Projesi. Ahşap Yapılarda Koruma ve Onarım Sempozyumu 5 (s. 179-192). İstanbul.
7. [8] Perçin O.,Uzun O., Saçlı C. (2016), Isıl İşlem Görmüş Meşe Odununun (Quercus Petraea L.) Bazı Fiziksel Özelliklerinin ve Yüzey Pürüzlülüğünün Belirlenmesi,IFC İnternational Furniture Congress.
8. [9] TS ISO 13061 - TS ISO 13061- : Odunun fiziksel ve mekanik özellikleri – Kusursuz küçük ahşap numunelerin deney yöntemleri - Bölüm 1: Fiziksel ve mekanik deneyler için nem muhtevasının belirlenmesi / Physical and mechanical properties of wood - Test methods for small clear wood specimens - Part 1: Determination of moisture content for physical and mechanical tests, Türk standartları Enstitüsü, 2.12.2021, ANKARA.

9. [10] TS EN 4084: Wood- Determination of Radial and Tngential Swelling, 20 December 1983, Türk Standartları. ANKARA.