In this study, ZnFe alloy was deposited on carbon steel electrode (KC) by chronopotentiometry technique. The poly (N-methylpyrrole-co-o-anisidine) (PNMP-co-POA) copolymer film was synthesized on ZnFe coated carbon steel electrode (KC/ZnFe) surface by using cyclic voltammetry technique in 0.30 M oxalic acid solution. PNMP-co-POA coated KC/ZnFe electrode (KC/ZnFe/PNMP-co-POA) is characterized by electrochemical impedance spectroscopy, linear sweep voltammetry and anodic polarization techniques. The Nyquist diagrams showed that the polarization resistance of the KC/ZnF /PNMP-co-POA electrode was significantly higher than that of the KC and KC/ZnFe electrodes, thus demonstrating that the synthesized PNMA-co-POA copolymer film had good anticorrosive properties.
Bu çalışmada ZnFe alaşımı karbon çelik elektrot (KÇ) yüzeyine kronopotansiyometri tekniği ile kaplanmıştır. Poly(N-metilpirol-co-o-anisidin) (PNMP-co-POA) kopolimer filmi ZnFe kaplı karbon çelik elektrot (KÇ/ZnFe) yüzeyine dönüşümlü voltametri tekniği kullanılarak 0.30 M okzalik asit çözeltisinde sentezlenmiştir. Yüzeyine PNMP-co-POA kaplanmış KÇ/ZnFe elektrot (KÇ/ZnFe/PNMP-co-POA) elektrokimyasal empedans spektroskopisi, doğrusal taramalı voltametri ve anodik polarizasyon teknikleriyle karakterize edilerek KÇ ve KÇ/ZnFe elektrotlarıyla karşılaştırılmıştır. Nyquist diyagramları KÇ/ZnFe/PNMP-co-POA elektrodun polarizasyon direncinin KÇ ve KÇ/ZnFe elektrotlarına göre oldukça yüksek olduğunu dolayısıyla sentezlenen PNMA-co-POA kopolimer filmin antikorozif özelliğinin iyi olduğunu göstermiştir.
Primary Language | Turkish |
---|---|
Subjects | Chemical Engineering |
Journal Section | Kimya / Chemistry |
Authors | |
Publication Date | March 1, 2020 |
Submission Date | August 1, 2019 |
Acceptance Date | November 4, 2019 |
Published in Issue | Year 2020 |