Evaluation of the Color Stability of Contemporary Resin Composites Polymerized with LED Curing Unit Used in Different Modes

Yıl 2024, , 157 - 161, 19.08.2024

Özge Gizem Yenidünya , Başak Yazkan , Nilgün Akgül , Mehmet Alperen Şahin

https://doi.org/10.15311/selcukdentj.1370105

Öz

Aim: To compare the color changes of current bulk-fill composites polymerized with different modes immersed in coffee solution with a conventional resin composite.
Materials and Method: 120 disc-shaped specimens were prepared, 40 specimens from each of three different restorative materials [GrandioSO (GSO), GrandioSO x-tra (GSX), VisCalor bulk (VCB)], using 8-mm diameter and 4-mm thickness molds. Each composite group was polymerized by applying the high power (1200 mW/cm2) and turbo (2100 mW/cm2) modes of the LED curing unit for the times specified in the instructions (n=20). Each group was divided into two subgroups to be immersed into beverages (coffee, and distilled water) (n=10). The color change values [CIEDE2000 (ΔE00)] were calculated at the end of the 1st, 7th, and 30th days. Three-way ANOVA and multiple comparison tests with Tukey HSD at a significance level of p<0.05 were performed for the comparisons of ΔE00 values.
Results: When the ΔE00-t3 values are examined, the samples of GSX composite polymerized with turbo mode and stored in coffee indicated the highest statistically significant values (17.45 ± 0.95), while the lowest values were recorded in the samples stored in distilled water of all tested composite*polymerization mode groups.
Conclusion: The highest color stability after 30 days of storage was observed in the conventional composite group, regardless of polymerization mode, compared to the bulk-fill composites tested. It can be said that the preheating procedure can improve the color stability of bulk-fill composites.
Keywords: color stability; preheating; polymerization mode.

Anahtar Kelimeler

color stability, polymerization mode, preheating

Farklı Modlarda Kullanılan LED Işık Cihazı ile Polimerize Edilen Güncel Rezin Kompozitlerin Renk Stabilitesinin Değerlendirilmesi

Öz

Amaç: Bu çalışmada, farklı modlar ile polimerize edilen güncel bulk-fill kompozitlerin, kahve solüsyonunda bekletilmesi ile meydana gelen renk değişimlerinin geleneksel bir rezin kompozit ile CIEDE2000 formülasyonu kullanılarak karşılaştırmalı olarak incelenmesi amaçlanmıştır.
Gereç ve Yöntem: Üç farklı restoratif materyalin [GrandioSO (GSO), GrandioSO x-tra (GSX), VisCalor bulk (VCB)] her birinden 40 örnek olmak üzere, 8×4 mm kalıplar kullanılarak 120 adet disk şeklinde örnek hazırlandı. Her bir kompozit grubu LED ışık kaynağının yüksek güç (1200 mW/cm2) ve turbo (2100 mW/cm2) modları talimatlarda belirtilen sürelerce uygulanarak polimerize edildi (n=20). Ardından her bir grup, iki farklı içecekte (kahve ve distile su) bekletilmek üzere alt gruplara ayrıldı (n=10). Renk değişim değerleri [CIEDE2000 (ΔE00)] 1., 7. ve 30. günlerin sonunda hesaplandı. ΔE00 değerlerinin karşılaştırılmasında p<0,05 anlamlılık düzeyinde üç yönlü varyans analizi ve çoklu karşılaştırmalar için Tukey HSD testi kullanıldı.
Bulgular: ΔE00-t3 değerleri incelendiğinde, turbo mod ile polimerize edilen GSX kompozitin kahvede bekletilen numuneleri istatistiksel olarak anlamlı en yüksek ortalama değeri (17.45 ± 0.95) verirken, en düşük değerler test edilen tüm kompozit*polimerizasyon modu gruplarının distile suda bekletilen numunelerinde kaydedilmiştir.
Sonuçlar: 30 günlük bekletme sonrası en iyi renk stabilitesi, test edilen bulk-fill kompozitlere kıyasla polimerizasyon modu fark etmeksizin geleneksel kompozit grubunda izlenmiştir. Ön ısıtma prosedürünün bulk-fill kompozitlerin renk stabilitesini iyileştirebileceği söylenebilir.
Anahtar kelimeler: ön ısıtma; polimerizasyon modu; renk stabilitesi.

Anahtar Kelimeler

ön ısıtma, polimerizasyon modu, renk stabilitesi

Etik Beyan

Bu çalışma hayvanlar üzerinde yapılmamıştır ve herhangi bir insan unsuru taşımamaktadır.

Kaynakça

• 1. Sulaiman TA, Suliman AA, Mohamed EA, Rodgers B, Altak A, Johnston WM. Optical properties of bisacryl‐, composite‐, ceramic‐resin restorative materials: An aging simulation study. J Esthet Restor Dent 2021; 33(6): 913-918.
• 2. Alberton Da Silva V, Alberton Da Silva S, Pecho OE, Bacchi A. Influence of composite type and light irradiance on color stability after immersion in different beverages. J Esthet Restor Dent 2018; 30(5): 390-396.
• 3. Ardu S, Duc O, Di Bella E, Krejci I, Daher R. Color stability of different composite resins after polishing. Odontology 2018; 106(3): 328-333.
• 4. Guler S, Unal M. The evaluation of color and surface roughness changes in resin based restorative materials with different contents after waiting in various liquids: An SEM and AFM study. Microsc Res Tech 2018; 81(12): 1422-1433.
• 5. Llena C, Fernández S, Forner L. Color stability of nanohybrid resin-based composites, ormocers and compomers. Clin Oral Investig 2017; 21(4): 1071-1077.
• 6. Ribeiro JS, Peralta SL, Salgado VE, Lund RG. In situ evaluation of color stability and hardness' decrease of resin‐based composites. J Esthet Restor Dent 2017; 29(5): 356-361.
• 7. Eldwakhly E, Ahmed DRM, Soliman M, Abbas MM, Badrawy W. Color and translucency stability of novel restorative CAD/CAM materials. Dent Med Probl 2019; 56(4): 349-356.
• 8. Colombo M, Gallo S, Poggio C, Ricaldone V, Arciola CR, Andrea S. New resin-based bulk-fill composites: In vitro evaluation of micro-hardness and depth of cure as infection risk indexes. Materials 2020; 13(6), 1308.
• 9. Bilgili Can D, Özarslan M. Evaluation of color stability and microhardness of contemporary bulk‐fill composite resins with different polymerization properties. J Esthet Restor Dent 2022; 1-9.
• 10. Lopes LCP, Terada RSS, Tsuzuki FM, Giannini M, Hirata R. Heating and preheating of dental restorative materials-a systematic review. Clin Oral Investig 2020; 24(12): 4225-4235.
• 11. Yang J, Silikas N, Watts DC. Pre-heating time and exposure duration: Effects on post-irradiation properties of a thermo-viscous resin-composite. Dent Mater 2020; 36(6): 787-793.
• 12. Deb S, Di Silvio L, Mackler HE, Millar BJ. Pre-warming of dental composites. Dent Mater 2011; 27(4): e51-59.
• 13. Al-Zain AO, Eckert GJ, Platt JA. The influence of distance on radiant exposure and degree of conversion using different light-emitting-diode curing units. Oper Dent 2019; 44(3): E133-E144.
• 14. Gan JK, Yap AU, Cheong JW, Arista N, Tan CBK. Bulk-fill composites: effectiveness of cure with poly-and monowave curing lights and modes. Oper Dent 2018; 43(2): 136-143.
• 15. Sharma G, Wu W, Dalal EN. The CIEDE2000 color‐difference formula: Implementation notes, supplementary test data, and mathematical observations. Color Res Appl 2005; 30(1): 21-30.
• 16. Piccoli YB, Lima VP, Basso GR, Salgado VE, Lima GS, Moraes R. Optical stability of high-translucency resin-based composites. Oper Dent 2019; 44(5): 536-544.
• 17. Gasparik C, Culic B, Varvara MA, Grecu A, Burde A, Dudea D. Effect of accelerated staining and bleaching on chairside CAD/CAM materials with high and low translucency. Dent Mater J 2019; 38(6): 987-993.
• 18. Paravina RD, Ghinea R, Herrera LJ, Della Bona A, Igiel C, Linninger M, et al. Color difference thresholds in dentistry. J Esthet Restor Dent 2015; 27: S1-S9.
• 19. Torso VH, Fraga MAA, Lopes RM, Aranha ACC, Correr‐Sobrinho L, Correr AB. Charcoal‐based dentifrices: Effect on color stability and surface wear of resin composites. J Esthet Restor Dent 2021; 33(5), 815-823.
• 20. Ozkanoglu S, Akin EG. (2020). Evaluation of the effect of various beverages on the color stability and microhardness of restorative materials. Niger J Clin Pract 2020; 23(3): 322-322.
• 21. Aydin N, Karaoğlanoğlu S, Oktay EA, Kiliçarslan MA. Investigating the color changes on resin‐based CAD/CAM Blocks. J Esthet Restor Dent 2020; 32(2): 251-6.
• 22. Backes CN, França FMG, Turssi CP, do Amaral FLB, Basting RT. Color stability of a bulk-fill composite resin light-cured at different distances. Braz Oral Res 2020; 34: e119.
• 23. Ertas E, Guler AU, Yucel AC, Koprulu H, Guler E. Color stability of resin composites after immersion in different drinks. Dent Mater J 2006; 25(2): 371-376.
• 24. Lee EH, Ahn JS, Lim YJ, Kwon HB, Kim MJ. Effect of post-curing time on the color stability and related properties of a tooth-colored 3D-printed resin material. J Mech Behav Biomed Mater 2022; 126: 104993.
• 25. Arocha MA, Mayoral JR, Lefever D, Mercade M, Basilio J, Roig M . Color stability of siloranes versus methacrylate-based composites after immersion in staining solutions. Clin Oral Investig 2013; 17(6): 1481-1487.
• 26. Erdemir U, Yıldız E, Eren MM. Effects of sports drinks on color stability of nanofilled and microhybrid composites after long-term immersion. J Dent 2012; 40: e55-e63.
• 27. Shamszadeh S, Sheikh-Al-Eslamian SM, Hasani E, Abrandabadi AN, Panahandeh N. Color stability of the bulk-fill composite resins with different thickness in response to coffee/water immersion. Int J Dent 2016; 2016: 7186140.
• 28. Sulaiman TA, Rodgers B, Suliman AA, Johnston WM. Color and translucency stability of contemporary resin‐based restorative materials. J Esthet Restor Dent 2021; 33(6): 899-905.
• 29. Hotta M, Murase Y, Shimizu S, Kusakabe S, Takagaki T, Nikaido T. Color changes in bulk-fill resin composites as a result of visible light-curing. Dent Mater J 2022; 41(1): 11-16.
• 30. Strazzi-Sahyon HB, Passos Rocha E, Gonçalves Assunção W, Henrique dos Santos P. Influence of Light-Curing Intensity on Color Stability and Microhardness of Composite Resins. Int J Periodontics Restor Dent 2020; 40(1): 129-134.
• 31. Domingos PADS, Garcia PPNS, Oliveira ALBMD, Palma-Dibb RG. Composite resin color stability: influence of light sources and immersion media. J Appl Oral Sci 2011; 19(3): 204-211.