Invesitigation of Effect on Physical Properties by Adding Slag Waste to Floor Tile Body

Öz

In this project, it is aimed to utilize the slag waste generated during iron and steel production as an alternative raw material within the scope of industrial symbiosis within the body of ceramic floor tiles. Following the steps in the ceramic tile production process, masse compositions containing slag in different proportions were created. Slag is included in the recipe composition at the rate of 1%, 3%, 5%, 8% and 10%. Physical tests (water absorption, strength, firing shrinkage) were applied to the bodies obtained within the scope of TS EN ISO 10545 standard. Finally, the color values (L*a*b*) of the bodies were measured. As a result of the study, it has been determined that the slag waste can be used in body recipe between 1 and 3wt.% with a certain investment.

Anahtar Kelimeler

• Floor tile
• Iron and steel
• Slag waste
• Recycling

Yer Karosu Bünye Reçetesine Cüruf Atığı İlavesinin Fiziksel Özelliklere Etkisinin İncelenmesi

Öz

Gerçekleşen bu projede demir ve çelik üretimi esnasında ortaya çıkan cüruf atığınının endüstriyel simbiyoz kapsamında alternatif hammadde olarak seramik yer karosu bünyesinde değerlendirilmesi amaçlanmıştır. Seramik karo üretim sürecindeki aşamaları takiben farklı oranlarda cüruf içerikli masse kompozisyonları oluşturulmuştur. Cüruf, reçete kompozisyonuna %1, %3, %5, %8 ve %10 oranında dahil edilmiştir. TS EN ISO 10545 standardı kapsamında elde edilen bünyelere fiziksel testler (su emme, mukavemet, pişme küçülme) uygulanmıştır. Son olarak bünyelerin renk değerleri (L*a*b*) ölçülmüştür. Çalışma sonucunda cüruf atığının belirli bir yatırım sonucunda ve %1-3 oranında kullanılabilir olduğu saptanmıştır.

Anahtar Kelimeler

• Yer karosu
• Demir ve çelik
• Cüruf atığı
• Gerikazanım

Kaynakça

1. [1] Torres P., Fernandes H.R., Agathopoulas S., Tulyaganov D.U., and Ferreira J.M.F., “Incorporation Of Granite Cutting Sludge In Industrial Porcelain Tile Formulations” Journal of European Ceramic Society,24, 3177-3185, 2004
2. [2] Joulazadeh M.H., Joulazadeh F.,” Slag; Value Added Steel Industry By Products “Archives of Metallurgy and Materials, 55, 1137-1145, 2010
3. [3] Ünal S., Yücel O., Kurt M., Gül S. GÜL, “Atık’tan Ürün’e Demir-Çelik Cürufu”, İleri Teknolojiler Çalıştayı, sy. 255-267, 2014
4. [4] Song Q., Guo M.Z., Wang L., and Ling T.C.,” Use of Steel Slag as Sustainable Construction Materialas: A Review of Accelerated Carbonation Treatment” Conservation and Recycling, 173, 105740, 2021
5. [5] Baycık S., “Granüle Yüksek Fırın Curuflarının Karo Sektöründe Kullanılabilirliğinin Araştırılması’’ İstanbul Teknik Üniversitesi, Fen Bilimleri Enstitüsü, Yüksek Lisans Tezi, 138s, İstanbul, 2003
6. [6] Türkiye Seramik Federasyonu, “Seramik Sektörü Yerli Katma Değer Raporu-8. Dönem Faaliyet Raporu”, sy. 13-25, 2019
7. [7] Reed J.S.,” Introduction to The Principles of Ceramic Prosessing” JohnWiley & Sons., 1998
8. [8] Yi H., Xu G., Cheng H., Wang J., Wan Y., and Chen H., “An Overview of utilization of steel slag” Procedia Environ Sci., 16, 791-801, 2012

9. [9] Kaya G., Turan S., “ Yüksek Fırın Cüruflarının Seramik Sektöründe Katma Değeri Yüksek Ürünlerin Eldesinde Değerlendirilmesi” Mühendis ve Makine, 45, 536, 48-60, 2003
10. [10] Teo P.T., et al., “Characterization of EAF Steel Slag Waste: The Potential Green Resource for Ceramic Tile Production” Procedia Chemistry, 19, 842-846, 2016
11. [11] TS EN ISO 10545-3 Seramik Karolar-Su Emme, Görünür Gözeneklilik, Bağıl Yoğunluk ve Hacim Kütlesinin Tayini
12. [12] TS EN ISO 10545-4 Seramik Karolar- Seramik Karolar Eğilme Dayanımı ve Kırılma Dayanımı Tayini
13. [13] Berns R.S.,” Billmeyer and Saltzman's Principles of Color Technology” J. Wiley/New York, 2000
14. [14] Özcan A., “Kağıt Yüzey Pürüzlülüğünün L* a * b * değerleri üzerine etkisinin belirlenmesi” İstanbul Ticaret Üniversitesi Fen Bilimleri Dergisi, 7, 53-61, 2008