INVESTIGATION OF BORON WASTE FOR POTENTIAL USE IN THE SYNTHESIS OF CORDIERITE CERAMICS AT LOWER TEMPERATURES
Öz
The utilization of industrial by-products in ceramic production has become an essential strategy for enhancing both the sustainability and competitiveness of the ceramics industry. This study investigates the valorization of boron waste as a sustainable alternative raw material and sintering additive in the production of cordierite ceramics (2MgO.2Al2O3.5SiO2). Cordierite ceramics are essential for high-temperature applications due to their low coefficient of thermal expansion and excellent thermal shock resistance; however, their synthesis typically requires high temperatures and narrow sintering ranges, leading to high energy consumption. In this work, cordierite bodies were formulated using magnesite, kaolin, and quartz, with boron waste additions ranging from 0 to 1 wt.% to evaluate its potential as a cost-effective fluxing agent. The samples were produced via the slip casting method and sintered at 1260°C and 1320°C for 2 hours. Phase analysis, performed using X-ray diffraction (XRD) and Rietveld refinement. Additionally, the bulk densities of the sintered specimens were determined by the Archimedes method, while their flexural strengths were measured using three-point bending tests. The results, quantified via Rietveld refinement, indicate that the cordierite phase content increased with the addition of 1 wt.% boron waste at 1320°C. Furthermore, a significant improvement in mechanical properties was observed; the flexural strength rose to 30.36 MPa. This study demonstrates that the incorporation of boron waste not only promotes the synthesis of high-performance cordierite ceramics at lower temperatures but also offers a viable pathway for environmental protection and resource management through the effective recycling of industrial wastes.
Anahtar Kelimeler
Cordierite, Boron waste, Phase evolution, Sintering
Destekleyen Kurum
This study was supported by The Scientific and Technological Research Council of Türkiye (TUBITAK Grant No: 2241 / 1139B411701184)
Proje Numarası
2241 / 1139B411701184
Etik Beyan
The authors declare that this manuscript is original, has not been published before, and is not currently being considered for publication elsewhere.No conflict of interest has been declared by the authors.
Kaynakça
- Akpinar S., and Tıkız S., (2019), Çeşitli Bor Oksit Katkılarının Kordiyerit Seramiklerin Sinterleme Davranışına ve Elektriksel Özelliklerine Etkilerinin Araştırılması, AKÜ FEMÜBİD 19, Özel Sayı (62-70). Erişim adresi: https://fenbildergi.aku.edu.tr/wp-content/uploads/2019/10/10-BO101_son.pdf
- Buchanan, R.C. (Ed.) (2004), Ceramic Materials for Electronics, 3rd ed.; Dekker: New York, NY, USA; Basel, Switzerland, revised expanded; ISBN 9780824740283. Erişim adresi: https://books.google.com.tr
- Camerucci, M.A., Cavalieri, A.L. and Moreno, R., (1998), Slip Casting Of Cordierite And Cordierite-Mullite Materials, Journal of the European Ceramic Society, Volume 18, Issue 14, 2149-2157 DOI: https://doi.org/10.1016/S0955-2219(98)00108-3
- Cameruccia M.A., Urretavizcaya G., Cavalieri A.L., (2003) Sintering of cordierite based materials, Ceramics International 29 159–168. DOI: https://doi.org/10.1016/S0272-8842(02)00100-1
- Chen Z, Xu Z, Cui F, Zhang J, Sun X, Shang Y, Guoa R, Liua N, Caia S, Zheng C, (2022), Direct ink writing of cordierite ceramics with low thermal expansion coefficient, Journal of the European Ceramic Society 42,1685–1693 DOI: 10.1016/j.jeurceramsoc.2021.12.017
- Çelik, O.C., 2008, Kordiyerit+Müllit, Kordiyerit+Anartit, Kordiyerit+Anortit+Müllit Kompozit Refrakterlerinin Mikroyapısal İncelenmesi, Gebze İleri Teknoloji Enstitüsü, Yüksek Lisans Tezi. Erişim adresi:https://tez.yok.gov.tr/UlusalTezMerkezi/tezDetay.jsp?id=rSK1QnQJi4gVsTIILGF9EQ&no=COs5DPr434ZVHiJfubUx2A
- Demirci Y., and Günay E., (2011), Crystallization behavior and properties of cordierite glass-ceramics with added boron oxide, Journal of Ceramic Processing Research. Vol. 12, No. 3, pp. 352~356. Erişim adresi: http://pdf.hanrimwon.com/journal.aspx?journal_code=JCPR&journal_vol=012&journal_issue=03&pdf_file=25.352-356_2010-177.pdf&kinds=JOU
- Gören R., Özgür C., Göçmez H., (2006), The preparation of cordierite from talc, fly ash, fused silica and alumina mixture, Ceramics International, 32, 53–56. DOI:https://doi.org/10.1016/j.ceramint.2005.01.001
- Guo Y., Ge Y., Liu W., Zhao J., Zhang J., Wang S., (2024) Reactive-Sintered Low-Thermal-Expansion Cordierite Ceramic with High Stiffness, J. Ceram. Sci. Technol., 15 [2] 69-78 DOI: 10.4416/JCST2024-00003
- Naskar M. K., Chatterjee M., (2004), A novel process for the synthesis of cordierite (Mg2Al4Si5O18) powders from rice husk ash and other sources of silica and their comparative study, Journal of the European Ceramic Society, 24, 3499–3508. DOI: https://doi.org/10.1016/j.jeurceramsoc.2003.11.029