In this study, Nickel-Chrome-Molybdenum alloy is manufactured using investment casting method with centrifugal casting device from a polyurethane foam model in a regular and open-pore form, as a hard tissue implant. The samples produced have 10, 20, and 30 (±3) pores per inch and 0.0008, 0.0017, and 0.0027 g/mm3 densities, respectively.
Young’s modulus, hardness and mechanical behaviors of the samples were investigated by SEM, EDS and compressive test.
As a result, it is seen that the pore size and the pore wire diameter of the samples could be controlled thus compression strength and young modulus. In this way it was understood that an implant material could be produced with similar mechanical properties to the human bone.
Metal foams Biomaterials İnvestment Casting Nickel-Chrome-Molybdenum Mechanical Properties
The Scientific Research Foundation, Firat University
1018
The authors acknowledge the Scientific Research Foundation, Firat University (FUBAP—Project no. 1018) for their financial support.
Birincil Dil | İngilizce |
---|---|
Konular | Malzeme Üretim Teknolojileri |
Bölüm | Araştırma Makalesi |
Yazarlar | |
Proje Numarası | 1018 |
Yayımlanma Tarihi | 30 Aralık 2021 |
Yayımlandığı Sayı | Yıl 2021 Cilt: 11 Sayı: 2 |
All articles published by EJT are licensed under the Creative Commons Attribution 4.0 International License. This permits anyone to copy, redistribute, remix, transmit and adapt the work provided the original work and source is appropriately cited.