Çeşitli içeceklere maruz bırakılan kompozit rezinlerin ağartıcı diş macunu ile fırçalandıkdan

Yıl 2013, Cilt: 23 Sayı: 3, 331 - 336, 01.03.2013

Dt. Hanife Kamak Dt. Fehime Alkan Dt. Tufan Can Okay Prof. Dr. Hülya Erten

Öz

Aim: The aim of this study was the microroughness evaluation of composite resin samples which are exposed to various types of drinks after brushing with whitening toothpaste. Material and Method: As acidic drinks coke, orange juice, sport drink, green tea, apple tea, green tea + lemon tea; as resin restorative materials Tetric, Premise and Filtek Z – 250; as whitening toothpaste Plus White were used during the study. 28 samples were prepared as 5 mm in diameter and 2 mm in thickness from every material. For three composite resin groups; we had 84 samples, totally. Every sample was immersed within the asidic drinks at room temperature for 3h/ day during 1 week. The control group samples were stored at % 0,9 isotonic sodium chloride without subjecting to any cycling. This process was repeated for 7 days, by renewing the used asidic drinks every day. The samples were brushed every day with brushing machine, after removing asidic drinks. After the samples were dried at the end of 7 days, surface roughness was measured by using (Surftest 211.Mitutoyo, Japan) profilometer equipment. Results: When surface roughness values of all materials has been examined, no significant difference has been actuarially observed among the roughness values of the composite samples kept into 0.9% isotonic sodium chloride (p>0.05); whereas, it has been determined that sports drink significantly causes more roughness than the other drinks in composite resin samples (p<0.05). It has been determined that, actuarially, Premise samples kept into sports drink are significantly more rough than Tetric and Filtek Z-250 (p<0.05). Conclusion: After being subjected to acidic beverages brushing with whitening toothpastes, composite resin samples were observed to cause microroughness.

Anahtar Kelimeler

Surface roughness, esthetics restorative materials, acidic drinks, whitening toothpaste

Çeşitli içeceklere maruz bırakılan kompozit rezinlerin ağartıcı diş macunu ile fırçalandıkdan

Öz

Amaç: Bu çalışmanın amacı, çeşitli tipteki içeceklere maruz bırakılan kompozit rezin örneklerinin ağartıcı diş macunu ile fırçalandıktan sonra mikropürüzlülüğünün değerlendirilmesidir. Gereç ve Yöntem: Çalışmada; asitli içecek olarak kola, portakal suyu, sporcu içeceği, yeşil çay, elma çayı, yeşil çay + limon çayı; dolgu materyalleri olarak Tetric, Premise (Dentin) ve Filtek Z – 250; diş macunu olarak Plus White kullanıldı. Her bir materyalden 5 mm çapında ve 2 mm kalınlığında 28 adet örnek hazırlandı. Üç kompozit rezin grubu için toplamda 84 örnek elde edildi. Her bir örnek oda sıcaklığında 24 saatte 3 saat olacak şekilde asidik içecekler içinde bekletildi. Kontrol grubundaki örnekler ise döngüye tabi tutulmaksızın % 0,9 izotonik sodyum klorür içerisinde saklandı. Bu işlem 7 gün boyunca, çalışmada kullanılan asidik içecekler her gün yenilenerek tekrarlandı. Örnekler her gün asidik içecekler içinden çıkartıldıktan sonra fırçalama makinesiyle fırçalandı. 7 gün sonunda örnekler kurutulduktan sonra profilometre (Surftest 211.Mitutoyo, Japonya) cihazı kullanılarak yüzey pürüzlülüğü ölçüldü. Sürekli değişkenler bakımından dağılımların normalliği Shapiro-Wilk testi ile grup varyanslarının homojenliği ise Levene testi ile kontrol edildi. Bulgular: Bütün materyallerin yüzey pürüzlülük değerlerine bakıldığında % 0.9 izotonik sodyum klorür içerisinde bekletilen kompozit rezin örneklerinin pürüzlülük değerleri arasında istatistiksel olarak anlamlı bir farklılık gözlenmezken (p>0.05); sporcu içeceğinin kompozit rezin örneklerinde diğer içeceklere göre anlamlı derecede daha fazla pürüzlülüğe neden olduğu belirlendi (p<0.05). Sporcu içeceğinde bekletilen Premise örneklerinin ise Tetric ve Filtek Z-250 örneklerine göre istatistiksel olarak anlamlı derecede daha fazla pürüzlü olduğu belirlendi (p<0.05). Sonuç: Asitli içeceklere maruz bırakıldıktan sonra ağartıcı özellikteki diş macunu ile fırçalamanın kompozit rezin örneklerinde mikropürüzlülüğe neden olduğu gözlenmiştir.

Anahtar Kelimeler

Yüzey pürüzlülüğü, estetik restoratif materyaller, asitli içecekler, ağartıcı diş macunu

Kaynakça

• Grippo JO, Simring M, Schreiner S. Attrition, abrasion, corrosion and abfraction revisited: a new perspective on tooth surface lesions. J Am Dental Ass 2004; 135: 1109–18.
• Wongkhantee S, Patanapiradej V, Maneenut C, Tantbirojn D. Effect of acidic food and drinks on surface hardness of enamel, dentine, and toothcoloured filling materials. J Dent 2006; 34: 214Lussy A, Jaeggi T, Jaeggi-Scharer S. Prediction of the erosive potential of some beverages. Caries Res 1995; 29: 349-54.
• Zero DT. Etiology of dental erosion - extrinsic factors. Eur J Oral Sci 1996;104:162-77.
• Edwards M, Creanor SL, Foye RH, Gilmour WH. Buffering capacities of soft drinks: the potential influence on dental erosion. J Oral Rehabil 1999; 26: 923-27.
• Beiraghi S, Atkins S, Rosen S, Wilson S, Odom J, Beck M. Effect of calcium lactate in erosion and S. mutans in rats when added to Coca-Cola. Pediatr Dent 1989; 11: 312-5.
• Geurtsen W., Leyhausen G. and Garcia Godoy F.: Effect of storage media on the fluoride release and surface microhardness of four polyacid-modified composite resins (“compomers”). Dent Mater 1999; 15: 196-201.
• Wu W. and Mc Kinney J.E.: Influence of chemicals on wear of dental composites. J Dent Res 1982; 61: 1180-3.
• Vieira A, Lugtenborg M, Ruben JL, Huysmans MC. Brushing abrasion of eroded bovine enamel pretreated with topical fluorides. Caries Res. 2006; 40: 224-30.
• Nomoto R, McCabe JF. A simple acid erosion test for dental water-based cements. Dent Mater 2001; 17: 53–9.
• Czarnecka B, Limanowska-Shaw H, Nicholson JW. Buffering and ion-release by a glass-ionomer cement under near-neutral and acidic conditions. Biomaterials 2002; 23: 2783–8.
• Mante MO, Saleh N, Tanna NK, Mante FK. Softening patterns of light cured glass ionomer cements. Dent Mater 1999;15:303–9.
• Lussi A, Jaeggi T, Zero D. The role of diet in the aetiology of dental erosion. Caries Res 2004; 38: 34–
• McKenzie MA, Linden RWA, Nicholson JW. The physical properties of conventional and resinmodified glass-ionomer dental cements stored in saliva, proprietary acidic beverages, saline and water. Biomaterials 2003;24:4063–9.
• Dodds M, Peggy P, Rodriguez D. The effect of some Mexican citric acid snacks on vitro tooth enamel erosion. Pediatr Dent 1997;19:339-40.
• Maupome G, Diez de Bonilla J, Torres-Villasenor G, Andrade- Delgado LC, Castaño VM. In vitro quantitative assessment of enamel microhardness after exposure to eroding immersion in cola drink. Caries Res 1998;32:148-53.
• West NX, Hughes JA, Addy M. Erosion of dentine and enamel in vitro by dietary acids: the effect of temperature, acid character, concentration and exposure time. J Oral Rehabil 2000;27:875-80.
• Barbour ME, Finke M, Parker DM, Hughes JA, Allen GC, Addy M. The relationship between softening and erosion caused by soft drinks at a range of temperatures. J Dent 2006;34:207-13.
• Goldstein G.R. and Lerner T.: The effect of toothbrushing on a hybrid composite resin. J Prosthet Dent 1991;66: 498-500.
• Zero D.T.: Etiology of dental erosion-extrinsic factors, Eur J Oral Sci 1996;104: 162-77.
• Wictorin L.: Effect of toothbrushing on acrylic resin veneering material. Acta Odontol Scand 1972;30: 383-3
• Hallgren A., Oliveby A. and Twetman S.: Caries associated microflora in plaque from orthodontic appliances retained with glass ionomer cement. Scand J Dent Res 1992;100: 140- 3.
• Toledano M., De La Torre F.J. and Osorio R.: Evaluation of two polishing methods for resin composites, Am J Dent 1994;7:328-30.
• Shintani H., Satou J., Satou N., Hatashihara H. and Inoue T.: Effects of various finishing methods on staining and accumulation of Streptococcus mutans HS-6 on composite resins, Dent Mater 1985;1: 225-7.
• Özel E, Gökçe K. Spor İçecekleri ve Dental Erozyon. Atatürk Üniv Diş Hek Fak Derg 2006; 16: 14Sarı ME, Koyutürk AE, Çankaya S. Günlük Tüketilen Yiyecek ve içeceklerin Mine ve Dolgu Materyallerinin Yüzey Sertliği Ve Pürüzlülüğüne Etkisi. Atatürk Üniv. Dis Hek. Fak. 2010;20(3):1531
• Attin T., Buchalla W., Trett A. and Hellwig E.: Toothbrushing abrasion of polyacidmodified composites in neutral and acidic buffer solutions, J Prosthet Dent 1988;80:148-50.
• Min JH, Kwon HK, Kim BI. The addition of nanosized hydroxyapatite to a sports drink to inhibit dental erosion: in vitro study using bovine enamel. J Dent. 2011; 39:629-35.
• Tanoue N., Matsumura H., Atsuta M. Wear and surface roughness of current prosthetic composites after toothbrush/dentifrice abrasion. J Prosthet Dent 2000; 84: 93- 97.
• Johnson WW, Dhuru VB, Brantley WA. Composite microfiller content and its effect on fracture toughness and diamaterial tensile strength. Dent Mater 1993; 9: 95- 8.
• Önal B. Restoratif diş hekimliğinde maddeler ve uygulamaları, Bornova- İzmir, 2004, 4-9, 66-98.
• Summit JB, Robbins JW, Hilton TJ, Schwartz RS. Fundamentalis of Operative Dentistry A Contemporary Approach 2006; 1: 289-339. Yazışma Adresi: Dt. Hanife KAMAK Gazi Üniversitesi
• Diş Hekimliği Fakültesi Diş Hastalıkları ve Tedavisi ABD Tel: [phone]
• Email: [e-mail]