In this study, the residual stresses in the forming of the seed capsule which used in manifacturing the ferforje was carried out. These residual stresses were made up in the process which bars with 8 mm diameter were converted to 6 x 6 mm2 square profiles. This process was actually a Rolling process performed at three levels. Plastic constant and strain hardening parameter were calculated at each level . Then, elasto-plastic stress analysis of the bar subjected to bending was analzed by means of Newton Cotes formulation. The load value that cause residual stresses on the steel bar was assumed to be constant in elasto-plastic analysis. Elastic, plastic and residual stresses under the load value were determined in each level and results were presented in the graphical format.
Anahtar Kelimeler
Öz
Bu çalışmada, ferforje yapımında kullanılan çelik kozanın imalatı esnasında ortaya çıkan artık gerilmeler hesaplanmıştır. Bu artık gerilmeler, çelik kozanın imalatında kullanılan 8 mm çaplı dairesel çubukların, 6 x 6 mm2'lik kare profil kesitli çubuklara dönüştürülmesi işleminde ortaya çıkmaktadır. Bu dönüştürme, gerçekte üç kademeli haddeleme işlemidir. Her kademede malzemenin plastik deformasyon sabiti ve sertleşme üsteli hesaplanmıştır. Daha sonra eğmeye maruz bırakılan çubukların elasto-plastik gerilme analizi, Newton-Cotes formülasyonu kullanılarak analitik olarak yapılmıştır. Bu çalışmada, çelik çubuk üzerinde artık gerilmeyi oluşturan yük değeri sabit tutulmuş ve bu yük değerine karşılık gelen elastik, plastik ve artık gerilme değerleri tesbit edilmiş ve sonuçlar grafikler halinde verilmiştir.
Anahtar Kelimeler
Ayrıntılar
| Birincil Dil | Türkçe |
|---|---|
| Bölüm | Makale |
| Yazarlar | |
| Yayımlanma Tarihi | 1 Ocak 2007 |
| Yayımlandığı Sayı | Yıl 2007 Cilt: 13 Sayı: 1 |