Optimizing A5356 Alloy Performance with WAAM: A Comprehensive Study

Yıl 2026, Cilt: 29 Sayı: 4 , 1 - 11 , 21.04.2026

Berfin Gürsu , Merve Sude Kayış , Hakan Ateş , Murat Kayaalp

https://doi.org/10.2339/politeknik.1634054
https://izlik.org/JA99UE94RN

Öz

Wire Arc Additive Manufacturing (WAAM) technology is an attractive fabrication method for structural components due to significantly lower consumable usage and higher filler material addition rates than conventional fusion welding. The present study used 1.2 mm welding wire, WAAM CMT-MIG technique, three different wire feed speeds (WFS), and corresponding heat input levels to produce high layer thicknesses. Samples extracted from the fabricated walls were subjected to non-destructive testing methods, including visual inspection (VT), penetrant testing (PT), and ultrasonic testing (UT), as well as various mechanical and material characterization tests such as tensile, flexure, and notch impact tests, microhardness measurements, XRD analysis, and microstructural evaluations using optical microscopy, SEM, and EDS. The results revealed that bending strength and microhardness improved under low heat input conditions. Moreover, these findings indicate that the WAAM technique holds promise as a manufacturing method for A5356 samples when lower heat input is applied.

Anahtar Kelimeler

WAAM MIG-CMT Heat input A5356

Destekleyen Kurum

TÜBİTAK

Teşekkür

The authors would like to thank the TUBITAK 2209-B project support code 1139B412302655. Thank you for the opportunity to present our paper at the ICMATSE Hybrid Conference.

Kaynakça

  • [1] Tekeli A. F. ve Seçkin B., “Tel Beslemeli Ark Eklemeli İmalat Yönteminde Soğuk Metal Transferi Teknolojisinin Kullanımı”, Mühendis ve Makine Dergisi, 44: 26-30, (2020).
  • [2] Ayan Y., “Farklı Malzeme Katmanlı Ürünlerin Tel Ark Eklemeli İmalatı”, Karabük University Institute of Graduate Studies, Ph.D. Thesis, 1-25, (2022).
  • [3] Çakır E. ve Ulutan M., “Tel Ark Katmanlı İmalat (TAKİ) Yöntemi ve Farklı Malzemelerde Mekanik Özelliklerinin İncelenmesi”, Bilecik Şeyh Edebali University Fen Bilimleri Dergisi, 10: 217-235, (2023).
  • [4] Kayacan M. Y. ve Yılmaz N., “DMLS eklemeli imalatta süreç ve maliyet modeli geliştirilmesi”, Politeknik Dergisi, 22(3): 763-770, (2019).
  • [5] Karakılınç U., Yalçın B. ve Ergene B., “Toz yataklı/beslemeli eklemeli imalatta kullanılan partiküllerin uygunluk araştırması ve partikül imalat yöntemleri”, Politeknik Dergisi, 22(4): 801-810, (2019).
  • [6] Polat Çoban N., Anaç N. ve Mert F., “Eklemeli imalat ile üretilen PLA parçaların yapıştırılmasında yapıştırma parametrelerinin mekanik dayanımına etkisinin incelenmesi”, Politeknik Dergisi, 26(3): 1145-1154, (2023).
  • [7] Raut L. P. ve Taiwade R. V., “Wire Arc Additive Manufacturing: A Comprehensive Review and Research Directions”, Journal of Materials Engineering and Performance, 30: 4768-4791, (2021).
  • [8] Saleh B., Fathi R., Tian Y. ve diğerleri, “Fundamentals and advances of wire arc additive manufacturing: materials, process parameters, potential applications, and future trends”, Archives of Civil and Mechanical Engineering, 23: 96, (2023).
  • [9] Zhang Y., Wang L. ve Liu H., “Automated Determination of Grain Features for Wire Arc Additive Manufacturing Process”, Journal of Materials Engineering and Performance, 32(5): 1234-1245, (2023).
  • [10] Köhler M., Hensel J. ve Dilger K., “Effects of Thermal Cycling on Wire and Arc Additive Manufacturing of Al-5356 Components”, Metals, 10: 952-963, (2020).
  • [11] Özsoy K. ve Duman B., “Eklemeli İmalat (3 Boyutlu Baskı) Teknolojilerinin Eğitimde Kullanılabilirliği”, International Journal of 3D Printing Technologies and Digital Industry, 1: 36-48, (2017).
  • [12] Karayel E., Bozkurt Y., Özdemir C. ve Kalender M., “Investigation of Mechanical Properties of Aluminum Alloys Produced by Wire Arc Additive Manufacturing Method”, Marmara University Institute of Natural and Applied Sciences, Master’s Thesis, 3-67, (2022).
  • [13] Mercan E., Ayan Y. ve Kahraman N., “Gazaltı metal ark kaynak (GMAK) yöntemiyle birleştirilen AA5754 ve AA6013 alüminyum alaşımlarının mikro yapı ve mekanik özellikleri”, Pamukkale University Mühendislik Bilimleri Dergisi, 26: 82-87, (2020).
  • [14] Ayan D. ve Nizamettin K., “Metal Eklemeli İmalat: Tel Ark Yöntemi ve Uygulamaları”, International Journal of 3D Printing Technologies and Digital Industry, 2: 74-84, (2018).
  • [15] Özsolak O., “Eklemeli İmalat Yöntemleri ve Kullanılan Malzemeler”, International Journal of Innovative Engineering Applications, 3(1): 9-14, (2019).
  • [16] Evrensel R. ve Ertek C., “Eklemeli İmalatta Alüminyum ve Alüminyum Alaşımlarının Uygulamaları ve Topoloji Optimizasyonu”, Journal of the Institute of Science and Technology, 13: 2008-2025, (2023).
  • [17] Gierth M., Henckell P., Ali Y., Scholl J. ve Bergmann J. P., “Wire Arc Additive Manufacturing (WAAM) of Aluminum Alloy AlMg5Mn with Energy-Reduced Gas Metal Arc Welding (GMAW)”, Materials, 13: 2671-2693, (2020).
  • [18] Nagasai B. P., Malarvizhi S. ve Balasubramanian V., “Wire Arc Additive Manufacturing of 5356 Aluminum Alloy Cylindrical Component: Mechanical Properties and Microstructural Characteristics”, Weld Fab Tech Times, (2023).
  • [19] Wang J., Feng J. C. ve Wang Y. X., “Microstructure of Al–Mg dissimilar weld made by cold metal transfer MIG welding”, Materials Science and Technology, 24(7): 827-831, (2008).
  • [20] Sachin Kumar, Gurraj Singh, Vishal S. Sharma ve diğerleri, “Investigation of Process Parameters for Quality Deposition of AL5356 using Cold Metal Transfer Wire Arc Additive Manufacturing (CMT-WAAM)”, Research Square, Preprint, (2024).
  • [21] Wang J., Shen Q., Kong X. ve Chen X., “Arc Additively Manufactured 5356 Aluminum Alloy with Cable-Type Welding Wire: Microstructure and Mechanical Properties”, Journal of Materials Engineering and Performance, 1-7, (2021).
  • [22] Wang J., Zhu K., Zhang W., Zhu X. ve Lu X., “Microstructural and defect evolution during WAAM resulting in mechanical property differences for AA5356 component”, Journal of Materials Research and Technology, 22: 982-996, (2023).
  • [23] Jiangang P., Bo Y., Jinguo G., Yu R., Hongjun C., Liang Z. ve Hao L., “Influence of arc mode on the microstructure and mechanical properties of 5356 aluminum alloy fabricated by wire arc additive manufacturing”, Journal of Materials Research and Technology, 20: 1893-1907, (2022).
  • [24] Langelandsvik G., Akselsen O. M., Furu T. ve Roven H. J., “Review of Aluminum Alloy Development for Wire Arc Additive Manufacturing”, Materials, 14: 5370, (2021).
  • [25] Li S., Zhang L. J., Ning J., Wang X., Zhang G. F., Zhang J. X., Na S. J. ve Fatemeh B., “Comparative study on the microstructures and properties of wire+ arc additively manufactured 5356 aluminum alloy with argon and nitrogen as the shielding gas”, Additive Manufacturing, 34: 101206, (2020).
  • [26] Li S., Zhang L. J., Ning J., Wang X., Zhang G. F., Zhang J. X. ve Na S. J., “Microstructures and mechanical properties of Al–Zn–Mg aluminum alloy samples produced by wire+ arc additive manufacturing”, Journal of Materials Research and Technology, 9: 13770-13780, (2020).
  • [27] Koduru J. P., Kumar T. V. ve Mantrala K. M., “A review of wire and arc additive manufacturing using different property characterization, challenges and future trends”, International Journal of System Assurance Engineering and Management, 15: 4563-4581, (2024).
  • [28] Zahid M., Hai K., Khan M., Shekha A., Pervaiz S., Moneeb Ali S., Abdul-Latif O. ve Salman M., “Wire Arc Additive Manufacturing (WAAM): Reviewing Technology, Mechanical Properties, Applications and Challenges”, ASME International Mechanical Engineering Congress and Exposition, Proceedings, 2A: V02AT02A042, (2020).
  • [29] Wieczorowski M., Pereira A., Carou D., Gapinski B. ve Ramírez I., “Characterization of 5356 Aluminum Walls Produced by Wire Arc Additive Manufacturing (WAAM)”, Materials, 16(7): 2570, (2023).
  • [30] GEKA - Gedik Kaynak, “AlMg 5 [Technical data sheet]”, www.gedikkaynak.com.tr, (t.y.).
  • [31] Karimi J., Bohlen A., Kamboj N. ve diğerleri, “Automated Determination of Grain Features for Wire Arc Additive Manufacturing”, Journal of Materials Engineering and Performance, 32: 10402-10411, (2023).
  • [32] Kayadelen A., Ateş H. ve Yılmaz O., “Wire Arc Additive Manufacturing (Metal Inert Gas-Cold Metal Transfer) of ER70S-6: Experimental and Computational Analysis on Process, Microstructure, and Mechanical Property Relationships”, Journal of Materials Engineering and Performance, (2025).
  • [33] Goldstein J., Newbury D., Joy D., Lyman C., Echlin P., Lifshin E., Sawyer L. ve Michael J., “Scanning Electron Microscopy and X-Ray Microanalysis”, Springer, (2018).
  • [34] Zuo X., Lv Z., Wang Y., Chen X. ve Qi W., “Microstructural Organization and Mechanical Properties of 5356 Aluminum Alloy Wire Arc Additive Manufacturing Under Low Heat Input Conditions”, Metals, 15(2): 116, (2025).
  • [35] Li J., Wang X. ve Zhao Y., “Wire and Arc Additive Manufacturing of High-Strength Al–Zn–Mg Alloy: Microstructure and Mechanical Properties”, Frontiers in Materials, 7: 656429, (2020).
  • [36] Köhler M., Fiebig S., Hensel J. ve Dilger K., “Wire and Arc Additive Manufacturing of Aluminum Components”, Metals, 9(5): 608, (2019).
  • [37] Sharma S. K., Chandra M., Kazmi K. H. ve diğerleri, “Surface Characteristics, Microstructural, and Tribological Behavior of Wire Arc Additive Manufactured Aluminum-5356 Alloy”, Journal of Materials Engineering and Performance, (2024).
  • [38] Liu J., Chen H., Li W. ve diğerleri, “Investigation on the microstructure and mechanical properties of 5356 aluminum alloy wire in continuous casting direct rolling process”, Journal of Materials Science, 59: 20428-20444, (2024).
  • [39] Girgsdies F., “Peak Profile Fitting in XRD”, Electron Microscopy Group, Department of Inorganic Chemistry, Fritz-Haber-Institut der MPG, Berlin, (2015).
  • [40] EN ISO 23277, “Non-destructive testing of welds - Penetrant testing of welds - Acceptance Levels”, ISO, (2015).
  • [41] EN ISO 11666-1, “Non-destructive testing of welds - Ultrasonic testing - Acceptance levels”, ISO, (2015).
  • [42] Wahsh L., Azzam M., Turky M., Salem H., Hamdy F., Mansour A. ve ElShater A., “Parameter Selection for Wire Arc Additive Manufacturing (WAAM) Process”, (2018).
  • [43] Chen F., Yang Y. H. ve Feng H., “Regional Control and Optimization of Heat Input during CMT by Wire Arc Additive Manufacturing: Modeling and Microstructure Effects”, Materials, 14: 1061, (2021).

WAAM ile A5356 Alaşım Performansının Optimize Edilmesi: Kapsamlı Bir Çalışma

Yıl 2026, Cilt: 29 Sayı: 4 , 1 - 11 , 21.04.2026

Berfin Gürsu , Merve Sude Kayış , Hakan Ateş , Murat Kayaalp

https://doi.org/10.2339/politeknik.1634054
https://izlik.org/JA99UE94RN

Öz

Tel Ark Eklemeli Üretim (WAAM) teknolojisi, geleneksel eritme kaynağına kıyasla önemli ölçüde daha düşük sarf kullanımı ve daha yüksek biriktirme oranları nedeniyle yapısal bileşenler için cazip bir üretim yöntemidir. Bu çalışmada, 1,2 mm kaynak teli, WAAM CMT-MIG (Soğuk Metal Transferi - Metal Soy Gaz) yöntemi kullanılarak üç farklı tel besleme hızı (WFS) ve üç farklı ısı girdisi değeri ile yüksek katman kalınlıklarında üretimler yapılmıştır. Üretilen duvarlardan elde edilen numuneler üzerinde görsel muayene (VT), penetrant testi (PT) ve ultrasonik muayene (UT) gibi tahribatsız muayene yöntemleri ve çekme testi, eğme testi, çentik darbe testi, mikrosertlik, XRD, mikroyapı analizleri (optik mikroskop, SEM ve EDS) dahil olmak üzere çeşitli testler gerçekleştirilmiştir. Sonuçlar analiz edilmiş ve düşük ısı girdisinde eğilme mukavemeti ve mikrosertliğin arttığı ortaya çıkmıştır. Ayrıca, bu sonuçlar WAAM yönteminin daha düşük ısı girdisi ile A5356 numuneler için bir üretim yöntemi olarak umut vaat ettiğini göstermektedir.

Anahtar Kelimeler

WAAM MIG-CMT ısı girdisi A5356

Destekleyen Kurum

TÜBİTAK

Teşekkür

Yazarlar, 1139B412302655 kodlu TÜBİTAK 2209-B projesinin desteğine teşekkür eder. ICMATSE Hybrid Konferans'ına makalemizi sunma fırsatı verdikleri için teşekkür ederiz.

Kaynakça

  • [1] Tekeli A. F. ve Seçkin B., “Tel Beslemeli Ark Eklemeli İmalat Yönteminde Soğuk Metal Transferi Teknolojisinin Kullanımı”, Mühendis ve Makine Dergisi, 44: 26-30, (2020).
  • [2] Ayan Y., “Farklı Malzeme Katmanlı Ürünlerin Tel Ark Eklemeli İmalatı”, Karabük University Institute of Graduate Studies, Ph.D. Thesis, 1-25, (2022).
  • [3] Çakır E. ve Ulutan M., “Tel Ark Katmanlı İmalat (TAKİ) Yöntemi ve Farklı Malzemelerde Mekanik Özelliklerinin İncelenmesi”, Bilecik Şeyh Edebali University Fen Bilimleri Dergisi, 10: 217-235, (2023).
  • [4] Kayacan M. Y. ve Yılmaz N., “DMLS eklemeli imalatta süreç ve maliyet modeli geliştirilmesi”, Politeknik Dergisi, 22(3): 763-770, (2019).
  • [5] Karakılınç U., Yalçın B. ve Ergene B., “Toz yataklı/beslemeli eklemeli imalatta kullanılan partiküllerin uygunluk araştırması ve partikül imalat yöntemleri”, Politeknik Dergisi, 22(4): 801-810, (2019).
  • [6] Polat Çoban N., Anaç N. ve Mert F., “Eklemeli imalat ile üretilen PLA parçaların yapıştırılmasında yapıştırma parametrelerinin mekanik dayanımına etkisinin incelenmesi”, Politeknik Dergisi, 26(3): 1145-1154, (2023).
  • [7] Raut L. P. ve Taiwade R. V., “Wire Arc Additive Manufacturing: A Comprehensive Review and Research Directions”, Journal of Materials Engineering and Performance, 30: 4768-4791, (2021).
  • [8] Saleh B., Fathi R., Tian Y. ve diğerleri, “Fundamentals and advances of wire arc additive manufacturing: materials, process parameters, potential applications, and future trends”, Archives of Civil and Mechanical Engineering, 23: 96, (2023).
  • [9] Zhang Y., Wang L. ve Liu H., “Automated Determination of Grain Features for Wire Arc Additive Manufacturing Process”, Journal of Materials Engineering and Performance, 32(5): 1234-1245, (2023).
  • [10] Köhler M., Hensel J. ve Dilger K., “Effects of Thermal Cycling on Wire and Arc Additive Manufacturing of Al-5356 Components”, Metals, 10: 952-963, (2020).
  • [11] Özsoy K. ve Duman B., “Eklemeli İmalat (3 Boyutlu Baskı) Teknolojilerinin Eğitimde Kullanılabilirliği”, International Journal of 3D Printing Technologies and Digital Industry, 1: 36-48, (2017).
  • [12] Karayel E., Bozkurt Y., Özdemir C. ve Kalender M., “Investigation of Mechanical Properties of Aluminum Alloys Produced by Wire Arc Additive Manufacturing Method”, Marmara University Institute of Natural and Applied Sciences, Master’s Thesis, 3-67, (2022).
  • [13] Mercan E., Ayan Y. ve Kahraman N., “Gazaltı metal ark kaynak (GMAK) yöntemiyle birleştirilen AA5754 ve AA6013 alüminyum alaşımlarının mikro yapı ve mekanik özellikleri”, Pamukkale University Mühendislik Bilimleri Dergisi, 26: 82-87, (2020).
  • [14] Ayan D. ve Nizamettin K., “Metal Eklemeli İmalat: Tel Ark Yöntemi ve Uygulamaları”, International Journal of 3D Printing Technologies and Digital Industry, 2: 74-84, (2018).
  • [15] Özsolak O., “Eklemeli İmalat Yöntemleri ve Kullanılan Malzemeler”, International Journal of Innovative Engineering Applications, 3(1): 9-14, (2019).
  • [16] Evrensel R. ve Ertek C., “Eklemeli İmalatta Alüminyum ve Alüminyum Alaşımlarının Uygulamaları ve Topoloji Optimizasyonu”, Journal of the Institute of Science and Technology, 13: 2008-2025, (2023).
  • [17] Gierth M., Henckell P., Ali Y., Scholl J. ve Bergmann J. P., “Wire Arc Additive Manufacturing (WAAM) of Aluminum Alloy AlMg5Mn with Energy-Reduced Gas Metal Arc Welding (GMAW)”, Materials, 13: 2671-2693, (2020).
  • [18] Nagasai B. P., Malarvizhi S. ve Balasubramanian V., “Wire Arc Additive Manufacturing of 5356 Aluminum Alloy Cylindrical Component: Mechanical Properties and Microstructural Characteristics”, Weld Fab Tech Times, (2023).
  • [19] Wang J., Feng J. C. ve Wang Y. X., “Microstructure of Al–Mg dissimilar weld made by cold metal transfer MIG welding”, Materials Science and Technology, 24(7): 827-831, (2008).
  • [20] Sachin Kumar, Gurraj Singh, Vishal S. Sharma ve diğerleri, “Investigation of Process Parameters for Quality Deposition of AL5356 using Cold Metal Transfer Wire Arc Additive Manufacturing (CMT-WAAM)”, Research Square, Preprint, (2024).
  • [21] Wang J., Shen Q., Kong X. ve Chen X., “Arc Additively Manufactured 5356 Aluminum Alloy with Cable-Type Welding Wire: Microstructure and Mechanical Properties”, Journal of Materials Engineering and Performance, 1-7, (2021).
  • [22] Wang J., Zhu K., Zhang W., Zhu X. ve Lu X., “Microstructural and defect evolution during WAAM resulting in mechanical property differences for AA5356 component”, Journal of Materials Research and Technology, 22: 982-996, (2023).
  • [23] Jiangang P., Bo Y., Jinguo G., Yu R., Hongjun C., Liang Z. ve Hao L., “Influence of arc mode on the microstructure and mechanical properties of 5356 aluminum alloy fabricated by wire arc additive manufacturing”, Journal of Materials Research and Technology, 20: 1893-1907, (2022).
  • [24] Langelandsvik G., Akselsen O. M., Furu T. ve Roven H. J., “Review of Aluminum Alloy Development for Wire Arc Additive Manufacturing”, Materials, 14: 5370, (2021).
  • [25] Li S., Zhang L. J., Ning J., Wang X., Zhang G. F., Zhang J. X., Na S. J. ve Fatemeh B., “Comparative study on the microstructures and properties of wire+ arc additively manufactured 5356 aluminum alloy with argon and nitrogen as the shielding gas”, Additive Manufacturing, 34: 101206, (2020).
  • [26] Li S., Zhang L. J., Ning J., Wang X., Zhang G. F., Zhang J. X. ve Na S. J., “Microstructures and mechanical properties of Al–Zn–Mg aluminum alloy samples produced by wire+ arc additive manufacturing”, Journal of Materials Research and Technology, 9: 13770-13780, (2020).
  • [27] Koduru J. P., Kumar T. V. ve Mantrala K. M., “A review of wire and arc additive manufacturing using different property characterization, challenges and future trends”, International Journal of System Assurance Engineering and Management, 15: 4563-4581, (2024).
  • [28] Zahid M., Hai K., Khan M., Shekha A., Pervaiz S., Moneeb Ali S., Abdul-Latif O. ve Salman M., “Wire Arc Additive Manufacturing (WAAM): Reviewing Technology, Mechanical Properties, Applications and Challenges”, ASME International Mechanical Engineering Congress and Exposition, Proceedings, 2A: V02AT02A042, (2020).
  • [29] Wieczorowski M., Pereira A., Carou D., Gapinski B. ve Ramírez I., “Characterization of 5356 Aluminum Walls Produced by Wire Arc Additive Manufacturing (WAAM)”, Materials, 16(7): 2570, (2023).
  • [30] GEKA - Gedik Kaynak, “AlMg 5 [Technical data sheet]”, www.gedikkaynak.com.tr, (t.y.).
  • [31] Karimi J., Bohlen A., Kamboj N. ve diğerleri, “Automated Determination of Grain Features for Wire Arc Additive Manufacturing”, Journal of Materials Engineering and Performance, 32: 10402-10411, (2023).
  • [32] Kayadelen A., Ateş H. ve Yılmaz O., “Wire Arc Additive Manufacturing (Metal Inert Gas-Cold Metal Transfer) of ER70S-6: Experimental and Computational Analysis on Process, Microstructure, and Mechanical Property Relationships”, Journal of Materials Engineering and Performance, (2025).
  • [33] Goldstein J., Newbury D., Joy D., Lyman C., Echlin P., Lifshin E., Sawyer L. ve Michael J., “Scanning Electron Microscopy and X-Ray Microanalysis”, Springer, (2018).
  • [34] Zuo X., Lv Z., Wang Y., Chen X. ve Qi W., “Microstructural Organization and Mechanical Properties of 5356 Aluminum Alloy Wire Arc Additive Manufacturing Under Low Heat Input Conditions”, Metals, 15(2): 116, (2025).
  • [35] Li J., Wang X. ve Zhao Y., “Wire and Arc Additive Manufacturing of High-Strength Al–Zn–Mg Alloy: Microstructure and Mechanical Properties”, Frontiers in Materials, 7: 656429, (2020).
  • [36] Köhler M., Fiebig S., Hensel J. ve Dilger K., “Wire and Arc Additive Manufacturing of Aluminum Components”, Metals, 9(5): 608, (2019).
  • [37] Sharma S. K., Chandra M., Kazmi K. H. ve diğerleri, “Surface Characteristics, Microstructural, and Tribological Behavior of Wire Arc Additive Manufactured Aluminum-5356 Alloy”, Journal of Materials Engineering and Performance, (2024).
  • [38] Liu J., Chen H., Li W. ve diğerleri, “Investigation on the microstructure and mechanical properties of 5356 aluminum alloy wire in continuous casting direct rolling process”, Journal of Materials Science, 59: 20428-20444, (2024).
  • [39] Girgsdies F., “Peak Profile Fitting in XRD”, Electron Microscopy Group, Department of Inorganic Chemistry, Fritz-Haber-Institut der MPG, Berlin, (2015).
  • [40] EN ISO 23277, “Non-destructive testing of welds - Penetrant testing of welds - Acceptance Levels”, ISO, (2015).
  • [41] EN ISO 11666-1, “Non-destructive testing of welds - Ultrasonic testing - Acceptance levels”, ISO, (2015).
  • [42] Wahsh L., Azzam M., Turky M., Salem H., Hamdy F., Mansour A. ve ElShater A., “Parameter Selection for Wire Arc Additive Manufacturing (WAAM) Process”, (2018).
  • [43] Chen F., Yang Y. H. ve Feng H., “Regional Control and Optimization of Heat Input during CMT by Wire Arc Additive Manufacturing: Modeling and Microstructure Effects”, Materials, 14: 1061, (2021).
Toplam 43 adet kaynakça vardır.

Ayrıntılar

Birincil Dil İngilizce
Konular Malzeme Üretim Teknolojileri, Metaller ve Alaşım Malzemeleri , Malzeme Mühendisliği (Diğer)
Bölüm Araştırma Makalesi
Yazarlar

Berfin Gürsu 0009-0005-7894-8672

Merve Sude Kayış 0009-0007-0919-1260

Hakan Ateş 0000-0002-5132-4107

Murat Kayaalp 0009-0001-3655-1619

Gönderilme Tarihi 6 Şubat 2025
Kabul Tarihi 20 Ağustos 2025
Erken Görünüm Tarihi 12 Ekim 2025
Yayımlanma Tarihi 21 Nisan 2026
DOI https://doi.org/10.2339/politeknik.1634054
IZ https://izlik.org/JA99UE94RN
Yayımlandığı Sayı Yıl 2026 Cilt: 29 Sayı: 4

Kaynak Göster

APA Gürsu, B., Kayış, M. S., Ateş, H., & Kayaalp, M. (2026). Optimizing A5356 Alloy Performance with WAAM: A Comprehensive Study. Politeknik Dergisi, 29(4), 1-11. https://doi.org/10.2339/politeknik.1634054
AMA 1.Gürsu B, Kayış MS, Ateş H, Kayaalp M. Optimizing A5356 Alloy Performance with WAAM: A Comprehensive Study. Politeknik Dergisi. 2026;29(4):1-11. doi:10.2339/politeknik.1634054
Chicago Gürsu, Berfin, Merve Sude Kayış, Hakan Ateş, ve Murat Kayaalp. 2026. “Optimizing A5356 Alloy Performance with WAAM: A Comprehensive Study”. Politeknik Dergisi 29 (4): 1-11. https://doi.org/10.2339/politeknik.1634054.
EndNote Gürsu B, Kayış MS, Ateş H, Kayaalp M (01 Nisan 2026) Optimizing A5356 Alloy Performance with WAAM: A Comprehensive Study. Politeknik Dergisi 29 4 1–11.
IEEE [1]B. Gürsu, M. S. Kayış, H. Ateş, ve M. Kayaalp, “Optimizing A5356 Alloy Performance with WAAM: A Comprehensive Study”, Politeknik Dergisi, c. 29, sy 4, ss. 1–11, Nis. 2026, doi: 10.2339/politeknik.1634054.
ISNAD Gürsu, Berfin - Kayış, Merve Sude - Ateş, Hakan - Kayaalp, Murat. “Optimizing A5356 Alloy Performance with WAAM: A Comprehensive Study”. Politeknik Dergisi 29/4 (01 Nisan 2026): 1-11. https://doi.org/10.2339/politeknik.1634054.
JAMA 1.Gürsu B, Kayış MS, Ateş H, Kayaalp M. Optimizing A5356 Alloy Performance with WAAM: A Comprehensive Study. Politeknik Dergisi. 2026;29:1–11.
MLA Gürsu, Berfin, vd. “Optimizing A5356 Alloy Performance with WAAM: A Comprehensive Study”. Politeknik Dergisi, c. 29, sy 4, Nisan 2026, ss. 1-11, doi:10.2339/politeknik.1634054.
Vancouver 1.Berfin Gürsu, Merve Sude Kayış, Hakan Ateş, Murat Kayaalp. Optimizing A5356 Alloy Performance with WAAM: A Comprehensive Study. Politeknik Dergisi. 01 Nisan 2026;29(4):1-11. doi:10.2339/politeknik.1634054

Amaç ve Kapsam

 Temel mühendislik alanlarındaki hem deneysel hem de kuramsal çalışmaların yer aldığı dergimiz, mühendisliğin hızla gelişen alanlarına ilişkin makalelerin yayınına öncelik tanır ve disiplinlerarası yöntem ve teknolojiler üzerine yoğunlaşmayı,mühendislik bilimlerindeki en güncel bilimsel ve teknolojik gelişmeleri araştırmacılara, mühendislere ve ilgili kitlelere ulaştırmayı hedefler. Dergiye gönderilen bilimsel çalışmaların yayımlanmış veya sözlü veya poster sunum olarak başka yerde yayın için değerlendirme aşamasında bulunmaması gereklidir.


“Politeknik Dergisi" temel mühendislik konularını kapsayan bir dergidir. Dergi ulusal ve uluslararası düzeyde bilim, teknoloji ve mühendislik alanlarında orijinal bir araştırmayı bulgu ve sonuçlarıyla yansıtan ve bilime katkısı olan araştırma makalelerini veya yeterli sayıda bilimsel makaleyi tarayıp, konuyu bugünkü bilgi ve teknoloji düzeyinde özetleyen, değerlendirme yapan ve bulguları karşılaştırarak yorumlayan tarama makalelerini kabul etmektedir.

Dergimize makale gönderen ve/veya dergimizde hakemlik yapan /yapacak olan tüm kullanıcıların kurumsal e-posta hesapları ile sisteme kayıt olmaları gerekmektedir (yahoo.com, hotmail.com, gmail.com vb. uzantılı e-posta hesapları kullanılmamalıdır).

Dergimize ait herhangi bir ŞABLON formatı  bulunmamaktadır. İlk gönderi için makalelerin aşağıdaki kurallara göre hazırlanması gerekmektedir. 

Gazi Üniversitesi Politeknik Dergisi, Fen ve Mühendislik alanlarında çalışan bilim insanları arasındaki bilimsel iletişimi oluşturmak amacıyla, bilimsel özgün makaleleri Türkçe veya İngilizce olarak kabul etmektedir.

Araştırma Makalesi: Orijinal bir araştırmayı bulgu ve sonuçlarıyla yansıtan çalışmalar,

Tarama Makalesi: Yeterli sayıda bilimsel makaleyi tarayıp, konuyu günümüzün bilgi ve teknoloji düzeyinde özetleyen, değerlendirme yapan ve bu bulguları karşılaştırarak yorumlayan yazılar,

Teknik Not: Yapılan bir araştırmanın önemli bulgularını açıklayan yeni bir yöntem veya teknik tanımlayan yazılar. 

Bütün yazıların Telif Hakkı Devir Formu, makalenin bütün yazarları tarafından doldurulup editörlüğe iletilmelidir. Telif Hakkı Devir Formu göndermeyen yazarların yayınları işleme konulmaz. Yayınlanmasına karar verilen makaleler üzerine yazarlar tarafından sonradan hiçbir eklenti yapılamaz.

Her makale en az iki hakeme gönderilerek şekil ve içerik bakımından incelenir. Dergide yayınlanabilecek nitelikteki olduğu belirlenen makalelerin dizgisi yapılarak yayına hazır hale getirilir.

SUNUŞ

İlk gönderi esnasında, makalenin yazar(lar)ı tarafından benzerlik taraması yapılarak benzerlik oranını gösteren raporun makale ile birlikte yüklenmesi gerekmektedir. Detaylı bilgi için tıklayınız.

Her makalede yapılan çalışmanın özetlendiği bir Özet Sayfası bulunmalıdır. (Bu sayfa makalenin ilk sayfası olacak şekilde makalenizi tek dosya halinde gönderiniz). Özet sayfasına ait şablon dosyaya ulaşmak için tıklayınız.

1. METİN : Times New Roman yazı karakterinde ve 12 pt olacak şekilde yazılmalı, kaynaklar ve şekiller dahil tarama yazıları dışında 20 sayfayı geçmemelidir. Yazarlar makalelerinin ne türde bir yazı olduğunu belirtmelidirler.

2. BAŞLIK : Eserin başlığı, ilk harfleri büyük olacak şekilde Türkçe ve İngilizce olarak yazılmalı, başlık metne uygun, kısa ve açık olmalıdır.

Metin içerisindeki 1. derece başlıkların tamamı büyük harfle, 2. derece başlıkların tüm kelimelerinin ilk harfleri büyük harfle ve 3. ve daha alt başlıklar için başlığın yalnızca ilk kelimesi büyük harfle olacak şekilde yazılmalıdır (Metin içerisinde kullanılan başlıkların ve alt başlıkların tümünün İngilizceleri parantez içerisinde belirtilmelidir. Yazım dili İngilizce olan makalelerde, parantez içerisinde herhangi bir şey belirtilmemelidir. Tüm metin İngilizce olmalıdır)

3. ÖZET : 200 kelimeyi geçmeyecek şekilde Türkçe ve İngilizce yazılmalıdır. İngilizce özetin başına eserin başlığı da ingilizce olarak yazılmalıdır.

4. ANAHTAR KELİMELER : En az 3 en fazla 5 adet Türkçe/ İngilizce olarak verilmelidir.

5. METİN : Genel olarak giriş, yöntem, bulgular, sonuç ve tartışmaya ilişkin kısımları kapsar.

6. KAYNAKLAR : Metinde parantez içerisindeki [1], [2] vb. rakamlarla numaralandırılmalı ve metin sonunda da eser içinde veriliş sırasına göre yazılmalıdır.

Kaynak bir makale ise: Yazarın soyadı adının baş harfi, tırnak içerisinde makalenin tam başlığı, derginin adı (varsa uluslararası kısaltmaları), cilt no: makalenin başlangıç ve bitiş sayfa no, (yıl)

Örnek: Sözen A., Özbaş E., Menlik T., Çakır M. T., Gürü M. and Boran K., ''Improving the thermal performance of diffusion absorption refrigeration system with alumina nanofluids'', International Journal of Refrigeration, 44: 73-80, (2014)

Kaynak bir kitap ise: Yazarın soyadı adının başharfi, tırnak içerisinde kitabın adı, cilt no, varsa editörü, yayınevinin adı, yayın no, yayınlandığı yer, (yıl).

Kaynak kitaptan bir bölüm ise: Bölüm yazarının soyadı adının başharfi, tırnak içerisinde bölümün adı, bölümün alındığı kitabın adı, yayınevinin adı, yayınlandığı yer, (yıl).

Kaynak basılmış tez ise: Yazarın soyadı adının baş harfi, tırnak içerisinde tezin adı, cinsi (yüksek lisans, doktora), sunulduğu üniversite ve enstitüsü, (yıl).

Kaynak kongreden alınmış tebliğ ise: Yazarın soyadı adının baş harfi, tırnak içerisinde tebliğin adı, kongrenin adı, yapıldığı yer, tebliğin başlangıç ve bitiş sayfa no, (yıl).

Kaynak bir standart ise: Standardın numarası, tırnak içerisinde standardın adı, (yıl).

7. ÇİZELGE VE ŞEKİLLER: Çizelge içermeyen bütün görüntüler (fotoğraf, çizim, diyagram, grafik, harita vs.) şekil olarak isimlendirilmelidir. Her bir çizelge ve şekil, metin içinde gireceği yere yerleştirilmelidir. Bütün şekiller metin içinde ardışık olarak numaralandırılmalıdır (Metin içerisinde kullanılan Çizelge ve Şekillerin tümünün ingilizceleri parantez içerisinde belirtilmelidir. Yazım dili İngilizce olan makalelerde, parantez içerisinde herhangi bir şey belirtilmemelidir. Tüm metin İngilizce olmaldır).

8. FORMÜLLER VE BİRİMLER: Metin içerisindeki tüm formüller equation formatında yazılmalıdır. Formüllere (1), (2) şeklinde sıra numarası verilmelidir. Tüm birimler SI birim sisteminde olmalıdır.

9. SİMGELER VE KISALTMALAR : Metin sonunda kaynaklardan önce verilebilir.

10. TEŞEKKÜR : Eğer kişi veya kurumlara teşekkür yapılacaksa bu kısımda yazılmalı ve kaynaklardan önce verilmelidir.

11. ETİK BEYANI : Dergimizde yayımlanacak makalelerde etik kurul izini ve/veya yasal/özel izin alınmasının gerekip gerekmediği belirtilmiş olmalıdır. Eğer bu izinlerin alınması gerekli ise, izinin hangi kurumdan, hangi tarihte ve hangi karar veya sayı numarası ile alındığı açıkça sunulmalıdır. Ayrıca çalışma insan ve hayvan deneklerinin kullanımını gerektiriyor ise çalışmanın uluslararası deklarasyon, kılavuz vb. uygun gerçekleştirildiği beyan edilmelidir. İzin alınmasının gerekmediği durumlar için TEŞEKKÜR bölümünden sonra aşağıdaki metin eklenmelidir.  

        Türkçe dilindeki makaleler için:
        ETİK STANDARTLARIN BEYANI
        Bu makalenin yazar(lar)ı çalışmalarında kullandıkları materyal ve yöntemlerin etik kurul izni ve/veya yasal-özel bir izin gerektirmediğini beyan ederler.


        İngilizce dilindeki makaleler için:
        DECLARATION OF ETHICAL STANDARDS
        The author(s) of this article declare that the materials and methods used in this study do not require ethical committee permission and/or legal-special permission.

12. YAZAR KATKILARININ BEYANI: Bu bölümde makalede adı geçen her bir araştırmacının makaleye olan katkısı belirtilmelidir.

13. ÇIKAR ÇATIŞMASININ BEYANI: Makale yazarları arasındaki çıkar çatışması durumu belirtilmelidir. Herhangi bir çıkar çatışması yoksa "Bu çalışmada herhangi bir çıkar çatışması yoktur" ibaresi yazılmalıdır.

YAYIN ETİĞİ BİLDİRİMİ
Yayın etiği, en iyi uygulama kılavuzlarını sağlamak ve bu nedenle derginin editörleri, yazarları ve hakemler tarafından uyulması açısından çok önemlidir. Politeknik Dergisi, COPE'nin Davranış Kuralları ve Dergi Editörleri İçin En İyi Uygulama Kılavuz İlkeleri (https://publicationethics.org/resources/code-conduct) tarafından açıklanan ilkelere uygundur ve sadece şeffaflık ilkeleri değil, aynı zamanda en iyi bilimsel uygulama Yayın Etik Kurulu (COPE) tarafından belirlenen kurallara uygun olan makaleleri yayınlar.

Baş Editör ve Alan Editörlerinin Görevleri
Tarafsızlık
Derginin baş editörü ve bölüm editörleri, dergiye gönderilen makalelerin hangisinin yayınlanması gerektiğine karar vermekten sorumludur. Bu süreçte yazarlar ırk, etnik köken, cinsiyet, din ve vatandaşlıklarına göre editörler tarafından ayırt edilmez. Editörlerin yayınlanacak bir makaleyi kabul etme, gözden geçirme veya reddetme kararları, yalnızca makalenin önemi, özgünlüğü ve açıklığına ve ayrıca makalede yapılan çalışmanın derginin kapsamına uygunluğuna dayanmaktadır.
Gizlilik
Baş editör ve bölüm editörleri, gönderilen bir makale hakkında herhangi bir bilgiyi başkasıyla paylaşmamalıdır. Ayrıca ilgili yazar, hakemler / muhtemel hakemler ve yayıncı personel tarafından açıklanmamalıdır. Editörler, yazarlar tarafından sunulan tüm materyallerin inceleme sürecinde gizli kalmasını sağlayacaktır.
Çıkar Çatışması ve Açıklama
Gönderilmiş bir makalede açıklanan yayınlanmamış materyaller, yazarın yazılı izni olmadan hiçbir hakemin kendi çalışmalarında kullanılmamalıdır. Hakem değerlendirmesi sürecinden elde edilen münhasır bilgi veya görüşler gizli tutulmalı ve kişisel çıkarlar için kullanılmamalıdır. Hakemler, rekabetçi, işbirlikçi veya makalelere bağlı yazarlar, şirketler veya kurumlardan herhangi biriyle olan diğer ilişkilerden / bağlantılardan kaynaklanan çıkar çatışmalarına sahip oldukları yazıları dikkate almamalıdır.
Akran inceleme süreci
Baş editör / bölüm editörleri, dergi sistemine gönderilen her bir yazı için çift kör bir akran inceleme sürecinin etkin bir şekilde yapılmasını sağlamalıdır.
Etik olmayan davranışların yönetimi
Editörler, yayıncılarla birlikte, gönderilen bir makale veya yayınlanan bir makale hakkında etik şikâyetler sunulduğunda rasyonel olarak duyarlı önlemler almalıdır.

Yazar(lar)ın Görevleri
Makalenin Yazarı
Tasarım, yorumlama ve uygulama dâhil olmak üzere bildirilen çalışmaya önemli bir katkı sağlayanlara daraltılmalıdır. Gönderilen yazıya önemli katkılarda bulunan tüm yazarlar ortak yazar olarak listelenmelidir.

Özgünlük ve intihal
Gönderdikleri makalenin içeriğinden, dilinden ve özgünlüğünden yazarlar sorumludur. Yazarlar, orijinal eserlerini tamamen oluşturduğunu ve yazarlar çalışmayı ve / veya diğer yazarların sözlerini kullanmışlarsa, bunun uygun bir şekilde alıntılandığını veya alıntı yapıldığını temin etmelidir. İntihal, bir başkasının makalesini yazarın kendi makalesi olarak göstermek, bir başkasının makalesinin önemli kısımlarını (atıfta bulunmadan) kopyalamak veya başka bir deyişle, başkaları tarafından yapılan araştırmaların sonuçlarını almaktan farklı biçimlerdedir. Tüm formlarındaki intihal, etik olmayan yayıncılık davranışını içerir ve kabul edilemez. Hakemlere bir makale gönderilmeden önce, intihal araştırması için iThenticate aracılığıyla benzerlik açısından kontrol edilir.

Fon kaynaklarının tanınması
Makalede bildirilen araştırma için tüm finansman kaynakları, referanslar öncesinde makalenin sonunda ayrıntılı olarak belirtilmelidir.

İfşa ve çıkar çatışmaları
Tüm yazarlar makalelerinde, makalelerinin bulgularını veya yorumunu etkilemek için yorumlanabilecek herhangi bir maddi veya diğer maddi çıkar çatışmasını açıklamalıdır. Proje için tüm finansal destek kaynakları da açıklanmalıdır. Açıklanan potansiyel çıkar çatışmaları örnekleri arasında istihdam, danışmanlıklar, hisse senedi mülkiyeti, onur, ücretli uzman tanıklığı, patent başvuruları / kayıtları ve hibeler veya diğer fonlar yer almaktadır. Potansiyel çıkar çatışmaları mümkün olan en erken aşamada bildirilmelidir.

Raporlama standartları
Makalenin yazarları, yapılan çalışmanın doğru bir açıklamasını ve önemi ile ilgili objektif bir tartışma sunmalıdır. Temel veriler, metinde doğru olarak verilmelidir. Bir makale, diğer araştırmacıların çalışmayı tekrar etmelerine izin vermek için yeterli ayrıntıyı ve referansları içermelidir. Zor veya bilerek kesin olmayan ifadeler etik olmayan davranışlar oluşturur ve kabul edilemez. İnceleme ve profesyonel yayın makaleleri de kesin olmalı, özgün ve objektif olmalı ve editoryal düşünce çalışmaları açıkça ifade edilmelidir.

Veri erişimi ve saklama
Yazarlardan editoryal inceleme süreci için bir makaleyle bağlantılı ham verileri sağlamaları istenebilir ve herhangi bir durumda, yayınlandıktan sonra belirli bir süre için bu verileri saklamaları gerekebilir.

Çoklu, gereksiz veya eşzamanlı yayın
Gönderilen makaleler başka herhangi bir dergiye gönderilmemiş olmalıdır. Aynı makaleyi aynı anda birden fazla dergiye göndermek etik olmayan yayıncılık davranışını içerir. Yazarlar ayrıca makalenin daha önce başka bir yerde yayınlanmadığından da emin olmalıdır.

Yayınlanmış çalışmalarda ana hatalar
Bir yazar yayınlanmış eserinde önemli bir hata veya yanlışlıkla karşılaştığında, dergi editörünü veya yayıncısına bu durumu derhal bildirmek ve makaleyi geri çekmek veya düzeltmek için editörle işbirliği yapmak yükümlülüğündedir.

Hakemlerin Görevleri
Hakemler, makale le ilgili görüşlerini tamamlayarak yorumlarını kendisine tanımlanan zaman içerisinde göndermelidir. Eğer makale, hakemin ilgi alanına uygun değilse, makale editöre geri gönderilmelidir, böylece diğer hakemler zaman kaybetmeden atanabilirler.

Katkı
Hakemler, hakemli bir dergi olan derginin kalitesine katkıda bulunan ana üyelerdir. Alınan makaleyi incelemesi için kalifiye olmayan hakemler derhal editöre bildirmeli ve bu makaleyi incelemeyi reddetmelidir.

Gizlilik
İnceleme için gönderilen yazılar gizli belgeler olarak değerlendirilmelidir. Editör tarafından yetkilendirilmedikçe başkalarıyla gösterilmemeli veya tartışılmamalıdır.

Nesnellik standartları
Yorumlar objektif olarak gerçekleştirilmelidir. Yazarın kişisel eleştirisi uygun değildir. Hakemler açıkça destekleyici argümanlarla görüşlerini ifade etmelidir.

Kaynakların tanınması
Hakemler, yazarlar tarafından alıntılanmayan yayınlanmış çalışmaları tanımlamalıdır. Bir gözlem, türetme veya argümanın daha önce bildirildiği herhangi bir ifadeye ilgili atıfta bulunulmalıdır. Bir gözden geçiren aynı zamanda editörün dikkatini, ele alınan yazı ile kişisel bilgileri olan yayınlanmış diğer herhangi bir makale arasında hayati bir benzerlik ya da çakışma olduğuna dikkat etmelidir.

İfşa ve çıkar çatışması
Hakemler, rekabetçi, işbirlikçi veya yazılarla bağlantılı yazarlar, şirketler veya kurumlarla yapılan diğer ilişkilerden / bağlantılardan kaynaklanan çıkar çatışmalarına sahip oldukları makaleleri dikkate almamalıdır.

DERGİ POLİTİKASI
Makale Değerlendirme Süreci
Hakem Davetinin Geçerlilik Süresi : 30 gün
Hakem Daveti İçin Verilen Ekstra Süre : 15 gün
Hakemin Makaleyi Değerlendirme Süresi : 21 gün
Yazarın Düzeltmelerini Gerçekleştirmesi İçin Verilen Süre : 30 gün
Makale Değerlendirmesi İçin Hakeme Verilen Ekstra Süre : 7 gün

Ücret Politikası
Dergimize gönderilen makalelerin değerlendirilmesi/basılması gibi süreçlerde yazarlardan herhangi bir ücret talep edilmemektedir. 

Makale Geri Çekme Süreci
Yayımlanmış bir makalenin geri çekilmesi işlemi ilgili makalenin tüm yazarlarının ortak talebine istinaden yapılmaktadır. Geri çekilen makaleye ait bilgiler yazar(lar)ın editörlüğümüze başvurduğu tarihten sonra yayımlanacak ilk sayımızda GERİ ÇEKME(RETRACTION) başlığı altında bildirilir. 

Politeknik Dergisi makale gönderimi veya basım aşamasında herhangi bir ücret talep etmemektedir.

Atıf Dizinleri

Google Scholar
TR Dizin
Emerging Sources Citation Index (ESCI)
Thomson Reuters / Clarivate Analytics
EBSCO
SOBIAD

Genel Yayın Yönetmeni

Musa ATAR

Baş Editör

Adnan Sözen
Adnan SÖZEN

  
Enerji Sistemleri Mühendisliği, Enerji

Editörler

Murat Tolga ÖZKAN
Serhat KARYEYEN

Editör Yardımcıları

Fatih Emre BORAN
Volkan YILMAZ

Editör Asistanı

Erdem ÇİFTÇİ

Editörler Kurulu

Hülya DURMUŞ
Hüseyin PEKER
İhsan TOKTAŞ
Zafer AYAZ
Nihat OZTURK
O. Ayhan ERDEM
Figen BALO
Mustafa ÖZER
Orhan KAPLAN
Mustafa Bahadır ÖZDEMİR
Hacı Bayram KARADAĞ
İsmail AYDIN
İhsan KORKUT
Halil DEMİR
Melih OKUR
Ahmet GÜRAL
Kasım SERBEST
Murat YÜCEL
Emine Özge KARACA
Cemil ÇETİNKAYA
Volkan YILMAZ
Fatih Emre BORAN

Yayın Danışma Kurulu

Mehmet ESEN
İlker USTA
Ulvi ŞEKER
Murat HOŞÖZ
Hüseyin Rıza BÖRKLÜ
Mustafa AKTAŞ
Mehmet DEMİRTAŞ
Günnur KOCAR
Engin ÖZDEMİR
Ayhan ÖZÇİFÇİ
H. Serdar YÜCESU
Tayfun MENLİK
Metin GÜRÜ
Sare SAHİL
Erol KURT
Ramazan BAYINDIR
Ebru AKPINAR
Ramazan YILMAZ
Prof. Dr. Yasin VAROL
Nadire Şule ATILGAN
Ramazan KÖSE
Erol ARCAKLIOĞLU
Metin İPEK
Dilek KUMLUTAŞ
İshak KARAKAYA
Jamal KHATİB
Musa ATAR

Teknik Sorumlu

Şulenur ASAL
İrem KARAASLAN
Coşkun YÜKSEL

Yayın Etiği Kurulu

Murat Tolga ÖZKAN
Erdem ÇİFTÇİ
Serhat KARYEYEN
 
TARANDIĞIMIZ DİZİNLER (ABSTRACTING / INDEXING)
181341319013191 13189 13187 13188 18016 

download Bu eser Creative Commons Atıf-AynıLisanslaPaylaş 4.0 Uluslararası ile lisanslanmıştır.